AATCC Technical Manual/2006Developed in 1941 by AATCC Commit-tee RA63; revised 1952, 1996, 2001,2005; reaffirmed 1943, 1961, 1964,1967, 1971, 1974, 1977, 1980, 1985,1989; editorially revised 1987. Techni-cally equivalent to ISO 4920.

1. Purpose and Scope

1.1This test method is applicable to any textile fabric, which may or may not have been given a water-repellent finish.It measures the resistance of fabrics to wetting by water. It is especially suitable for measuring the water-repellent effi-cacy of finishes applied to fabrics.

1.2 The results obtained with this test method depend on the resistance to wet-ting or water repellency of the fibers,yarns and finishes on the fabric, and upon the construction of the fabric.

2. Principle

tures on a standard chart.

3. Terminology

3.1water repellency, n.—to resist wetting.

3.2 face, n.—in textiles ble surface in an end product.

4. Safety Precautions

NOTE:be consulted and followed.

4.1laboratory areas.

5. Uses and Limitations

screening finishes. It is not intended,however, for use in predicting the proba-ble rain penetration resistance of fabrics,since it does not measure penetration of water through the fabric. For testing rain penetration, AATCC Method 35, Water Resistance: Rain Test, should be used.

6. Apparatus and Materials

6.1 AATCC Spray Tester (see 11.1,Figs. 1, 2, 2A and 3).

6.2 Graduated cylinder, 250 mL.6.3 Water, distilled.6.4 Stopwatch (see 8.3)

7. Test Specimens

7.1 Three test specimens 180.0 × 180.0mm (7.0 × 7.0 in.) are needed and should be conditioned at 65 ± 2% relative hu-midity and 21 ± 1°C (70 ± 2°F) for a min-

imum of 4 h before testing.

7.2 Where possible, each specimen should contain different groups of length-wise and widthwise yarns.

8. Procedure

8.1 Calibrate the apparatus by pouring 250 mL of distilled water at 27 ± 1°C (80± 2°F) into the funnel of the tester and measure the time required for the funnel to empty.

8.1.1 The spray time must be between 25-30 s, otherwise the nozzle should be checked to see if the holes are enlarged or blocked.

8.2 Fasten the test specimen securely in the 152.4 mm (6.0 in.) diameter hoop so that the face of the fabric specimen will be exposed to the water spray. The surface of the specimen should be smooth and without wrinkles.

AATCC Test Method 22-2005

Water Repellency: Spray Test

previously held.

8.6 Repeat steps 8.2 through 8.5 for all three specimens.

9. Evaluation and Report

9.1 Immediately after tapping, com-pare the wet or spotted pattern with the rating chart (see Fig. 1). Rate the face of the specimen. Each test specimen is as-signed a rating corresponding to the near-est level on the rating chart.

9.1.1 Intermediate ratings can be used for ratings of 50 or higher (95, 85, 75, 60) (see flow chart in Appendix A).

9.1.2 In rating loosely woven or porous fabrics, such as voile, any passage of wa-ter through the openings of the fabric is disregarded.

9.2 Report the individual rating results for each test specimen. Do not average the results.

10. Precision and Bias

10.1 Precision. Precision of this test method is based on interlaboratory tests conducted in 1994, using six laboratories, three fabrics, two operators per labora-tory and three determinations per fabric. Separate tests were run on two days. The data sets from each lab were combined for analysis, which required averaging the individual ratings. There were no sig-nificant differences found between days.

10.1.1 The Spray Rating Scale is dis-crete and discontinuous, but results are based on averages which tend to normal-ity. Also, ratings are assigned against de-veloped grade standards (photographs), rather than by arbitrary visual assign-ment. For these reasons, RA63 has made

a judgment that analysis of variance be

used in determining the precision of this

method, without correction for disconti-

nuity.

10.1.2 The three fabrics used in this

study cover a range of 100 to 80 Spray

Rating. Obviously, this is a limited study

upon which to base a statement of preci-

sion for the method. It is the best and

only estimate of precision currently avail-

able. Users of the test method should be

guided accordingly. In making fabric

comparisons for Spray Rating, laborato-

ries are encouraged to establish their lev-

els by running fabrics of known perfor-

mance prior to any test comparisons, and

to bring the practice of the test method

under statistical control.

10.1.3 Plant experience consistently

has shown variation in spray ratings near

a grade of 100 to be quite small, with in-

creasing variation as the grade goes

lower. This has been verified again, in

this limited study. For this reason, critical

difference tables are shown for two

ranges.

10.1.4 Single fabric precision parame-

ters for two fabric levels are given in Ta-

bles I and II.

10.2 Bias. This test method has no

known bias. There is no referee method

by which to determine the true value of

Spray Rating and to find any existing bias

in this methodology.

11. Notes

11.1 The AATCC Spray Test Unit consist-

ing of hoop, nozzle, funnel, stand and Spray

Test Rating Chart is available from AATCC,

Table I—Spray Rating Range—80

Components of Variance

V

lab

=17.2222

V

op

=9.2593

V

err

=9.3750

Table II—Spray Rating Range—100

Components of Variance

V

lab

=0

V

op

=0.6945

V

err

=4.4841

Single Fabric Precision Parameters

N

Single

Operator

Within

Laboratory

Between

Laboratory

18.512.016.6

2 6.010.415.5

3 4.9 9.815.1

4 4.2 9.414.9

5 3.8 9.214.8

Single Fabric Precision Parameters

N

Single

Operator

Within

Laboratory

Between

Laboratory

1 5.9 6.3 6.3

2 4.2 4.8 4.8

3 3.

4 4.1 4.1

4 2.9 3.7 3.7

5 2.

6 3.5 3.5

P.O. Box 12215, Research Triangle Park NC

27709; tel: 919/549-8141; fax: 919/ 549-8933;

e-mail: orders@https://www.360docs.net/doc/dd9199291.html,; SDL Atlas L.L.C.,

1813A Associate Lane, Charlotte NC 28217;

tel: 704/329-0911; fax: 704/329-0914; e-mail:

info@https://www.360docs.net/doc/dd9199291.html,; or Advanced Testing In-

struments Corp., 316D Business Pkwy., Greer

SC 29651-7119; tel: 864/989-0566; fax: 864/

989-0567; e-mail: aticorporation@https://www.360docs.net/doc/dd9199291.html,.

