宝钢冷轧牌号对照表
宝钢冷轧牌号对照表低碳钢
Q/BQB 402-2003
Q/BQB
403-2003
Q/BQB
408-2003
JIS
G3141-1996
JFS
A2001-1998
EN
10130-1999
DIN
1623
（1）
-1983
ASTM
A1008-02el
GB/T
5213-2001
ISO
3574-1994
SPCC DC01 BLC SPCC JSC270C DC01 St12 CS - CR1 SPCD DC03 BLD SPCD JSC270D DC03 RRSt13 DS - CR2 SPCE DC04 BUSD SPCE JSC270E DC04 St14 DDS SC1 CR3 SPCE DC05 BUFD SPCEN JSC270F DC05 - EDDS SC2 CR4 - DC06 BSUFD - JSC260G DC06 - - SC3 CR5
碳素结构钢
Q/BQB 410-2003 DIN 1623-(2)-1986
t37-2G St37-2G
St44-3G St44-3G
St52-3G St52-3G
加磷钢
Q/BQB411 JFS A2001-1998 JIS G3135-1986 PrEN 10268-2002
B170P1 JSC340P SPFC340 -
B210P1 JSC390P SPFC390 -
B250P1 JSC440P SPFC440 -
B180P2 JSC340W - H180P
B220P2 JSC390W - H220P
烘烤硬化钢
Q/BQB 416-2003 JFS A 2001-1998 JIS G 3135-1986 prEN 10268-2002 B140H1 JSC270H －-
B180H1 JSC340H －-
B180H2（BH340）－SPFC 340 H H180B
双相钢
Q/BQB 418-2003 JFS A2001-1998 SAE J2340-1999
B240/390DP －-
B280/440DP －-
B340/590DP JSC590Y 600DL1
B400/780DP JSC780Y -
低合金高强钢
Q/BQB419-2003 JFS A2001-1998 SAE J2340-1999 prEN 10268-2002 B340LA JSC440R 340X H340LA
B410LA JSC590R - H420LA
碳素结构钢化学成分和力学性能
行業數據 2009-07-08 19:27 阅读60 评论0
字号：大中小
根据GB 70O一88
1 牌号和化学成分
1.1 钢的牌号和化学成分(熔炼分析)应符合表1规定。
表1
注：1)Q235A、B级沸腾钢锰含量上限为0.60％。
1.1.1 沸腾钢硅含量不大于0.07％；半镇静钢硅含量不大于0.17％；镇静钢硅含量下限值为0.12%
1.1.2 D级钢应含有足够的形成细晶粒结构的元素，例如钢中酸溶铝含量不小于0.015％或全铝含量不小于0.020％。
1.1.3 钢中残余元素铬、镍、铜含量应各不大于0.30％，氧气转炉钢的氮含量应不大于0.008％。如供方能保证，均
可不做分析。
经需方同意.A级钢的铜含量。可不大于0.35％。此时.供方应做铜含量的分析.并在质量证明书中注明其含量。
1.1.4 钢中砷的残余含量应不大于0.080％。用含砷矿冶炼生铁所冶炼的钢。砷含量由供需双方协议规定。如原料中
没有含砷.对钢中的砷含量可以不做分析。
1.1.5在保证钢材力学性能符合本标准规定情况下，各牌号A级钢的碳、碓锰含量和各牌号其他等级钢碳、锰含量下
限可以不作为交货条件，但其含量(熔炼分析)应在质量证明书中注明。
1.1.6 存供直商品钢锭(包括连铸坯)、钢坯时，供方应保证化学成分(熔炼分析)符合表1规定·但为保证轧制钢材各
项性能；={=合本标准要求.各牌号A、B级钢的化学成分可以根据需方要求进行适当j周整.另订协议。
1.2 成品钢材、商品钢坯的化学成分允许偏差应符合GB 222中表1的规定。
沸腾钢成品钢材和商品钢坯化学成分偏差不作保证。5.2 冶炼方法钢由氧气转炉、平炉或电炉冶炼.除非需方有特殊要求，并在合同中注明，冶炼方法一般由供方自仃：臭定。
2力学性能
钢材的拉伸和冲击试验应符合表2规定，弯曲试验应符合表3规定。
表2
表3
注:B试样宽度．a为钢材厚度(直径)。
Q235是普碳钢冷轧材料，
一、我国钢号表示方法概述
钢的牌号简称钢号，是对每一种具体钢产品所取的名称，是人们了解钢的一种共同语言。我国的钢号表示方法，根据国家标准《钢铁产品牌号表示方法》（GB221-79）中规定，采用汉语拼音字母、化学元素符号和阿拉伯数字相结合的方法表示。
即：
①钢号中化学元素采用国际化学符号表示，例如Si,Mn,Cr……等。混合稀土元素用“RE”（或“Xt”）表示。
②产品名称、用途、冶炼和浇注方法等，一般采用汉语拼音的缩写字母表示，见表。
③钢中主要化学元素含量（%）采用阿拉伯数字表示。表：GB标准钢号中所采用的缩写字母及其涵义
。
二、我国钢号表示方法的分类说明
1．碳素结构钢
①由Q+数字+质量等级符号+脱氧方法符号组成。它的钢号冠以“Q”，代表钢材的屈服点，后面的数字表示屈服点数值，单
位是MPa例如Q235表示屈服点（σs）为235 MPa的碳素结构钢。
②必要时钢号后面可标出表示质量等级和脱氧方法的符号。质量等级符号分别为A、B、C、D。脱氧方法符号：F表示沸腾钢；b表示半镇静钢：Z表示镇静钢；TZ表示特殊镇静钢，镇静钢可不标符号，即Z和TZ都可不标。例如Q235-AF表示
A级沸腾钢。
③专门用途的碳素钢，例如桥梁钢、船用钢等，基本上采用碳素结构钢的表示方法，但在钢号最后附加表示用途的字母。
2．优质碳素结构钢
①钢号开头的两位数字表示钢的碳含量，以平均碳含量的万分之几表示，例如平均碳含量为0.45%的钢，钢号为“45”，它不
是顺序号，所以不能读成45号钢。
②锰含量较高的优质碳素结构钢，应将锰元素标出，例如50Mn。
③沸腾钢、半镇静钢及专门用途的优质碳素结构钢应在钢号最后特别标出，例如平均碳含量为0.1%的半镇静钢，其钢号为
10b。
3．碳素工具钢
①钢号冠以“T”，以免与其他钢类相混。
②钢号中的数字表示碳含量，以平均碳含量的千分之几表示。例如“T8”表示平均碳含量为0.8%。
③锰含量较高者，在钢号最后标出“Mn”，例如“T8Mn”。
④高级优质碳素工具钢的磷、硫含量，比一般优质碳素工具钢低，在钢号最后加注字母“A”，以示区别，例如“T8MnA”。
4．易切削钢
①钢号冠以“Y”，以区别于优质碳素结构钢。
②字母“Y”后的数字表示碳含量，以平均碳含量的万分之几表示，例如平均碳含量为0.3%的易切削钢，其钢号为“Y30”。
③锰含量较高者，亦在钢号后标出“Mn”，例如“Y40Mn”。
