NORYL PPO 沙伯基础(原GE) GFN3 reisn

NORYL? GFN3resin

聚苯醚+PS

SABIC Innovative Plastics

Technical Data

absorption.Hydrolytic stability.Dimensional stability.Suitable for fluid engineering applications including pump housings,pump impellers and

材料状态?资料 1?

供货地区?北美洲

填料/增强材料?玻璃纤维增强材料,30%填料按重量性能特点?Low to No Water Absorption ?尺寸稳定性良好?水解稳定

用途?泵件机构评级?FDA 未评级?NSF 61

加工方法

?注射成型

多点数据

?Coefficient of Thermal Expansion vs.Temperature (ASTM E831)?Elastic Modulus vs Temperature (ASTM

D4065)?Flexural DMA (ASTM D4065)

?Instrumented Impact (Energy)(ASTM D3763)?Instrumented Impact (Load)(ASTM D3763)

?Pressure-Volume-Temperature (PVT -Zoller Method)?Shear DMA (ASTM D4065)

?Specific Heat vs.Temperature (ASTM D3417)?Tensile Creep (ASTM D2990)?Tensile Fatigue

?Tensile Stress vs.Strain (ASTM D638)

?Thermal Conductivity vs.Temperature (ASTM E1530)?

Viscosity vs.Shear Rate (ASTM D3835)

比重

1.29

1.29g/cm3ASTM D792熔流率(300°C/5.0kg)

8.7g/10min 8.7g/10min ASTM D1238溶化体积流率（MVR）(300°C/5.0kg)0.477in3/10min

7.82cm3/10min

ISO 1133

收缩率-流动(0.126in (3.20mm))0.0010到0.0040in/in

0.10到0.40%

Internal Method

-- 3 1.33E+6psi 9150MPa ASTM D638-- 1.27E+6psi 8740MPa ISO 527-2/1抗张强度

断裂 416800psi 116MPa ASTM D638断裂17000psi 117MPa ISO 527-2伸长率

断裂 4 2.0% 2.0%ASTM D638断裂 1.8% 1.8%ISO 527-2弯曲模量

1.97in (50.0mm)跨距 5 1.16E+6psi 8000MPa ASTM D7903.94in (100mm)跨距 6 1.04E+6psi 7170MPa ASTM D790-- 1.26E+6psi 8710MPa ISO 178弯曲强度

--26500psi 183MPa ISO 178屈服,1.97in (50.0mm)跨距 526100psi 180MPa ASTM D790屈服,3.94in (100mm)跨距 6

23500psi

162MPa

ASTM D790

NORYL? GFN3resin

聚苯醚+PS

-22°F(-30°C) 5.6ft·lb/in212kJ/m2

73°F(23°C) 6.1ft·lb/in213kJ/m2

简支梁缺口冲击强度 7ISO179/1eU -22°F(-30°C)22ft·lb/in247kJ/m2

73°F(23°C)19ft·lb/in239kJ/m2

悬壁梁缺口冲击强度

-22°F(-30°C) 2.3ft·lb/in120J/m ASTM D256 73°F(23°C) 2.2ft·lb/in120J/m ASTM D256 -22°F(-30°C) 8 5.5ft·lb/in212kJ/m2ISO180/1A 73°F(23°C) 8 5.9ft·lb/in212kJ/m2ISO180/1A 无缺口悬臂梁冲击

73°F(23°C)11ft·lb/in590J/m ASTM D4812 -22°F(-30°C) 817ft·lb/in236kJ/m2ISO180/1U 8

66psi(0.45MPa),未退火,0.126in(3.20mm)288°F142°C ASTM D648 66psi(0.45MPa),未退火,0.252in(6.40mm)317°F158°C ASTM D648

66psi(0.45MPa),未退火,2.52in(64.0mm)

289°F143°C ISO75-2/Bf 跨距 9

264psi(1.8MPa),未退火,0.126in(3.20mm)279°F137°C ASTM D648 264psi(1.8MPa),未退火,0.252in(6.40mm)280°F138°C ASTM D648

264psi(1.8MPa),未退火,2.52in(64.0mm)

279°F137°C ISO75-2/Af 跨距 9

维卡软化温度

--289°F143°C ISO306/B50 --297°F147°C ISO306/B120线形膨胀系数ASTM E831流动:-40到104°F(-40到40°C)0.000017in/in/°F0.000031cm/cm/°C

横向:-40到104°F(-40到40°C)0.000034in/in/°F0.000062cm/cm/°C

RTI Elec194°F90.0°C UL746 RTI Imp194°F90.0°C UL746

介电强度(0.126in(3.20mm),in Oil)550V/mil22kV/mm ASTM D149介电常数ASTM D150 50Hz 2.93 2.93

60Hz 2.93 2.93

耗散因数ASTM D150 50Hz0.00090 0.00090

60Hz0.00090 0.00090

耐电弧性 10PLC7 PLC7 ASTM D495相比耐漏电起痕指数(CTI)PLC4 PLC4 UL746高电弧燃烧指数(HAI)PLC4 PLC4 UL746高电压电弧起痕速率(HVTR)PLC3 PLC3 UL746

极限氧指数26%26%ASTM D2863

NORYL? GFN3resin

聚苯醚+PS

干燥温度230到250°F110到121°C 干燥时间 3.0到4.0hr 3.0到4.0hr 干燥时间，最大8.0hr8.0hr 建议的最大水分含量0.020%0.020% 建议注入量30到70%30到70% 螺筒后部温度510到600°F266到316°C 螺筒中部温度530到610°F277到321°C 螺筒前部温度550到620°F288到327°C 射嘴温度570到620°F299到327°C 加工（熔体）温度570到620°F299到327°C 模具温度180到230°F82.2到110°C 背压50.0到100psi0.345到0.689MPa 螺杆转速20到100rpm20到100rpm