Appendix A

Flow Chart of Evaluation and Report

国家纺织品检测标准

国家纺织品检测标准 国家纺织品检测标准保证了纺织产品的基本安全性 纺织品的安全主要包括制品所用面料是否含有有害物质,所用材料是否卫生,产品的结构和附件是否安全和牢固等。主要有: ——甲醛:含过量甲醛的纺织品在人们的穿着过程中会释放出甲醛,对呼吸道黏膜和皮肤产生强烈刺激,引发呼吸道炎症和皮肤炎。 ——PH值:人的皮肤带有一层弱酸性物质,以防止疾病的侵入,因此纺织品上的PH值在中性至弱酸性对皮肤最为有益。如果PH值过高,会对皮肤产生刺激,并使皮肤易受到其他病菌的侵害。 ——异味:一些挥发性物质,特别是一些奇特气味的物质表示有过量的化学药剂残留在纺织品上。 ——禁用偶氮染料:部分偶氮染料在一定条件下会还原出有致癌作用的芳香胺。这些染料被皮肤吸收后,在人体的正常代谢反应条件下,可能发生还原反应而分解出致癌芳香胺,并经过活化作用改变人体的DNA结构,引起人体病变和诱发癌症。 ——色牢度:染色牢度不佳时,染料会从纺织品转移到皮肤上,在细菌的生物催化作用下发生还原反应,诱发癌症或引起过敏。有的纺织晶和服装遇水、遇摩擦就会发生掉色的情况。 强制性国家标准GB 18401-2003《国家纺织产品基本安全技术规范》是以控制纺织品中主要的有害物质,提升纺织产品的质量,保证人们的基本安全健康为目的,在全国范围内强制实施的一部适用于服用和装饰用纺织产品的通用安全技术规范。该标准适用于品、装饰用品等,对纺织产品中的甲醛含量、pH值、色牢度(耐水、耐汗渍、耐摩擦、耐唾液)、异味和禁用偶氮染料项目提出A类、B类和C类

三档指标进行控制,其中婴幼儿用品要求符合A类指标,内衣、衬衣、袜子、床单等直接接触皮肤的产品要求符合B类指标,外套、毛衣、床罩等非直接接触皮肤的产品要求符合C类指标。 GB18401—2003《国家纺织产品基本安全技术要渤的发布和实施标志着我国政府不仅对食品和药品直接入口类产品的安全性严格监控,也对危险性较小的纺织品和服装的安全性问题进行关注,强制引导生产者制造安全的纺织品,并倡导消费者转向对纺织产品安全性和环保性的注重;标志着我们的纺织标准更进一步地与国际接轨,由注重产品的耐用质量和外观质量转向安全质量,提高了行业的生态生产意识。 广大的纺织企业和经营单位积极执行GB18401—2003,努力为消费者提供安全健康的纺织产品。再加上近两年国家对纺织产品有害物质的严格监控,有效地控制了不良产品在市场上的流通和进口,对规范市场和保护消费者的健康安全有着显著的作用,目前市场上销售的纺织产品在安全性方面有明显的提高。根据国家主管部门对各类纺织产品质量的抽查监督结果,可以说商场销售的纺织产品能够让人放心穿着,甲醛含量基本上都能达到国家标准的要求,禁用的偶氮染料也很少有检出,消费者可以放心购买、穿着和使用纺织品和服装产品。 消费者在选购纺织品时,首先看产品上有无符合性说明,标明“婴幼儿用品”、(GBl8401)A类、B类或C类字样的产品应该是符合国家基本安全标准要求的。专业的检验人员在进行纺织品异味检测时是靠嗅的。消费者在选购纺织品和服装时,应该首先闻一下产品是否有霉味、高沸程石油味(如汽油、煤油味)、鱼腥味、芳香烃味、香味等气味。尤其是一些香味毛巾、香味手帕等,要避免购买。内衣,尤其是婴幼儿用品,量买那些素色、小面积印花图案的产品,所用染料、涂料越少越好,尽量不要买印花摸起来较硬的纺织品。内衣以及婴幼儿服装,穿之前最

沥青混凝土路面抗滑性能的影响因素及检测方法

沥青混凝土路面抗滑性能的影响因素及检测方法 引言 随着公路事业的发展,道路的行车速度有了很大提高,与此同时,交通事故的数量也在不断增加。路面的抗滑能力直接影响高速行驶车辆的安全性,因此公路建设部门和养护管理部门越来越重视路面的抗滑性能,并将其作为高等级公路交、竣工验收及养护质量检查评定中的一项重要指标。 路面抗滑性能是指车辆轮胎受到制动时沿表面滑移所产生的力,是保证公路行车安全及维护必要的允许行车速度的一项重要指标,同时该指标也是路面设计、筑路材料、施工工艺、养护等各项技术水平的综合反映。 1 影响沥青混凝土抗滑性能的因素 一般来说,影响沥青混凝土路面抗滑性能的因素主要有两大方面:一个是路面的外在因素,另一个是路面的内在因素。 1.1 外在因素 ○1.路面潮湿程度 当路表面处于潮湿、积水状态时,摩擦系数会减小很多。因此在公路交通事故中,雨天发生的事故所占比例很高。雨水在路表面积聚,形成水膜,车速越快,轮胎与水膜接触区的水越来不及排出,使轮胎与路面不能充分接触,因此路面抗滑能力大幅度下降。 ○2路面的污染 当路面有杂物,如矿物质的尘埃、路面的油渍、轮胎磨损产生的橡胶粉末等时,也会降低路面的抗滑能力。经测试,受污染路面的摩擦系数会降低5~20%。 1.2 内在因素 ○1沥青混凝土配合比设计中沥青的用量 沥青用量对沥青混凝土路面抗滑性能的影响是非常明显的。沥青在沥青混凝土中起粘合作用,沥青用量过大,除在混凝土中形成结构沥青外,还将有自由沥青存在,自由沥青在夏季高温状态下较不稳定,会溢出路面表面,形成路面沥青膜,俗称“泛油”。泛油的沥青路面被车辆碾压后形成高低不平的形状,造成雨水排不出去,路面抗滑性能大大下降,极易导致交通事故;另外在高温时的重交通情况下,由于沥青高温强度较低,会使路面表面矿料被压入下层,而使沥青被