5．合金结构钢
①钢号开头的两位数字表示钢的碳含量，以平均碳含量的万分之几表示，如40Cr。
②钢中主要合金元素，除个别微合金元素外，一般以百分之几表示。当平均合金含量＜1.5%时，钢号中一般只标出元素符号，而不标明含量，但在特殊情况下易致混淆者，在元素符号后亦可标以数字“1”，例如钢号“12CrMoV”和“12Cr1MoV”，前者铬含量为0.4-0.6%，后者为0.9-1.2%，其余成分全部相同。当合金元素平均含量≥1.5%、≥2.5%、≥3.5%……时，在元素符号后面应标明含量，可相应表示为2、3、4……等。例如18Cr2Ni4WA。
③钢中的钒V、钛Ti、铝AL、硼B、稀土RE等合金元素，均属微合金元素，虽然含量很低，仍应在钢号中标出。例如20
MnVB钢中。钒为0.07-0.12%，硼为0.001-0.005%。
④高级优质钢应在钢号最后加“A”，以区别于一般优质钢。
⑤专门用途的合金结构钢，钢号冠以（或后缀）代表该钢种用途的符号。例如，铆螺专用的30CrMnSi钢，钢号表示为ML
30CrMnSi。
6．低合金高强度钢
①钢号的表示方法，基本上和合金结构钢相同。
②对专业用低合金高强度钢，应在钢号最后标明。例如16Mn钢，用于桥梁的专用钢种为“16Mnq”，汽车大梁的专用钢种为
“16MnL”，压力容器的专用钢种为“16MnR”。
7．弹簧钢
弹簧钢按化学成分可分为碳素弹簧钢和合金弹簧钢两类，其钢号表示方法，前者基本上与优质碳素结构钢相同，后者基本上
与合金结构钢相同。
8．滚动轴承钢
①钢号冠以字母“G”，表示滚动轴承钢类。
②高碳铬轴承钢钢号的碳含量不标出，铬含量以千分之几表示。例如GCr15。渗碳轴承钢的钢号表示方法，基本上和合金
结构钢相同。
9．合金工具钢和高速工具钢
①合金工具钢钢号的平均碳含量≥1.0%时，不标出碳含量；当平均碳含量＜1.0%时，以千分之几表示。例如Cr12、CrWMn、
9SiCr、3Cr2W8V。
②钢中合金元素含量的表示方法，基本上与合金结构钢相同。但对铬含量较低的合金工具钢钢号，其铬含量以千分之几表示，
并在表示含量的数字前加“0”，以便把它和一般元素含量按百分之几表示的方法区别开来。例如Cr06。
③高速工具钢的钢号一般不标出碳含量，只标出各种合金元素平均含量的百分之几。例如钨系高速钢的钢号表示为“W18Cr
4V”。钢号冠以字母“C”者，表示其碳含量高于未冠“C”的通用钢号。
10．不锈钢和耐热钢
①钢号中碳含量以千分之几表示。例如“2Cr13”钢的平均碳含量为0.2%；若钢中含碳量≤0.03%或≤0.08%者,钢号前分别冠以
“00”及“0”表示之，例如00Cr17Ni14Mo2、0Cr18 Ni9等。
②对钢中主要合金元素以百分之几表示，而钛、铌、锆、氮……等则按上述合金结构钢对微合金元素的表示方法标出。
11．焊条钢
它的钢号前冠以字母“H”，以区别于其他钢类。例如不锈钢焊丝为“H2Cr13”，可以区别于不锈钢“2Cr13”。
12．电工用硅钢
①钢号由字母和数字组成。钢号头部字母DR表示电工用热轧硅钢，DW表示电工用冷轧无取向硅钢，DQ表示电工用冷轧
取向硅钢。
②字母之后的数字表示铁损值（W/kg）的100倍。
③钢号尾部加字母“G”者，表示在高频率下检验的；未加“G”者，表示在频率为50周波下检验的。
例如钢号DW470表示电工用冷轧无取向硅钢产品在50赫频率时的最大单位重量铁损值为4.7W/kg。
13．电工用纯铁
①它的牌号由字母“DT”和数字组成，“DT”表示电工用纯铁，数字表示不同牌号的顺序号，例如DT3。
②在数字后面所加的字母表示电磁性能：A——高级、E——特级、C——超级，例如DT8A。
三、部分新老钢号对照
1、碳结钢新、老标准钢号对照。
GB700-88新标准系参照采用国际标准ISO630《结构钢》，而GB700-79旧标准主要参照前苏联IOCT380，因此两者的钢号表示方法以及对各钢号所规定的技术要求都不相同，现将新旧标准钢号对照如下。
冷轧板的牌号
冷轧板的牌号 牌号：Q195A-Q235A、Q195AF-Q235AF、Q295A(B)-Q345 A(B)；SPCC、SPCD、SPCE、ST12-15;DC01-061、Q—普通碳素结构钢屈服点（极限）的代号，它是“屈”的第一个汉语拼音字母的大小写；195、215、235、255、275—分别表示它们屈服点（极限）的数值，单位：兆帕MPa（N/mm2）；由于Q235钢的强度、塑性、韧性和焊接性等综合机械性能在普通碳素结构钢中属最了，能较好地满足一般的使用要求，所以应用范围十分广泛。 2、S-钢（Steel）、P-板（Plate）、C-冷轧（cold）、第四位C-普通级（common）。 3、ST-钢（Steel）、12-普通级冷轧薄钢板、 标记：尺寸精度—尺寸—钢板品种标准 冷轧钢板：钢号—技术条件标准 标记示例：B-0.57501500-GB708-88；钢板、标准号Q/BQB402，牌号SPCC，热处理状态退火+平整（S），表央加工状态为麻面D，表面质量为FB级的切边（切边EC，不切边EM）钢板、厚度0.5mm，B级精度，宽度1000mm，A级精度，长度2000mm，A级精度，不平度精度为PF.A，则标记为：钢板ECQ/BQB 402-SPCC-SD-FB/（0.51000A2000A-PF.A）； 冷轧钢板：Q225-GB912-89 主要产地有：宝钢、鞍钢、本钢、武钢、邯钢、包钢、唐钢、涟钢、济钢等 冷轧板也叫SPCC 他是一种五金冲压的材料! 冷轧板卷是以热轧卷为原料，在室温下在再结晶温度以下进行轧制而成，包括板和卷，国内众多钢厂如宝钢、武钢、鞍钢等均可以生产。其中成张交货的称为钢板，也称盒板或平板；长度很长、成卷交货的称为钢带，也称卷板。 [编辑本段]冷轧的定义 是再结晶下的轧制,但一般理解为使用常温轧制材料的轧制.铝冷轧分为板轧和箔轧.厚度在0.15~以上的称为板,0.15~以下的称为箔.欧美多采用3~6台连续式轧机作为冷轧设备 生产过程中由于不进行加热，所以不存在热轧常出现的麻点和氧化铁皮等缺陷，表面质量好、光洁度高。而且冷轧产品的尺寸精度高，产品的性能和组织能满足一些特殊的使用要求，如电磁性能、深冲性能等。规格：厚度为0.2-4mm，宽度为600-2 000mm，钢板长度为1 200-6 000mm。牌号：Q195A-Q235A、Q195AF-Q235AF、Q295A(B)-Q345 A(B)；SPCC、SPCD、SPCE、ST12-15;DC01-06 性能：主要采用低碳钢牌号，要求具有良好的冷弯和焊接性能，以及一定的冲压性能。 应用领域 冷轧板带用途很广，如汽车制造、电气产品、机车车辆、航空、精密仪表、食品罐头等。冷轧薄钢板是普通碳素结构钢冷轧板的简称，也称冷轧板，俗称冷板，有时会被误写成冷扎板。冷板是由普通碳素结构钢热轧钢带，经过进一步冷轧制成厚度小于4mm的钢板。由于在常温下轧制，不产生氧化铁皮，因此，冷板表面质量好，尺寸精度高，再加之退火处理，其机械性能和工艺性能都优于热轧薄钢板，在许多领域里，特别是家电制造领域，已逐渐用它取代热轧薄钢板。适用牌号：Q195、Q215、Q235、Q275；SPCC（日本牌号）；ST12（德国牌号）符号： 1、Q—普通碳素结构钢屈服点（极限）的代号，它是“屈”的第一个
我国钢材牌号的分类及其含义
我国在此是以钢材的用途分类作为表示方法分类的基础： 1）碳素结构钢： 表示方法：Q+数字+（质量等级符号）+（脱氧方法符号）+（专门用途的符号） ①钢号冠以“Q”，代表钢材的屈服点； ②“Q”后面的数字表示屈服点数值，单位是MPa。例如Q235表示屈服点（σs）为235 MPa的碳素结构钢； ③必要时钢号后面可标出表示质量等级和脱氧方法的符号。 质量等级符号分别为A、B、C、D。 脱氧方法符号：F表示沸腾钢；b表示半镇静钢：Z表示镇静钢；TZ表示特殊镇静钢，镇静钢可不标符号，即Z和TZ都可不标。例如Q235-AF表示A级沸腾钢。专门用途的碳素钢：例如桥梁钢、船用钢等，基本上采用碳素结构钢的表示方法，但在钢号最后附加表示用途的字母。 2）优质碳素结构钢 表示方法：数字+（元素符号）+（脱氧方法符号）+（专门用途的符号） ①钢号开头的两位数字表示钢的碳含量，以平均碳含量的万分之几表示，例如平均碳含量为0.45%的钢，钢号为“45”，它不是顺序号，所以不能读成45号钢。 ②锰含量较高的优质碳素结构钢，应将锰元素标出，例如50Mn。 ③沸腾钢、半镇静钢及专门用途的优质碳素结构钢应在钢号最后特别标出，例如平均碳含量为0.1%的半镇静钢，其钢号为10b。 3）碳素工具钢 表示方法：字母T+数字+（元素符号）+（质量等级符号） ①钢号冠以“T”，以免与其他钢类相混。 ②钢号中的数字表示碳含量，以平均碳含量的千分之几表示。例如“T8”表示平均碳含量为0.8%。 ③锰含量较高者，在钢号最后标出“Mn”，例如“T8Mn”。 ④高级优质碳素工具钢的磷、硫含量，比一般优质碳素工具钢低，在钢号最后加注字母“A”，以示区别，例如“T8MnA”。 4）易切削钢 表示方法：字母Y+数字+（元素符号） ①钢号冠以“Y”，以区别于优质碳素结构钢。 ②字母“Y”后的数字表示碳含量，以平均碳含量的万分之几表示，例如平均碳含量为0.3%的易切削钢，其钢号为“Y30”。 ③锰含量较高者，亦在钢号后标出“Mn”，例如“Y40Mn”。 5）合金结构钢 表示方法：（专门用途符号）+数字+主要合金元素符号和数字+微量合金元素符号+（质量等级符号）+（专门用途符号） ①钢号开头的两位数字表示钢的碳含量，以平均碳含量的万分之几表示，如 40Cr。
钢结构：冷轧产品各国牌号对照表
材料类别宝钢企标国标 日本工业 标准 德国工业 标准 欧州标 准 美国材料试验 协会标准备注牌号牌号牌号牌号牌号标准号 冷轧低碳及超低碳钢板及钢带 商用级 （CQ） SPCC ST12 Q195 10 －P 10－S 08－P 08－S 08Al－P 08Al－S SPCC ST12FeP01 ASTM A366/A366M－ 96（已由ASTM A366/A366M－ 97取代） 1．1．GB11253 －89中的Q195 为普通碳素结 构钢。 2．2．此类钢可 制作汽车零部 件，家具外壳、 桶钢制家具等 简单成型、弯曲 或焊接加工的 产品。 冲压级 （DQ） SPCD ST13 10－Z 08－Z 08Al－Z SPCD USt13 RRSt13 FeP03 ASTM A619/A619M－ 96（1997年后 作废） 可制作汽车门、 窗、挡泥板、马 达外壳等冲压 成型及较复杂 变形加工的零 部件。 深冲级 （DDQ） SPCE－F SPCE－HF SPCE－ZF ST14－F ST14－HF ST14－ZF ST14－T 08Al－F 08Al－HF 08Al－ZF SPCE ST14FeP04 ASTM A620/A620M－ 96（已由ASTM A620/A620M－ 97取代） 1． 1．可制作 汽车前车灯、油 箱、门、窗等深 冲成型及复杂、 剧烈变形加工 的零部件。 2．2．Q/BQB403 －99新增加 ST14－T是专供 上海大众汽车 厂用的。 特深冲级 （SD DQ） ST15FeP05 可制作汽车油 箱、前车灯、复 杂的车底板等 变形很复杂的 零部件。 超深 冲级（ED DQ） ST16 BSC2 （BIF2） FeP06 1． 1．此类为 超深冲无间隙 原子钢。 2． 2． EN 10130 －91的FeP06取
冷轧板包括什么材质
冷轧板包括什么材质？（比如：Q235是属于冷板吗？） 冷轧板卷是以热轧卷为原料，在室温下在再结晶温度以下进行轧制而成，包括板和卷，国内众多钢厂如宝钢、武钢、鞍钢等均可以生产。其中成张交货的称为钢板，也称盒板或平板；长度很长、成卷交 货的称为钢带，也称卷板。 生产工艺：生产过程中由于不进行加热，所以不存在热轧常出现的麻点和氧化铁皮等缺陷，表面质量好、光洁度高。而且冷轧产品的尺寸精度高，产品的性能和组织能满足一些特殊的使用要求，如电磁 性能、深冲性能等。 规格：厚度为0.2-4mm，宽度为600-2 000mm，钢板长度为1 200-6 000mm。 牌号：Q195A-Q235A、Q195AF-Q235AF、Q295A(B)-Q345 A(B)；SPCC、SPCD、SPCE、ST12-15;DC01-06 性能：主要采用低碳钢牌号，要求具有良好的冷弯和焊接性能，以及一定的冲压性能。 应用领域：冷轧板带用途很广，如汽车制造、电气产品、机车车辆、航空、精密仪表、食品罐头等。 请教大家钢材材质,牌号的相关知识! 请教大家一些问题:镀锌,冷轧,热轧钢材的材质与牌号代表的什么意思: 如SGCC,DX51D+Z,JY120,WLZX,DX51D
环保,SGH340,DC520+Z,SECCN5,DX520+ZF,ST02Z,SPCC,DC01,ST12,ST14,45#等还有很多,希 望大家能够介绍一下这方面的知识,或者那个网站可以查到这些资料!谢谢大家! 问题补充：不同牌号和材质的钢材,都具体什么做什么用的,大都用在什么地方? 钢材按大类分，按用途分，可分为型材、板材、管材、建材三大类。 而本问题所提出的冷轧、热轧和镀锌属于板材类钢材。 SGCC（镀锌板） DX51D+Z（以DX51D冷板为基材的镀锌板） JY120（咬合级，锌层120g/m2的镀锌板） WLZX（武钢产专用无锌花标准镀锌板） DX51D环保（以DX51D冷板为基材的镀锌板，环保即为符合欧盟环保要求RoHs指令）SGH340（以热轧为基材的镀锌板，通常是邯郸钢厂生产的）DC52D+Z（以DC52D冷板为基材，可冲压级的镀锌板） SECCN5（电镀锌板、表面进行耐指纹处理） DX52D+ZF（镀锌板） ST02Z（以ST02冷板为基板的镀锌板） SPCC（这个是冷板中常用的牌号） DC01（冷板中常用的牌号，武钢常用） ST12（冷板中常用的牌号） ST14（深冲级冷板） 45#（中碳钢的牌号）