各国不同防火阻燃性纺织品的评价标准

各国不同防火阻燃性纺织品的评价标 准 1

2

各国不同的防火阻燃性纺织品的评价标准 绝大部分的纺织材料是可燃的,即使经过阻燃技术处理也难以阻止纤维在火焰中燃烧。但经过阻燃处理的纺织品会不同程度地降低燃烧速度或离开火源后能够迅速停止燃烧,因此阻燃是一个相正确概念。 在人们日常生活中,各种火险隐患无所不在。为了减少由于纺织品易燃引起的火灾事故,减少由此造成的对人生命和财产安全的危害,纺织品燃烧性能的测试受到了世界各国的高度关注。 针对纺织品的不同用途,世界各国制定的阻燃法规也已由飞机内饰纺织材料、地毯和建筑装潢材料逐渐扩大到睡衣、家具沙发套、床垫和室内装饰物等。英国、美国、日本等国家还以法律形式规定:妇女、儿童、老年人、残疾人的服装以及睡衣必须是具有阻燃功能的,且须在产品上标明。中国在这方面的立法和标准化工作也在不断加大力度。 3

评判标准 评判织物的阻燃性能一般采用两种标准:一是从织物的燃烧速率来进行评判。即经过阻燃整理的面料按规定的方法与火焰接触一定的时间,然后移去火焰,测定面料继续有焰燃烧的时间和无焰燃烧的时间,以及面料被损毁的程度。有焰燃烧的时间和无焰燃烧的时间越短,被损毁的程度越低,则表示面料的阻燃性能越好;反之,则表示面料的阻燃性能不佳。 另一种是经过测定样品的氧指数(也称极限氧指数)来进行评判。面料燃烧都需要氧气,氧指数LOI是样品燃烧所需氧气量的表述,故经过测定氧指数即可判定面料的阻燃性能。氧指数越高则说明维持燃烧所需的氧气浓度越高,即表示越难燃烧。该指数可用样品在氮、氧混合气体中保持烛状燃烧所需氧气的最小体积百分数来表示。从理论上讲,纺织材料的氧指数只要大于21%(自然界空 气中氧气的体积浓度),其在空气中就有自熄性。根据氧指数的大小,一般将纺织品分为易燃(LOI<20%)、可燃(LOI=20%~26%)、 难燃(LOI=26%~34%)和不燃(LOI>35%)四个等级。事实上,几乎所有常规纺织材料(纤维)都属易燃或可燃的范围。 4

防火标准

CPSC 16CFR 1610服装织物的易燃性标准 本标准规定了布料织物和其它用于服装织物的易燃性测试方法;建立了三个易燃性等级以及各等级的相应指标。明确指出具有何种燃烧特性的织物不宜于服装制品(包括玩具制品),应拒绝使用。 易燃性等级与划分准则:毛绒纺织物易燃性等级划分: a) 等级1,若规定的火焰在纺织品表面蔓延时间大于7秒,为一般易燃性;b) 等级2,若规定的火焰在纺织品表面蔓延时间大于4-7秒,为中等易燃性;c) 等级3,若规定的火焰在纺织品表面蔓延时间小于4秒,为快速剧烈易燃性。 玩具上所使用的纺织材料的易燃性能只允许为一般易燃性材料。 非毛绒纺织物易燃性等级划分:a) 等级1,若规定的火焰在纺织品表面蔓延时间大于 3.5秒,为一般易燃性;PASS b) 等级2,若规定的火焰在纺织品表面蔓延时间小于3.5秒,为快速剧烈易燃性; CPSC 16CFR 1615/1616儿童睡衣燃烧标准 2008年8月14日,美国《2008消费品安全改进法案》(CPSIA)正式实施,其中第102条规定,法案实施90天之后,儿童产品必须由第三方认证机构进行强制性认证,方可进入美国市场或在美国市场销售。儿童睡衣当然属于儿童产品,因此目前要想出口到美国,必须进行第三方认证。 1. 定义和范围在这两份标准中,详细规定了适用于标准的定义,如儿童睡衣、尺码、婴儿服装、制品、装饰品、连匹织物、织物的生产批、服装的生产批、试样等,并引用了易燃织物法案中的有关定义。16CFR1615适用于尺码为0~6岁的儿童睡衣,但不适用于尿布、内衣、婴儿服装和紧身服装,这4类产品应符合服用纺织品易燃性标准(16CFR1610)和聚乙烯塑料膜易燃性标准(16CFR1611)中相应的要求。16CFR1616适用于尺码为7~14岁的儿童睡衣。 2. 燃烧性能要求这两份标准规定了具体的试验方法和燃烧性能要求。要求儿童睡衣按照规定的程序试验,5个试样的平均炭长不超过17.8 cm(7.0 in.),没有一块试样的炭长为25.4 cm (10 in.)。对于使用时需洗涤的儿童睡衣,应按照规定的程序进行洗涤,然后测定燃烧性能。对于标有“只能干洗”的产品,应按消费品安全委员会确认的干洗方法进行干洗。 3. 测试样品要求5片3.5 英寸宽x 10英寸 16 CFR 1610 美国阻燃服装标准,美国的纺织品防火标准规例/ 标准 16 CFR 1610 、 16 CFR 1615/1616 1产品类别 CPSC 16 CFR 1610为衣着类纺织品(一般成衣)的防火标准,但不包括帽子、手套、鞋子及衬里(interlining),此一标准是纺织品与成衣防火的最低要求,适用于所有成人及儿童成衣。 16 CFR 1615/1616 针对儿童睡衣防火作更严格的规范,所有作为儿童睡衣用途之成衣或材料,必需符合此规范,其测试必须依Fabric testing,Prototype seam/trim testing & Production garment testing等步骤进行。 2.处理 16 CFR 1610:根据特定的程序经过干洗后在温度35℃浴比1:30的水中5分钟,清洗2遍,低温烘干1小时。 16 CFR 1615/1616 :根据AATCC124的水洗方法在60度的温度下水洗,(66±5)℃下滚筒烘干.50次.放置样品在105℃的烘箱里30分钟. 3.样品尺寸 16 CFR 1610:选择燃烧快的方向来取样。2 英寸x 6英寸(原样和处理后的样品各5片) 16 CFR 1615/1616:5片3.5 英寸宽x 10英寸 4.火焰 16 CFR 1610:气体:丁烷,火焰高度:5/16英寸,时间:1s 16 CFR 1615/1616:气体:97%的甲烷,火焰高度:1.5英寸,时间:2s 5.测试 16 CFR 1610:测试分两组(原样和处理的样品), 根据燃烧时间及在45度燃烧室内的燃烧状况,记录火的蔓延时间. 16 CFR 1615/1616:把试样悬挂在测试架上,火焰在测试样的底部点火燃烧3秒钟后,再把火焰移开,待测试样上火焰自行熄灭后,量测燃