完整的常用金属材料及牌号
金属板材的选用及牌号 我们通常所说的板材，是指薄钢板（带）；而所谓的薄钢板，是指板材厚度小于4mm的钢板，它分为热轧板和冷轧板。众所周知，在家电制造领域里，冷轧板以及以冷轧板为原板的镀锌板的用途十分广泛，冰箱、空调、洗衣机、微波炉、燃气热水器等等的零件材料的选用都与它紧密相连。近年来，国外牌号钢材的大量涌入，丰富了国内钢材市场，使板材选用范围逐步扩大了，这对提高家电产品的制造质量，提供更丰富的款式和外观，起到了显而易见的作用；然而，由于国外的板材型号与我国板材牌号及标记不一致，再加上目前市面上很少有这方面专门介绍的资料和技术书籍，这给如何选用比较恰当的钢板带来了一定的困惑。 本文针对上述情况，介绍了在我国经常用到和使用最多的几个国家（日本、德国、俄罗斯）的冷轧薄钢板以及以冷轧板为原板的镀锌板的基本资料，并归纳出与我们国家钢板牌号的相互对应关系，借此提高我们对国外板材的识别和认知度，并能熟练选用之。 1 板材牌号及标记的识别 1.1 冷轧普通薄钢板 冷轧薄钢板是普通碳素结构钢冷轧板的简称，俗称冷板。它是由普通碳素结构钢热轧钢带，经过进一步冷轧制成厚度小于4mm的钢板。由于在常温下轧制，不产生氧化铁皮，因此，冷板表面质量好，尺寸精度高，再加之退火处理，其机械性能和工艺性能都优于热轧薄钢板，在许多领域里，特别是家电制造领域，已逐渐用它取代热轧薄钢板。 适用牌号：Q195、Q215、Q235、Q275； 符号：Q—普通碳素结构钢屈服点（极限）的代号，它是“屈”的第一个汉语拼音字母的大小写；195、215、235、255、275—分别表示它们屈服点（极限）的数值，单位：兆帕MPa（N/mm2）；由于Q235钢的强度、塑性、韧性和焊接性等综合机械性能在普通碳素结构钢中属最了，能较好地满足一般的使用要求，所以应用范围十分广泛。 标记：尺寸精度—尺寸—钢板品种标准 冷轧钢板：钢号—技术条件标准 标记示例：B-0.5×750×1500-GB708-88 冷轧钢板：Q225-GB912-89 产地：鞍钢、武钢、宝钢等 1.2 冷轧优质薄钢板 同冷轧普通薄钢析一样，冷轧优质碳素结构钢薄钢板也是冷板中使用最广泛的薄钢板。冷轧优质碳素薄钢板是以优质碳素结构钢为材质，经冷轧制成厚度小于4mm的薄板。 适用牌号：08、08F、10、10F
国内外冷轧无取向硅钢牌号对照表
国内外冷轧无取向硅钢牌号对照表 ID thickne ss,mm Russia（俄罗斯）Germany（德国）China（中国）Japan（日本）USA（美国）U.K.（英国）South Korea（南韩）Japan（日本）Japan（日本）Europe（欧洲）GOST 21427.2DIN 46400 .1GB/T 2521JIS C-2552AISI，ASTM A -667BS601.P.1KS C -2510NSC KSC EN 10106 grade P1,5B2500 grade P1,5B2500 grade P1,5B5000 grade P1,5B5000 grade P1,5 grade P1,5KS POSKO P1,5 grade P1,5 grade P1,5 grade P1,5B5000 W/kg,not more Tl, not less W/kg,not more Tl, not less W/kg,not more W/kg,not more Tl, not less W/kg,not more W/kg,not more grade W/kg,not more W/kg,not more W/kg,not more W/kg,not more 1 0.35 35H210 2.1 2 235 -35A 2.35 1.4935W230 2.3 1.635A230 2.3 1.6 35H230 2.335RM230 2.3M235-35A 2.35 1.6 32413 2.5 1.5V250 -35A 2.5 1.4935W250 2.5 1.635A250 2.5 1.6M15 36F145 2.53GRADE250 2.5 PN-09 2.5335H250 2.535RM250 2.5M250-35A 2.5 1.6 4 GRADE265 2.65SE13C PN-10 2.65 52412 2.7 1.5V270 -35A 2.7 1.4935W270 2.7 1.635A270 2.7 1.6M19 36F158 2.75 35H270 2.735RM270 2.7M270-35A 2.7 1.6 6 GRADE280 2.8 7 M22 36F168 2.93 PN-11 2.93 824113 1.5V300 -35A3 1.49 35A3003 1.6 GRADE3003 35H300335RM3003 9 35W3003 1.6 M27 36F180 3.13GRADE315 3.15SE15C PN-12 3.1 M300-35A3 1.6 10 V330 -35A 3.3 1.49 M36 36F190 3.31GRADE335 3.35 M330-35A 3.3 1.6 11 35W360 3.6 1.6135A360 3.6 1.61 SE18C PN-14 3.636H360 3.635RM360 3.6 12 35W440 4.4 1.6435A440 4.4 1.64 SE23C PN-18 4.435H440 4.435RM440 4.4 13 35W4004 1.62 SE26C PN-205 14 SE29C PN-23 5.5 1 0.5 50W230 2.3 1.6 50H230 2.3 2 V250 -50A 2.5 1.4950W250 2.5 1.6 50H250 2.550RM250 2.5M250-50A 2.5 1.6 32414 2.7 1.49V270 -50A 2.7 1.4950W270 2.7 1.650A270 2.7 1.6 50H270 2.750RM270 2.7M270-50A 2.7 1.6 42413 2.9 1.5V290 -50A 2.9 1.4950W290 2.9 1.650A290 2.9 1.6M15 47F168 2.93 PN-09 2.950H290 2.950RM290 2.9M290-50A 2.9 1.6 52412 3.1 1.5V310 -50A 3.1 1.4950W310 3.1 1.650A310 3.1 1.6M19 47F174 3.03 SE13C PN-10 3.150H310 3.150RM310 3.1M310-50A 3.1 1.6 6 M22 47F185 3.22 PN-11 3.22 7 V330 -50A 3.3 1.4950W330 3.3 1.6 M27 47F190 3.31 M330-50A 3.3 1.6 8 V350 -50A 3.5 1.550W350 3.5 1.650A350 3.5 1.6 GRADE355 3.55 50H350 3.550RM350 3.5M350-50A 3.5 1.6 92411 2.6 1.49 M36 47F205 3.57 SE15C PN-12 3.6 102312 3.8 1.58 1122164 1.6V400 -50A4 1.5150W4004 1.6150A4004 1.61M43 47F230 4.01GRADE4004SE18C PN-14450H400450RM4004M400-50A4 1.63 122215 4.5 1.64 GRADE450 4.5 13 V470 -50A 4.7 1.5250W470 4.7 1.6250A470 4.7 1.62 SE23C PN-18 4.750H470 4.750RM470 4.7M470-50A 4.7 1.64 142214 4.8 1.62 1522135 1.65 GRADE5005 1622125 1.6 17 V530 -50A 5.3 1.5450W540 5.4 1.65 M45 47F305 5.31 SE26C PN-20 5.4 M530-50A 5.3 1.65 182211 5.5 1.56 1921126 1.62V600 -50A6 1.55 50A6006 1.65M47 47F400 6.96 SE29C PN-23 6.2 2021117 1.6V700 -50A7 1.5850W6006 1.6550A7007 1.68 50H600650RM6006M600-50A6 1.66 212013 6.5 1.65 50W7007 1.68 50H700750RM7007M700-50A7 1.69 2220127 1.62 2320118 1.6V800 -50A8 1.58 50A8008 1.6847F4758.27 S-30PN-308 24 940-50SG9.4 1.5850W8008 1.68 50H800850RM8008M800-50A8 1.7 25 100-50SG11 1.58 50A100010 1.69 S-40PN-4010.5 M940-50A9.4 1.62 26 50W100010 1.6950A130013 1.69 S-50PN-501350H10001050RM100010 27 50W130013 1.69
冷板、冷轧板知识
冷板、冷轧板知识 冷板是普通碳素结构钢冷轧板的简称，也称冷轧板，俗称冷板，有时会被误写成冷扎板。冷板是由普通碳素结构钢热轧钢带，经过进一步冷轧制成厚度小于4mm的钢板。由于在常温下轧制，不产生氧化铁皮，因此，冷板表面质量好，尺寸精度高，再加之退火处理，其机械性能和工艺性能都优于热轧薄钢板，在许多领域里，特别是家电制造领域，已逐渐用它取代热轧薄钢板。 适用牌号：Q195、Q215、Q235、Q275；SPCC（日 本牌号）；ST12（德国牌号） 符号： 1、Q—普通碳素结构钢屈服点（极限）的代号，它 是“屈”的第一个汉语拼音字母的大小写；195、215、235、 255、275—分别表示它们屈服点（极限）的数值，单位： 兆帕MPa（N/mm2）；由于Q235钢的强度、塑性、韧性 和焊接性等综合机械性能在普通碳素结构钢中属最了，能 较好地满足一般的使用要求，所以应用范围十分广泛。 2、S-钢（Steel）、P-板（Plate）、C-冷轧（cold）、第四位C-普通级（common）。 3、ST-钢（Steel）、12-普通级冷轧薄钢板、 标记：尺寸精度—尺寸—钢板品种标准 冷轧钢板：钢号—技术条件标准 标记示例：B-0.-GB708-88；钢板、标准号Q/BQB402，牌号SPCC，热处理状态退火+平整（S），表央加工状态为麻面D，表面质量为FB级的切边（切边EC，不切边EM）钢板、厚度0.5mm，B级精度，宽度1000mm，A级精度，长度2000mm，A级精度，不平度精度为PF.A，则标记为：钢板ECQ/BQB 402-SPCC-SD-FB/（0.51000A2000A-PF.A）； 冷轧钢板：Q225-GB912-89 主要产地有：宝钢、鞍钢、本钢、武钢、邯钢、包钢、唐钢、涟钢、济钢等 冷轧普通薄钢板：由普通碳素结构钢或低合金结构钢冷轧制成。冷轧板表面质量较好。具有良好的冲压性能。对其要求要保证冷弯和杯试验合格，常用于汽车等行业和镀层板的原料。 冷轧优质薄钢板：主要包括各种优质钢冷轧薄板，最常用的是碳素结构钢板，尤其是深冲压用冷轧薄钢板，是由低碳优质钢08Al冷轧的薄板，钢板按表面质量分为三组；Ⅰ、Ⅱ、Ⅲ，分别表示特别高级、高级、较高的精整表面,按拉延级别分为ZF、HF、F级（代表用于冲制拉延最复杂、很复杂、复杂的零件）,根据钢板厚度允许偏差，又分为A、B两级精度、广泛用于汽车拖拉机工业。 冷轧钢板，表面光洁，加工优良，用于汽车、冰箱、洗衣机等家电，以及产业设备、各种建筑材料。随着经济发展，冷轧钢板已被称为现代社会的必须材料。冷轧产品的分类：热轧酸洗、轧硬卷、普通冷轧、镀锌（电镀锌、耐指纹、热镀锌）、镀铝锌、电镀锡、彩涂、电工钢（矽钢片）等。1、热轧酸洗： 2、轧硬卷：在常温下，对热轧酸洗卷进行连续轧制。 产品特点：因为没有经过退火处理，其硬度很高（HRB大于90），机械加工性能极差，只能进行简单的有方向性的小于90度的折弯加工（垂直于卷取方向）。 应用范围： （1）退火后加工成普通冷轧； （2）有退火前处理装置的镀锌机组加工镀锌； （3）基本不需要加工的面板。 常用钢号CDCM - SPCC （SPCD、SPCE、ST12、ST13、ST14、BLC、BLD、BUSD、BUFD、BSUFD
宝钢牌号字母含义