美国防火测试NFPA130标准详细介绍

美国防火测试NFPA130标准详细介绍 现在高铁、动车交通四通八达,但是高铁的安全与成功依托于严格的标准,其中防火性能涉及哪些标准呢?下面一起来看看美国防火测试。 标准名称--NFPA 130:2014美国轨道车辆材料防火测试标准 NFPA 130:2014 Standard for fixed guideway transit and passenger rail systems NFPA 130:2014 有轨列车及铁路客运体系标准 标准适用范围--轨道车辆材料防火测试标准NFPA 130:2014 NFPA 130标准包括所有的地铁、轨道交通工具、铁路系统的防火要求。 NFPA 130标准制定的目的就是建立统一的有轨列车及铁路客运体系的最低防火及其危险的要求。 NFPA 130:2014主要测试标准: ASTM E162 产品表面火焰传播的测试方法 ASTM E662 烟密度的测试方法 ASTM E648 地面材料临界热辐射量测试 BSS 7239 毒性的测试 BSS 7238 烟密度的测试方法 UL 1685 电线电缆防火测试 ASTM D 3675 柔性多孔材料的表面燃烧测试方法 ASTM C 1166 柔性火焰蔓延的试验方法 Bombardier SMP 800-C 毒性测试与分析 NFPA 130:2014测试项目及标准 1、车辆一般内部组件/材料NFPA 130测试项目及标准 ASTM E 162 表面燃烧测试 ASTM E 662 烟密度测试 BSS 7239 毒性测试 2、地面材料NFPA 130测试项目及标准 ASTM E 648 临界热辐射量测试 ASTM E 662 烟密度测试 BSS 7239 毒性测试 3、座垫、床垫NFPA 130测试项目及标准 ASTM D 3675柔性材料表面燃烧 ASTM E 662 烟密度测试 BSS 7239 毒性测试 4、隔热、隔音保温材料NFPA 130测试项目及标准 ASTM E 162 表面燃烧测试 ASTM E 662 烟密度测试 BSS 7239 毒性测试 5、弹性体NFPA 130测试项目及标准(门窗密封条、垫圈) ASTM C 1166 弹性体材料火焰延伸测试

澳洲纺织品防火测试AS 2755.1标准

澳洲纺织品防火测试AS 2755.1标准 纺织品包括纱线、机织物、针织物、编织物等。 AS 2755.1:纺织品防火测试-垂直样品引燃性测试-标准名称: AS 2755:纺织品防火测试 AS 2755:Textile fabrics - Burning behaviour AS 2755.1:纺织品防火测试-垂直样品引燃性测试 AS 2755.1:Determination of ease of ignition of vertically oriented specimens AS 2755.1:纺织品防火测试-垂直样品引燃性测试-样品要求: 3m全宽 AS 2755.1:纺织品防火测试-垂直样品引燃性测试-相关标准: -AS 2755.2:垂直方向试样火焰蔓延性能测定 AS 2755.2: Measurement of flame spread properties of vertically oriented specimens -AS 2755.3:纺织面料-燃烧行为的测定-表面燃烧时间的测定 AS 2755.3: TEXTILE FABRICS -DETERMINATION OF BURNING BEHAVIOUR-DETERMINATION OF SURFACE BURNING TIME -BS 5438: 当小火焰点火源作用于垂直放置的纺织面料和面料组合件的表面或底部边缘时的可燃性试验方法 BS 5438: Methods for Flammability of vertically oriented textile fabrics and fabric assemblies subjected to a small igniting flame -EN13772: 窗帘、幕布用纺织品-燃烧速率的测定 EN13772: TEXTILE AND TEXTILE PRODUCTS- BURNING BEHAVIOUR-CURTAINS AND DRAPES- MEASUREMENT OF FLAME SPREAD OF VERTICALLY ORIENTED SPECIMENS WWITH LARGE IGNITION SOURCE -EN 13773:织物和纺织品燃烧性能幕布和窗帘-分类方案 EN 13773: Textiles and textile products-Burning behaviour-Curtains and drapes-Classification scheme 办理纺织品防火测试流程: 1、项目申请——向检测机构监管递交申请。 2、资料准备——根据标准要求,企业准备好相关的认证文件。 3、产品测试——企业将待测样品寄到实验室进行测试。 4、编制报告——认证工程师根据合格的检测数据,编写报告。 5、递交审核——工程师将完整的报告进行审核。 6、签发证书——报告审核无误后,颁发报告。

实验1路面平整度的检测方法 (1)

实验1 路面平整度的检测方法:3米直尺法实验2 压实度试验检测方法(环刀法) 实验目的1掌握环刀法现场测定土的含水量,2掌握测定现场路基土密度的方法 实验目的1用于测定新建道路的路基、路面各层表面的平整度,以评定其的施工质量; 2 用于测定既有道路的路面平整度(主要是车辙),为路面维修提供依据; 3掌握用3m直尺测路面平整度的方法; 3掌握原始数据处理方法; 4 学会分析平整度检测误差来源的系统思维方法,为提高测量可信度奠定基础; 实验原理: 3m直尺测定法有单尺测定最大间隙及等距离(1.5m)连续测定两种。两种方法测定的路面平整度有较好的相关关系。 实验难点: 1测点的选择 实验过程备注器 材 (1)3m直尺(2)塞尺 实验流程一、讲解实验的理论,操作方法和数据处理方法。 重点讲解平整度检测误差来源的系统思维方法、用3m直尺测路面平整度的步骤,掌握结果处理方法 方法:1结合实验理论教学 2动手操作示范 二、准备工作 1在测试路段路面上选择测试地点 注意:1当为施工过程中质量检测需要时,测试地点根据需要确定,可以单杆检测; 2当为路基、路面工程质量检查验收或进行路况评定需要时,应首尾相接连续测量10尺。 3对旧路面已形成车辙的路面,应取车辙中间位置为测定位置,用粉笔在路面上作好标记。 三、实验步骤 1 在施工过程中检测时,按根据需要确定的方向,将3m直尺摆在测试地点的路面上。 2 目测3m直尺底面与路面之间的间隙情况,确定间隙为最大的位置。 3 用有高度标线的塞尺塞进间隙处,量记最大间隙的高度,精确至0.2mm。 4 施工结束后检测时,按现行《公路工程质量检验评定标准》(JTJ 071-98)的规定,每1处连续检测10尺,按上述步骤测记10个最大间隙。 四、结果处理 1计算: 单杆检测路面的平整度计算,以3m直尺与路面的最大间隙为测定结果。连续测定10尺时,判断每个测定值是否合格,根据要求计算合格百分率,并计算10个最大间隙的平均值。 合格率=(合格尺数/总测尺数)×100% 2单杆检测的结果应随时记录测试位置及检测结果。连续测定10尺时,应报告平均值、不合格尺数、合格率。