BUSD: （一）冲压用冷连轧钢带牌号命名方法 1、一般冲压用钢：BLC B——宝钢（BAOSTEEL）缩写；L——低碳（Low Carbon）；C——一般用（Commercial） 2、抗时效性低屈服钢：BLD B——宝钢（BAOSTEEL）缩写；L——低碳（Low Carbon）；D——冲压用（Drawing） 3、非时效性极深冲用钢：BUFD（BUSD） B——宝钢（BAOSTEEL）缩写；U——超级（Ultra）；F——成型（Formability）； D——冲压（Drawing） 4、非时效性超深冲用钢：BSUFD B——宝钢（BAOSTEEL）缩写；SU——超高级（Ultra+Super）；F——成型（Formability）； D——冲压（Drawing） · BUSD、BUFD 非时效性超深冲冷连轧钢带 · BSUFD 非时效性极超深冲冷连轧钢带 在制定BUSD、BUFD、BSUFD 生产工艺时，充分考虑了材质的加工性能，有利于用户在加工零件时减少冲压道次，BSUFD 的深冲及拉伸性能特别优越，适用于难成型部件以及冲压工序所需时间的缩短。 B280VK: （二）冷成型用高强度冷连轧钢带牌号命名方法 B ××× × × B——宝钢（BAOSTEEL）缩写；×××——最小屈服点值； ×——一般用V、X、Y、Z表示 V：高强度低合金，屈服点与抗拉强度差值无规定 X：V中屈服点最小值与抗拉强度最小值差别70MPa Y：V中屈服点最小值与抗拉强度最小值差别100MPa Z：V中屈服点最小值与抗拉强度最小值差别140MPa ×——氧化物/硫化物夹杂控制（K：镇静、细晶粒；F：K+硫化物控制；O：K、F外）例：B240ZK、B340VK SPCC——第一个S表示钢(Steel)，第二个P表示板（Plate），第三个C表示冷（Cold），第四个C表示商业（Commercial），整体表示一般用冷轧碳素钢薄板及钢带，相当于中国Q195-215A牌号。其中需保证抗拉试验时，在牌号末尾加T为SPCCT。 SPCD/DC03——第一个S表示钢(S teel)，第二个P表示板（Plate），第三个C表示冷（Cold），第四个D表示表示冲压（Drawing），整体表示冲压用冷轧碳素钢薄板及钢带，相当于中国08AL（13237）优质碳素结构钢。 SPCE/DC04——第一个S表示钢(Steel)，第二个P表示板（Plate），第三个C表示冷（Cold），第四个E表示深冲压，整体表示深冲用冷轧碳素钢薄板及钢带，相当于中国08AL（5213）深冲钢。需保证非时效性时，在牌号末尾加N为SPCEN。 其它表示符号： 1）冷轧碳素钢薄板及钢带调质代号：退火状态为A，标准调质为S，1/8硬为8，1/4硬为4，1/2硬为2，硬为1。 2）表面加工代号：无光泽精轧为D，光亮精轧为B。如SPCC-SD表示标准调质、无光泽精轧的一般用冷轧碳素薄板。再如SPCCT-SB表示标准调质、光亮加工，要求保证机械性能的冷轧碳素薄板。 热镀锌是指表面镀有一层锌的钢板。镀锌是一种经常采用的经济而有效的防腐方法。全世
最全的冷轧知识(材质牌号分类及生产工艺)
冷轧知识 一、普通冷轧板材简介 是由热轧薄板通过冷压力加工而得到的产品。由于经过多道次的冷轧，其表面质量优于热轧薄板，经过热处理后，可得到良好的力学性能。 1、普通冷轧板材的用途分类 根据生产企业的不同需求，通常将冷轧板分为：一般用冷轧板、冲压级冷轧板、深冲、特深冲及超深冲级冷轧板，一般以卷材和平板交货，厚度以毫米表示，宽度一般为：1000mm和1250mm，长度一般为2000mm和2500mm。 2、普通冷轧板材的牌号 常用牌号为：Q195、Q215、Q235、08AL、SPCC、SPCD、SPCE、SPCEN、ST12、ST13、ST14、ST15、ST16、DC01、DC03、DC04、DC05、DC06等； ST12：表示为最普通的钢号，与Q195、SPCC、DC01牌号材质基本相同； ST13/14：表示为冲压级的钢号，与08AL、SPCD、DC03/04牌号材质基本相同； ST15/16：表示为冲压级的钢号，与08AL、SPCE、SPCEN、DC05/06牌号材质基本相同。 3、普通冷轧板材的牌号尺寸表示方法 例如鞍钢产ST12，1*1250*2500/C，表示为：牌号ST12普通冷板，厚度为1mm，宽度为1250mm，长度为2500mm或C 卷材。外观为白铁皮精包装，机械性能为最普通的，最基础的钢号，只能用于折弯成型，不能用于冲压。使用于机械咬口用，例如冰箱的外壳，车辆油箱等。 ST13以上产品，用在需要深冲的行业，如汽车制造，柴油机的油箱等，具体要用哪一种，看其拉深的要求而定。 ST12与SPCC的差别：其两种产品的机械性能相差无几，只是退货方式不同，ST12材质的产品拉伸性能相对比SPCC 要强。 日本JIS标准材质含义 SPCC---S表示为钢（Steel），P表示为板（Plate），C表示冷（Cold），C表示商业（Commercial），为日本JIS 标准。 如需保证抗拉强度，在牌号末尾加T，为：SPCCT。SPCD---表示冲压用冷轧碳素钢薄板及钢带，相当于中国08AL （13237）优质碳素结构钢。SPCE---表示深冲用冷轧碳素钢薄板及钢带，相当于中国08AL（5213）深冲钢。如需保证非时效性，在牌号末尾加N为SPCEN。冷轧碳素钢薄板及钢带调质代号：退火状态为A，标准调质为S，1/8硬度为8，1/4硬度为4，1/2硬度为2，全硬度为1.表面加工代号：无光泽精轧为D，光亮精轧为B。例如SPCC-SD表示标准调质、无光泽精轧的一般用冷轧碳素薄板。再如SPCCT-SB表示标准调质、光亮加工，要求保证机械性能的冷轧碳素薄板。再如SPCC-1D表示硬的无光泽精轧冷轧碳素钢薄板。机械结构用钢牌号的表示方法为：S+含碳量+字母代号（C、CK），其中含碳量用中间值*100表示，字母C表示碳，字母K表示渗碳用钢。如碳结卷板S20C其含碳量为 0.18-0.23%。 中国GB标准材质含义 从牌号上基本上分为：Q195、Q215、Q235、Q255、Q275等。Q表示钢材屈服点“屈”字的汉语拼音首位字母，195、215等表示屈服点的数值，从化学成分上分，低碳钢牌号Q195、Q215、Q235、Q255、Q275牌号越大，含碳量、含锰量越高，其塑性就越稳定。 冷轧产品牌号与含义 冷轧产品 品名材质 碳结板SPCC、St12、DC01、Q235AB 优结钢板20-45#、08-15# 优质碳素钢08AL 低碳深冲板SC1、SPCE、ST14、DC04 超深冲板SC2、St15、DC05、SC3、St16、DC06、St17 耐腐蚀钢05CuPCrNi、09CuPCrNi、Q345GNHL 低碳冲压钢SPCD、ST13、DC03 深冲板SPCEN
钢材牌号对应表
我国在此是以钢材的用途分类作为表示方法分类的基础： 1）碳素结构钢：表示方法：Q+数字+（质量等级符号）+（脱氧方法符号）+（专门用途的符号）①钢号冠以“Q”，代表钢材的屈服点；②“Q”后面的数字表示屈服点数值，单位是MPa。例如Q235表示屈服点（σs）为235 MPa的碳素结构钢；③必要时钢号后面可标出表示质量等级和脱氧方法的符号。质量等级符号分别为A、B、C、D。脱氧方法符号：F表示沸腾钢；b表示半镇静钢：Z表示镇静钢；TZ表示特殊镇静钢，镇静钢可不标符号，即Z和TZ都可不标。例如Q235-AF表示A级沸腾钢。专门用途的碳素钢：例如桥梁钢、船用钢等，基本上采用碳素结构钢的表示方法，但在钢号最后附加表示用途的字母。 2）优质碳素结构钢表示方法：数字+（元素符号）+（脱氧方法符号）+（专门用途的符号）①钢号开头的两位数字表示钢的碳含量，以平均碳含量的万分之几表示，例如平均碳含量为0.45%的钢，钢号为“45”，它不是顺序号，所以不能读成45号钢。 ②锰含量较高的优质碳素结构钢，应将锰元素标出，例如50Mn。③沸腾钢、半镇静钢及专门用途的优质碳素结构钢应在钢号最后特别标出，例如平均碳含量为0.1%的半镇静钢，其钢号为10b。 3）碳素工具钢表示方法：字母T+数字+（元素符号）+（质量等级符号）①钢号冠以“T”，以免与其他钢类相混。②钢号中的数字表示碳含量，以平均碳含量的千分之几表示。例如“T8”表示平均碳含量为0.8%。③锰含量较高者，在钢号最后标出“Mn”，例如 “T8Mn”。④高级优质碳素工具钢的磷、硫含量，比一般优质碳素工具钢低，在钢号最后加注字母“A”，以示区别，例如“T8MnA”。 4）易切削钢表示方法：字母Y+数字+（元素符号）①钢号冠以“Y”，以区别于优质碳素结构钢。②字母“Y”后的数字表示碳含量，以平均碳含量的万分之几表示，例如平均碳含量为0.3%的易切削钢，其钢号为“Y30”。③锰含量较高者，亦在钢号后标出“Mn”，例如“Y40Mn”。 5）合金结构钢表示方法：（专门用途符号）+数字+主要合金元素符号和数字+微量合金元素符号+（质量等级符号）+（专门用途符号）①钢号开头的两位数字表示钢的碳含量，以平均碳含量的万分之几表示，如40Cr。 ②钢中主要合金元素，除个别微合金元素外，一般以百分之几表示。当平均合金含量＜1.5%时，钢号中一般只标出元素符号，而不标明含量，但在特殊情况下易致混淆者，在元素符号后亦可标以数字“1”，例如钢号“12CrMoV”和“12Cr1MoV”，前者铬含量为0.4-0.6%，后者为0.9- 1.2%，其余成分全部相同。当合金元素平均含量≥1.5%、≥ 2.5%、≥ 3.5%……时，在元素符号后面应标明含量，可相应表示为2、3、4……等。例如18Cr2Ni4WA。③钢中的钒V、钛Ti、铝AL、硼B、稀土RE等合金元素，均属微合金元素，虽然含量很低，仍应在钢号中标出。例如 20MnVB钢中：钒为0.07-0.12%，硼为0.001-0.005%。④高级优质钢应在钢号最后加“A”，以区别于一般优质钢。⑤专门用途的合金结构钢，钢号冠以（或后缀）代表该钢种用途的符号。例如铆螺专用的30CrMnSi钢，钢号表示为ML30CrMnSi 6）低合金高强度钢表示方法：（专门用途符号）+数字+主要合金元素符号和数字+微量合金元素符号+（质量等级符号）+（专门用途符号）①钢号的表示方法，基本上和合金结构钢相同。②对专业用低合金高强度钢，应在钢号最后标明。例如16Mn钢，用于桥梁的专用钢种为“16Mnq”，汽车大梁的专用钢种为 “16MnL”，压力容器的专用钢种为“16MnR”。 7）弹簧钢弹簧钢按化学成分可分为碳素弹簧钢和合金弹簧钢两类，其钢号表示方法，前者基本上与优质碳素结构钢相同，后者基本上与合金结构钢相同。 8）滚动轴承钢表示方法：高碳铬轴承钢：字母G+Cr元素符号和数字渗碳轴承钢：字母G+数字+主要合金元素符号和数字+微量合金元素符号+（质量等级符号）①钢号冠以字母“G”，表示滚动轴承钢类。②高碳铬轴承钢钢号的碳含量不标出，铬含量以千分之
宝钢冷轧牌号对照表
宝钢冷轧牌号对照表低碳钢 Q/BQB 402-2003 Q/BQB 403-2003 Q/BQB 408-2003 JIS G3141-1996 JFS A2001-1998 EN 10130-1999 DIN 1623 （1） -1983 ASTM A1008-02el GB/T 5213-2001 ISO 3574-1994 SPCC DC01 BLC SPCC JSC270C DC01 St12 CS - CR1 SPCD DC03 BLD SPCD JSC270D DC03 RRSt13 DS - CR2 SPCE DC04 BUSD SPCE JSC270E DC04 St14 DDS SC1 CR3 SPCE DC05 BUFD SPCEN JSC270F DC05 - EDDS SC2 CR4 - DC06 BSUFD - JSC260G DC06 - - SC3 CR5 碳素结构钢 Q/BQB 410-2003 DIN 1623-(2)-1986 t37-2G St37-2G St44-3G St44-3G St52-3G St52-3G 加磷钢 Q/BQB411 JFS A2001-1998 JIS G3135-1986 PrEN 10268-2002 B170P1 JSC340P SPFC340 - B210P1 JSC390P SPFC390 - B250P1 JSC440P SPFC440 - B180P2 JSC340W - H180P B220P2 JSC390W - H220P 烘烤硬化钢 Q/BQB 416-2003 JFS A 2001-1998 JIS G 3135-1986 prEN 10268-2002 B140H1 JSC270H －- B180H1 JSC340H －- B180H2（BH340）－SPFC 340 H H180B 双相钢 Q/BQB 418-2003 JFS A2001-1998 SAE J2340-1999 B240/390DP －- B280/440DP －- B340/590DP JSC590Y 600DL1 B400/780DP JSC780Y - 低合金高强钢 Q/BQB419-2003 JFS A2001-1998 SAE J2340-1999 prEN 10268-2002 B340LA JSC440R 340X H340LA B410LA JSC590R - H420LA
冷轧钢板的选择及应用