各国纺织面料的阻燃标准汇总

各国纺织面料的阻燃标准汇总 美国面料阻燃标准: 1. CA-117在美国是一种广泛使用的一次性防火标准,并不要求经过水后测试,适用多数出口美国的纺织品。 2. CS-191是美国通用的防护服防火标准,强调长期防火性能和穿着舒适性。加工工艺通常是两步合成法或多步合成法,有较高的技术含量和利润附加值。 3. NFPA-701、703是美国消防协会公布的一项防火标准,适用于公共场所的窗帘等不要求耐水的悬挂织物。测试中同时要求吸附干量、手感等理化指标。 4. TB-603全称BHFTI CTB-603 2005年01月01日起在全美实施。主要用于床垫、床褥等床具用品。测试方法为:完整的一张床垫(床褥)用大室燃烧法测试放热数值。 5. NFPA261.94适用于家具覆盖强物,包括沙发等。 6. FAR25-83飞机内装饰织物所要求的防火标准。 英国面料阻燃标准: 1. BS7177(BS5807)适用于英国公共场所的家具及床垫等织物。特别要求防火性能,测试方式严格。火种分为0~7级八个火源,分别对应于低度、中度、高度和极高度危险四个防火等级。 2. BS7175适用于酒店宾馆、娱乐场所及其他人员密集场所的永久性防火标准。测试要求通过Schedule 4 Part 1及Schedule 5 Part 1两种或更多的测试火种。

3. BS7176适用于家具覆盖织物,要求防火和耐水洗,测试时要求织物和填充物同时达Schedule 4 Part 1、Schedule 5 Part 1和烟密度、毒性等测试指标。是比BS7175(BS5852)更为严格的一项衬垫座椅防火标准。 4. BS5452适用于英国公共场所及所有进口家具中的床单及枕头类纺织品,要求经过50次水洗或干洗后仍然能够有效防火。 5.BS5438系列:英国BS5722儿童睡衣;英国BS5815.3床上用品;英国BS6249.1B窗帘。 德国面料阻燃标准: 1. DIN-4102(DIN66084)装饰织物防火标准; 2. DIN23320及DIN54336-80(DIN66083)防护服防火标准; 日本面料阻燃标准: 1. JISL1008-69飞机装饰织物防火标准; 2. JISL1091防护服标准; 3. JIS1201=FMVSS302汽车装饰织物防火标准; 法国面料阻燃标准: 1. NFG07-184防护服面料; 2. NFG92-501-505装饰织物防火标准;

纺织品燃烧性能测试方法大全

纺织品燃烧性能测试方法大全 关键词:燃烧实验法;限氧指数法;表面燃烧实验法;发烟性试验法;闪点和自燃点测定及点着温度测定;阻燃整理热分析;锥形量热计;锥形量热计 1、燃烧实验法 燃烧实验法,主要用来测定试样的燃烧广度(炭化面积和损毁长度)、续燃时间和阴燃时间。一定尺寸的试样,在规定的燃烧箱里用规定的火源点燃12s,除去火源后测定试样的续燃时间和阴燃时间。阴燃停止后,按规定的方法测出损毁长度。根据试样与火焰的相对位置,可以分为垂直法、倾斜法和水平法。垂直法是目前最为普遍的测定方法。这类实验比45°方向、水平方向燃烧更为剧烈。垂直燃烧实验又分垂直损毁长度法,垂直向火焰蔓延性能测定法、垂直向试样易点燃性测定法和表面燃烧性能测定法。GB/T5456-1997规定了纺织品燃烧性能垂直方向试样火焰蔓延性能的测定,该法用规定的点火器所产生的规定点火火焰,按规定点火时间对垂直向纺织试样点火,测定火焰在试样上蔓延至标记线(规定距离)所用的时间(以秒计)。亦可同时观察、测定和记录试样的其他有关火焰蔓延的性能。GB8746-88规定了纺织织物燃烧性能垂直向试样易点燃性的测定,该法用规定点火器产生的规定火焰,对垂直向纺织试样点火,测量织物点燃所需要的时间。GB8745-88规定了纺织织物表面燃烧性能的测定,在规定的试验条件下,在接近项部处点燃支承于垂直板上的干燥试样的起毛表面,测定火焰在织物表面向下蔓延至标记线的时间。垂直法可用于测定服装织物、装饰织物、帐篷织物等的阻燃性能;倾斜法适用于飞机内装饰用布;水平法适用于地毯之类的铺垫织物。 2、限氧指数法 限氧指数法是目前广泛使用的纺织品燃烧性能测试方法,它是指在规定的实验条件下,在氧、氮混合气体中,材料刚好能保持燃烧状态所需最低氧浓度,用LOI表示,LOI为氧所占混合气体的体积百分数。GB/T5454-1997规定了纺织品燃烧性能试验氧指数法,将试样夹于试样夹上垂直于燃烧筒内,在向上流动的氧氮气流中,点燃试样上端,观察其燃烧特性,并与规定的极限值比较其续燃时间或损毁长度。通过在不同氧浓度中一系列试样的试验,可以测得维持燃烧时氧气百分含量表示的最低氧浓度值,受试试样中要有40%-60%超过规定的续燃和阴燃时间或损毁长度。

服装纺织品防火测试ASTMD1230-94标准

服装纺织品防火测试ASTMD1230-94标准 我国是世界上最大的纺织品服装生产和出口国,纺织品的原料主要有棉花、羊绒、羊毛、蚕茧丝、化学纤维、羽毛羽绒等。 ASTM D1230-94服装纺织品防火测试-标准名称: ASTM D1230-94服装纺织品易燃性的标准试验方法 ASTM D1230-94 Standard Test Method for Flammability of Apparel Textiles ASTM D1230-94服装纺织品防火测试-标准简介: ASTM D1230-94服装纺织品的可燃性标准测试方法涵盖了用于服装而不是儿童 睡衣或防护服的纺织面料的可燃性评估。 注:本试验方法与16CFR 1610的服装纺织品可燃性测试不同。消费者产品安全委员会法规要求出售的纺织品必须达到16 CFR 1610的要求。 ASTM D1230-94服装纺织品防火测试-预处理条件: 1)干燥清洁并洗涤和干燥一次 2)在烘箱中105℃±3℃(221°±5°F)干燥30±2分钟,从烘箱中取出,并放置在一个无水硅胶干燥剂床的干燥器中,直到冷却,但不小于15分钟。ASTM D1230-94服装纺织品防火测试-测试原理 本标准规定了用于制作服装所用纺织品可燃性的试验方法,介绍了三类可燃性,确定了对纺织品分类的要求以及对在商业上称之为不适合作服装、具有燃烧可能的单层或多层织物的使用加以警告。 从纺织品上裁剪的试样,如果它们有起绒纤维表面,要准备刷毛;如果它们是经过防火整理,则要先干洗和洗涤。烘干的试样装在特殊仪器上呈45°角,一个标准化的火焰应用于近于仪器底部的织物表面点燃1秒钟,记录火焰燃烧长127mm(5英寸)织物所需的时间,对于起绒织物,记下织物基布是着火、烧焦或熔化。 ASTM D1230-94服装纺织品防火测试-测试样品: - 1平方米 ASTM D1230-94服装纺织品防火测试-相关标准: -ASTM D6413-2008 Standard test method for flame resistance of textiles(vertical test) ASTM D6413-2008纺织品燃烧性能-垂直法 -16 CFR 1611 乙烯基塑料薄膜的可燃性标准 16 CFR 1611 Standard for the flammability of vinyl plastic film -16 CFR Part 1610 服装纺织品易燃性标准 16 CFR Part 1610 Standard for the Flammability of Clothing Textiles

路面抗滑性能试验(DOC)

§ 8-1 手工铺砂法测定路面构造深度试验 一、目的与适用范围 本方法适用于测定沥青路面及水泥混凝土路面表面构造深度,用以评定路面表面的宏观粗糙度,路面表面的排水性能及抗滑性能。 二、仪具与材料 本试验需要下列仪具与材料: 1 、人工铺砂仪:由圆筒、推平板组成。 (1 )量砂筒:形状尺寸如图8-1 所示,一端是封闭的。容积为25 ± 0.15mL ,可通过称量砂筒中水的质量以确定其容积V ,并调整其高度,使其容积符合规定要求,带一专门的刮尺将筒口砂刮平。 (2 )推平板:形状尺寸如图8-2 所示,推平板应为木制或铝制,直径50mm ,底面粘一层厚1.5mm 的橡胶片,上面有一圆柱把手。 (3 )刮平尺:可用30cm 钢板尺代替。 2 、量砂:足够数量的干燥洁净的匀质砂,粒径0.15~ 0.3mm 。 3 、量尺:钢板尺、钢卷尺,或采用按式(8 -1 )将直径换算成构造深度作为刻度单位的专用的构造深度尺。 4 、其它:装砂容器(小铲)、扫帚或毛刷、挡风板等。 8-1 量砂筒(单位:㎜)图8-2 推平板(单位:㎜)

三、方法与步骤 1 、准备工作 (1 )量砂准备:取洁净的细砂晾干、过筛,取粒径为0.15~ 0.3mm 的砂置于适当的容器中备用。量砂只能在路面上使用一次,不宜重复使用。回收砂必须干燥、过筛处理后方可使用。 (2 )按公路路基路面现场测试随机选点的方法,对测试路段进行随机取样选点,决定测点所在横断面位置。测点应选在行车道的轮迹带上,距路面边缘不应小于1m 。 2 、试验步骤 (1) 用扫帚或毛刷子将测点附近的路面清扫干净,面积不小于30cm × 30cm 。 (2) 用小铲将砂沿筒向圆筒中注满砂,手提圆筒上方,在硬质路表面上轻轻叩打 3 次,使砂密实,补足砂面用钢尺一次刮平。 注:不可直接用量砂筒装砂,以免影响量砂密度的均匀性。 (3) 将砂倒在路面上,用底面粘有橡胶片的推平板,由里向外重复做摊铺运动,稍稍用力将砂细心地尽可能的向外摊开,使砂填入凹凸不平的路表面的空隙中,尽可能将砂摊成圆形,并不得在表面上留有浮动余砂。注意摊铺时不可用力过大或向外推挤。 (4) 用钢板尺测量所构成圆的两个垂直方向的直径,取其平均值,准确至5mm 。 (5) 按以上方法,同一处平行测定不少于3 次,3 个测点均位于轮迹带上,测点间距3~ 5m 。该处的测定位置以中间测点的位置表示。 四、计算 1 、路面表面构造深度测定结果按(8 — 1 )计算:

沥青路面抗滑性能的测试方法及评价指标

沥青路面抗滑性能的测试方法及评价指标 摘要:高速公路沥青混凝土路面使用状况直接决定着路面的养护决策,在规范已有的评价指标的基础上建立了车辙的评价指标及指标建议值,提出了在高温多雨地区路面综合评价指数PQI模型各指标权重的建议值,并采用决策树模型建立了高速公路沥青混凝土路面养护决策模型。 高速公路建成通车后,在交通荷载和自然因素的相互作用下,其路面使用性能有逐年下降的趋势,当这种趋势达到一定的程度时将出现各种病害。对高速公路管理部门而言,不单是要对局部出现病害的部位进行及时维修,更重要的是如何根据路面的使用性能下降的趋势有针对性地采取经济合理的养护策略。本文就此进行初步的探讨。 1沥青混凝土路面使用性能评价 高速公路沥青混凝土路面的养护决策,在很大程度上取决于对沥青混凝土路面使用性能的合理评价。对于沥青混凝土路面使用性能,主要从路面的破损状况、结构承载力、行驶质量、抗滑性能以及车辙状况等方面进行评价。 1.1路面破损状况评价 通过路面破损状况的调查全面掌握沥青混凝土路面出现的病害情况,同时进行量化。路面破损状况采用路面综合破损率DR进行评价,以路面状况指数PCI为评价指标,即: PCI一100—15×DR^0.412 对DR可按照《公路沥青路面养护技术规范》(JTJ 073.2—2001)的相关要求进行调查计算。一般说来,P CI越大表明路面的路况越好。 1.2沥青混凝土路面结构承载力评价 沥青混凝土路面的承载力是指路面达到预定的损害状况之前,还能承受行车荷载的作用次数或还能使用的年数。对沥青混凝土路面承载力通常用弯沉来评价,以路面强度指数(SSI)来作为评价指标,即: SSI=ld/lD 式中:SSI为路面强度指数;ld为沥青混凝土路面设计弯沉值,O.1 mm;lD为检测路段代表弯沉值,0.1 mm。 检测沥青混凝土路面弯沉的主要仪器有贝克曼梁、自动弯沉仪和落锤式弯沉仪(FWD)。对高速公路弯沉的检测宜使用FWD,因为FWD能较好地模拟行车荷载的作用,而且能够快速、安全、准确地采集所需的数据。1.3行驶质量评价 对路面而言,行驶质量是用纵向的平整度来评价的,其评价指标为行驶质量指数(RQI),即: RQI=11.5—0.75×IRI 式中:RQI为行驶质量指数;IRI为国际平整度指数,m/km。 对路面平整度进行检测的主要仪器有3 m直尺、连续式平整度仪、车载颠簸累积仪和激光平整度测试仪。对于高速公路沥青混凝土路面平整度的检测宜采用测试精度高、测试速度快的激光平整度测试仪。 1.4抗滑性能评价 路面的抗滑能力直接影响高速行驶车辆的安全性,为了保证路面在湿润状态下也能提供足够的摩阻力,必须对沥青混凝土路面的抗滑性能进行检测。沥青混凝土路面的抗滑性能主要取决于路表面的宏观构造和微观构造。常用的测试方法有摆式仪法、SCRIM摩擦系数测定车法以及测试构造深度的灌砂法。评价指标主要有横向力系数SFC、摆式仪摆值BPN和构造深度TD。为了保证检测数据的精度、检 测过程的安全以及减少对交通的干扰,对高速公路沥青混凝土路面的抗滑性能宜采用以SFC为主、TD为辅的评

国家纺织品检测标准

国家纺织品检测标准保证了纺织产品的基本安全性 纺织品的安全主要包括制品所用面料是否含有有害物质,所用材料是否卫生,产品的结构和附件是否安全和牢固等。主要有: ——甲醛:含过量甲醛的纺织品在人们的穿着过程中会释放出甲醛,对呼吸道黏膜和皮肤产生强烈刺激,引发呼吸道炎症和皮肤炎。 ——PH值:人的皮肤带有一层弱酸性物质,以防止疾病的侵入,因此纺织品上的PH值在中性至弱酸性对皮肤最为有益。如果PH值过高,会对皮肤产生刺激,并使皮肤易受到其他病菌的侵害。 ——异味:一些挥发性物质,特别是一些奇特气味的物质表示有过量的化学药剂残留在纺织品上。 ——禁用偶氮染料:部分偶氮染料在一定条件下会还原出有致癌作用的芳香胺。这些染料被皮肤吸收后,在人体的正常代谢反应条件下,可能发生还原反应而分解出致癌芳香胺,并经过活化作用改变人体的DNA结构,引起人体病变和诱发癌症。 ——色牢度:染色牢度不佳时,染料会从纺织品转移到皮肤上,在细菌的生物催化作用下发生还原反应,诱发癌症或引起过敏。有的纺织晶和服装遇水、遇摩擦就会发生掉色的情况。 强制性国家标准GB 18401-2003《国家纺织产品基本安全技术规范》是以控制纺织品中主要的有害物质,提升纺织产品的质量,保证人们的基本安全健康为目的,在全国范围内强制实施的一部适用于服用和装饰用纺织产品的通用安全技术规范。该标准适用于品、装饰用品等,对纺织产品中的甲醛含量、pH值、色牢度(耐水、耐汗渍、耐摩擦、耐唾液)、异味和禁用偶氮染料项目提出A类、B类和C类三档指标进行控制,其中婴幼儿用品要求符合A类指标,内衣、衬衣、袜子、床单等直接接触皮肤的产品要求符合B类指标,外套、毛衣、床罩等非直接接触皮肤的产品要求符合C类指标。 GB18401—2003《国家纺织产品基本安全技术要渤的发布和实施标志着我国政府不仅对食品和药品直接入口类产品的安全性严格监控,也对危险性较小的纺织品和服装的安全性问题进行关注,强制引导生产者制造安全的纺织品,并倡导消费者转向对纺织产品安全性和环保性的注重;标志着我们的纺织标准更进一步地与国际接轨,由注重产品的耐用质量和外观质量转向安全质量,提高了行业的生态生产意识。 广大的纺织企业和经营单位积极执行GB18401—2003,努力为消费者提供安全健康的纺织产品。再加上近两年国家对纺织产品有害物质的严格监控,有效地控制了不良产品在市场上的流通和进口,对规范市场和保护消费者的健康安全有着显著的作用,目前市场上销售的纺织产品在安全性方面有明显的提高。根据国家主管部门对各类纺织产品质量的抽查监督结果,可以说商场销售的纺织产品能够让人放心穿着,甲醛含量基本上都能达到国家标准的要求,禁用的偶氮染料也很少有检出,消费者可以放心购买、穿着和使用纺织品和服装产品。 消费者在选购纺织品时,首先看产品上有无符合性说明,标明“婴幼儿用品”、(GBl8401)A 类、B类或C类字样的产品应该是符合国家基本安全标准要求的。专业的检验人员在进行纺织品异味检测时是靠嗅的。消费者在选购纺织品和服装时,应该首先闻一下产品是否有霉味、高沸程石油味(如汽油、煤油味)、鱼腥味、芳香烃味、香味等气味。尤其是一些香味毛巾、香味手帕等,要避免购买。内衣,尤其是婴幼儿用品,量买那些素色、小面积印花图案的产品,所用染料、涂料越少越好,尽量不要买印花摸起来较硬的纺织品。内衣以及婴幼儿服装,穿之前最好洗一洗,检查一下童装的扣子是否牢固。 还有更多的测试项目供客户选择…….”