冷轧钢板的选择及应用 冷轧薄钢板是普通碳素结构钢冷轧板的简称，也称冷轧板，俗称冷板，有时会被误写成冷扎板。冷板是由普通碳素结构钢热轧钢带，经过进一步冷轧制成厚度小于4mm的钢板。由于在常温下轧制，不产生氧化铁皮，因此，冷板表面质量好，尺寸精度高，再加之退火处理，其机械性能和工艺性能都优于热轧薄钢板，在许多领域里，特别是家电制造领域，已逐渐用它取代热轧薄钢板。 适用牌号：Q195、Q215、Q235、Q275；SPCC（日本牌号）；ST12（德国牌号） 符号： 1、Q—普通碳素结构钢屈服点（极限）的代号，它是“屈”的第一个汉语拼音字母的大小写；195、215、235、255、275—分别表示它们屈服点（极限）的数值，单位：兆帕MPa（N/mm2）；由于Q235钢的强度、塑性、韧性和焊接性等综合机械性能在普通碳素结构钢中属最了，能较好地满足一般的使用要求，所以应用范围十分广泛。 2、S-钢（Steel）、P-板（Plate）、C-冷轧（cold）、第四位C-普通级（common）。 3、ST-钢（Steel）、12-普通级冷轧薄钢板、 标记：尺寸精度—尺寸—钢板品种标准 冷轧钢板：钢号—技术条件标准 标记示例：B-0.57501500-GB708-88；钢板、标准号Q/BQB402，牌号SPCC，热处理状态退火+平整（S），表央加工状态为麻面D，表面质量为FB级的切边（切边EC，不切边EM）钢板、厚度0.5mm，B级精度，宽度1000mm，A级精度，长度2000mm，A级精度，不平度精度为PF.A，则标记为：钢板ECQ/BQB 402-SPCC-SD-FB/（0.51000A2000A-PF.A）； 冷轧钢板：Q225-GB912-89 主要产地有：宝钢、鞍钢、本钢、武钢、邯钢、包钢、唐钢、涟钢、济钢等 冷轧普通薄钢板：由普通碳素结构钢或低合金结构钢冷轧制成。冷轧板表面质量较好。具有良好的冲压性能。对其要求要保证冷弯和杯试验合格，常用于汽车等行业和镀层板的原料。 冷轧优质薄钢板：主要包括各种优质钢冷轧薄板，最常用的是碳素结构钢板，尤
钢材钢号和牌号对照表
国标下差5%还是算不错的咯这些指的是综合指数，例如厚度，含碳量，刚才的钢性，拉伸性，高低温塑性变形，各类焊接指数，各类国家所要求的钢材的杂质含量指数。只是遵循一个国家所要求的标准，下差5%不是很严重的。但是要看你是用在什么地方，如果是承重，纯钢建筑上，最好是用国标的，因为这样就算退一步说，出了事故，你使用的是国标的钢材，保险公司都不会来反驳你。让自己吃亏。 钢材一般分钢铁厂的,比如中钢,宝钢,国产的钢因为加工工艺,原料等问题,一般比较差一点,也便宜一点.以下打* 都是用得较多的. SPHC 热孔板 SPTE 马口铁T=1mm *** SPCC 单光板/冷轧板T=1-3mm *** SECC 镀锌板/电解板T=1mm *** SGCC 精光铁板*** SUS 不锈钢301的硬一点,贵一点,304的就差一点了. *** SKT 钢材 COPPER 红铜** BRONZE 磷铜** STEEL 铁 SPCD 双光板** BRASS 黄铜** AL 1100 * ; AL 5052 t5 ** ; AL6063 t5 ***; aL6061 t4 ; AL1050 谁知道钢材检验国标GB222、GB223、228、232、247、2101、2106、2975、4159、6397的具体内容？汽车车架用热轧钢标准 钢材牌号和钢材牌号对照表 简介：我国钢铁牌号及日本硅钢铁牌号表示方法，以及材牌号对照表成份及标准汇编，现在提供给大家参考下。一、我国钢号表示方法概述钢的牌号简称钢号，是对每一种具体钢产品所取的名称，是人们了解钢 的一种共同语言 ... 我国钢材牌号及日本硅钢材牌号表示方法，以及材牌号对照表成份及标准汇编，现在提供给 大家参考下。 一、我国钢材牌号表示方法概述
冷轧钢板材质介绍讲解
冷轧钢板材质介绍 一、普通冷轧板材简介 是由热轧薄板通过冷压力加工而得到的产品。由于经过多道次的冷轧，其表面质量优于热轧薄板，经过热处理后，可得到良好的力学性能。 1、普通冷轧板材的用途分类 根据生产企业的不同需求，通常将冷轧板分为：一般用冷轧板、冲压级冷轧板、深冲、特深冲及超深冲级冷轧板，一般以卷材和平板交货，厚度以毫米表示，宽度一般为：1000mm和1250mm，长度一般为2000mm和2500mm。 2、普通冷轧板材的牌号 常用牌号为：Q195、Q215、Q235、08AL、SPCC、SPCD、SPCE、SPCEN、ST12、ST13、ST14、ST15、ST16、DC01、DC03、DC04、DC05、DC06等； ST12：表示为最普通的钢号，与Q195、SPCC、DC01牌号材质基本相同； ST13/14：表示为冲压级的钢号，与08AL、SPCD、DC03/04牌号材质基本相同； ST15/16：表示为冲压级的钢号，与08AL、SPCE、SPCEN、DC05/06牌号材质基本相同。 3、普通冷轧板材的牌号尺寸表示方法 例如鞍钢产ST12，1*1250*2500/C，表示为：牌号ST12普通冷板，厚度为1mm，宽度为1250mm，长度为2500mm或C卷材。外观为白铁皮精包装，机械性能为最普通的，最基础的钢号，只能用于折弯成型，不能用于冲压。使用于机械咬口用，例如冰箱的外壳，车辆油箱等。 ST13以上产品，用在需要深冲的行业，如汽车制造，柴油机的油箱等，具体要用哪一种，看其拉深的要求而定。 ST12与SPCC的差别：其两种产品的机械性能相差无几，只是退货方式不同，ST12材质的产品拉伸性能相对比SPCC要强。 日本JIS标准材质含义 SPCC---S表示为钢（Steel），P表示为板（Plate），C表示冷（Cold），C表示商业（Commercial），为日本JIS标准。 如需保证抗拉强度，在牌号末尾加T，为：SPCCT。SPCD---表示冲压用冷轧碳素钢薄板及钢带，相当于中国08AL（13237）优质碳素结构钢。SPCE---表示深冲
常用冲压薄板材料的牌号及其含义
常见的冲压用薄板材料牌号及其含义 一、冷轧板 牌号含义：第一个字母“S”——钢Steel的缩写；第二个字母“P”——板Plate的缩写；第三个字母“C”——冷轧板，Cold Rolled Plate；第四个字母表示材料的等级及用途，C表示一般用，D表示冲压用，E表示深冲压用，F表示特深冲压用，G表示超深冲压用 2、冷连轧低碳钢板 3、冲压用冷连钢板 4、冷连轧碳素结构钢板
5、高强度冷轧钢板 ①高强度冷成型用钢 ＨC××××Ｄ+× ＨC -----高强度冷成型用钢 ××× -----屈服强度下限值 × -----由B、P、Y表示【B：烘烤硬化（bake hardening steel）；P：
含P强化（phosphorized steel）；Y：IF钢（interstitial free steel）】 Ｄ-----热镀锌的英文缩写 ×-----镀层种类，由Z和ZF表示（Z：纯锌；ZF：合金化） 例：HC220PD+ZF Ｂ××××× Ｂ-----宝钢（BAOSTEEL ）缩写 ×××-----最小屈服强度值 ×-----强化方式（Ｐ：Ｐ强化；Ｈ：烘烤硬化） ×-----由1或2表示（1：超低碳；2：低碳） 例：Ｂ210P1 7、低合金高强度冷连轧钢板
由于电镀锌板的力学性能与其基本基本上没有差异，所以在此不再一一进行罗列，只简单地介绍电镀锌钢板的牌号命名方式及其含义。 ××××E+□○/○ ××××——对应的冷轧基板牌号； E——Electrog alvanized； □——锌层总类（Z-纯锌镀层；ZN-锌镍合金镀层）； ○/○——锌层含量（g/㎡）。 例如：BUFDE+Z 40/40，BUFDE+ZN 40/40 二、热轧板