常规纺织品测试GB18401

如对您有帮助,请购买打赏,谢谢您! 上海标检产品检测有限公司 常规纺织品测试GENERAL TXTILE TESTING (Ref. AATCC, ASTM, BS, ISO, AU, DIN,GB etc. Standards) 1.缩水率及有关测试 DIMENSIONAL STABILITY AND OTHER RELATED TESTS FOR FABRIC / GARMENT 水洗Washing 干洗Dry clean 熨斗Iron 蒸汽Steam iron Appearance after washing / dry cleaning /iron / steam iron 洗水/干洗/熨后/蒸汽熨后外观 2.颜色色牢度测试COLORFASTNESS TESTS 水洗 Washing 磨擦 Rubbing 汗水 Perspiration 干洗 Dry Cleaning 日晒 Light 水 Water 漂白 Bleaching 海水 Sea water 热压 Hot press 干热 Dry heat Dye transfer in storage Sublimation during storage 3.强度测试STRENTH TESTS 拉伸强力 Tensile strength 接缝强力 Seam Strength 接缝滑移 Seam slippage 撕裂强力 Tearing strength 顶破强力 Bursting strength 拉链强度 Zipper strength 粘合强力 Bonding strength 4.布料组织测试 CONSTRUCTION TESTS 经纬密度 Threads per unit length 线圈密度 Stitch density 纱线支数 Counts of yarn 布料宽度 Fabric width 布重 Fabric weight 布料厚度 Fabric thickness 曲斜变形 Bow & skew 纽斜 Crimp 5.纤维成份及其他分析测试测试COMPOSITION AND OTHER ANALYTICAL TESTS 纤维成份 Fibre composition 涂层鉴定 Identification of coating 水份含量 Moisture content 棉丝光效果测试 Mercerization in cotton 偶氮染料测试 Azo Dye 甲醛含量 Formaldehyde content 酸碱度 PH value 重金属分析 Heavy metal 6.纤维及纱线品质测试FIBRE & YARN TESTS 纤维直径 Fibre diameter 每根纱长丝数量 No. of filaments per yarn 纱捻度 Twist per unit length 纱线长度 Total length of thread 纱线净重 Net weight of thread 纱线强力 Single thread strength 绞纱强力 Lea strength 纤维熔点Melting point offiber 7.布料品质测试FABRIC PERFORMANCE TESTS 耐磨性能 Abrasion resistance 起毛球性能 Pilling resistance 折痕回复力 Wrinkle recovery 伸展及回复力 Stretch & recovery 布料硬挺度 Fabric stiffness 防湿水性 Water repellency 防漏水性 Water resistance 透气度 Air permeability 抗紫外线UV Transmittance Test 抗水性 Water resistance 防油性 Oil repellency 防污性 Soil release 8.羽绒测试FEATHER AND DOWN TESTS 成份分析 Composition analysis 种类 Total Down weight 耗氧指数 Oxygen index 酸度 Acidity 蓬松度 Filling power 透明度 Turbidity test 含水率 Moisture content 填充物重量 Net weight of filling materia 9.布料燃烧测试FLAMMABILITY TESTS FOR FABRIC 一般成衣燃烧性 Flammability of general cloth 儿童睡衣防火测试 Children's sleepwear 衣物防火测试 Flame resistance of cloth 布面燃点 Surface flash of fabrics 10.Anti-Microbial 抗菌性能检测 AATCC 100 /AATCC 147 / AATCC 30 Test III / ASTM D4576 / BS 1425 / JIS L1902 / JIS Z2801

路基路面抗滑性能试验检测方法

路基路面抗滑性能试验检测方法 一、概述 路面抗滑性能是指车辆轮胎受到制动时沿表面滑移所产生的力。通常,抗滑性能被看作是路面的表面特性,并用轮胎与路面间的摩阻系数来表示。表面特性包括路表面细构造和粗构造,影响杭滑性能的因素有路面表面特性、路面潮湿程度和行车速度。 路表面细构造是指集料表面的粗糙度,它随车轮的反复磨耗而渐被磨光。通常采用石料磨光值(PSV)表征抗磨光的性能。细构造在低速(30~ 50km/h以下)时对路表抗滑性能起决定作用。而高速时主要作用的是粗构造,它是由路表外露集料问形成的构造、功能是使车轮下的路表水迅速排除,以避免形成水膜。粗构造由构造深度表征。 抗滑性能测试方法有:制动距离法、偏转轮拖车法(横向力系数测试)、摆式仪法)构造深度测试法(手工铺砂仪法,电动铺砂仪法、激光构造深度仪法)。 路面的抗滑摆值是指用标准的手提式摆式摩擦系数测定仪测定的路面在潮湿条件下对摆的摩擦阻力。路表构造深度是指一定面积的路表面凹凸不平的开口孔隙的平均深度。路面横向摩擦系数是指用标准的摩擦系数测定车测定,当测定轮与行车方向成一定角度且以一定速度行驶时,轮胎与潮湿路面之间的摩擦阻力与试验轮上荷载的比值。 高速、一级公路的路面应具有良好的抗滑性能,其沥青路面抗滑性能应符合表6-12的要求,二级及三级公路应根据各路段的具体情况采取必要的技术措施、以提高路面杭滑性能。在设计高速、一级公路的沥青表面层时,应选用抗滑,耐磨石料,其石料磨光值应大于42。高速、一级公路的摩擦系数宜在竣工后第一个夏季采用摩擦系数测定车,以(50土1) km /h的车速测定横向力系数(SFC);宏观构造深度应在竣工后第一个夏季用铺砂法或激光构造深度仪测定,此时的测定值应符合规定的竣工验收值的要求。 对于水泥混凝土路面抗滑标准用构造深度表示:对高速、一级公路,构造深度TD为0.8mm,对于其他公路:TD为0.6mm。 上述抗滑标准仅为设计阶段的抗滑标准。公路在养护过程中,也有养护的具体标准。鉴于路面抗滑性能测试方法较多,下面仅介绍常见的试验方法。 二、构造深度测试方法 (一)手工铺砂法 1.目的与适用范围 本方法适用于测定沥青路面及水泥混凝土路面表面构造深度,用以评定路面表面的宏观粗糙度、路面表面的排水性能及抗滑性能。 2.仪具与材料 (1)人工铺砂仪:由圆筒、推平板组成。 ①量砂筒:一端是封闭的,容积为(25土0.15)mL,可通过称量砂 筒中水的质量以确定其容积V,并调整其高度,使其容积符合要求。带一专门的刮尺将筒口量砂刮平。 2推平板:推平板应为木制或铝制,直径50mm, 底面粘一层厚1.5mm的橡胶片,上面有一圆柱把手。 ③刮平尺:可用30cm钢尺代替。 (2)量砂:足够数量的干燥洁净的匀质砂,粒径为0.15~0.3mm。 (3)量尺;钢板尺、钢卷尺,或采用将直径换算成构造深度作为刻度单位的专 用的构造深度尺。 (4)其他:装砂容器(小铲)、扫帚或毛刷、挡风板等。

相关文档
最新文档