镁合金化学镀镍的研究进展

? 411 ? DOI: 10.19289/j.1004-227x.2018.09.009

镁合金化学镀镍的研究进展

宿辉*，王慧文

（黑龙江工程学院材料与化学工程学院，黑龙江 哈尔滨 150050）

摘要：从镀前处理、施镀过程、镀后处理、退镀等方面综述了镁合金化学镀镍工艺的研究现状，指出了其存在的主要问题，探

讨了镁合金化学镀镍的发展趋势。

关键词：镁合金；化学镀镍；前处理；后处理；退镀

中图分类号：TQ153.2; TG178 文献标志码：B 文章编号：1004 – 227X (2018) 09 – 0411 – 07

Progress in research of electroless nickel plating on magnesium alloys // SU Hui*, WANG Hui-wen

Abstract: The current status of research on electroless nickel plating for magnesium alloys was reviewed with respect to

pretreatment, plating process, post-treatment, and stripping method. The main existing problems were pointed out. The

development trends of electroless nickel plating for magnesium alloys were discussed.

Keywords: magnesium alloy; electroless nickel plating; pretreatment; post-treatment; stripping

First-author’s address: College of Materials and Chemical Engineering, Heilongjiang Institute of Technology, Harbin

150050, China

镁合金是继钢铁、铝之后的第三大类金属结构材料，被誉为“21世纪的绿色工程材料”，具有比强

度高、比弹性模量大、密度低、导热导电性能好等优点，在航天航空、汽车工业、电子通信等领域得到

广泛应用[1-4]。但镁的标准电极电位仅为?2.37 V ，具有很高的化学活性，表面易被氧化、腐蚀，而所得氧

化膜疏松、多孔，对基体基本无保护能力，故镁合金的腐蚀问题已严重限制了其发展和应用[5-7]。对镁合

金进行适当的表面处理可提高其耐蚀性，主要方法有化学镀、电镀、化学转化膜、有机涂层等。其中，

化学镀镍因所得镍–磷合金镀层具有良好的耐蚀性、耐磨性，施镀时不需要外加电源，设备投资少，不受

工件尺寸和形状的限制，环境友好等优点，成为提高镁合金耐蚀性的主要方法[8-11]。

本文从镀前处理、施镀工艺、镀后处理等方面总结分析了镁合金化学镀镍工艺的研究现状，指出目

前国内外化学镀镍工艺存在的主要问题，探讨了其未来的发展趋势。

1 镀前处理

镁合金具有很高的化学活性，其表面易氧化成膜，属于难镀金属。化学镀镍前，必须进行前处理以

除去MgO 膜，同时生成具有保护和催化作用的新膜层，主要步骤包括除油、酸洗、活化和制备中间层。

1. 1

酸洗活化 1. 1. 1 酸洗

酸洗可去除镁合金表面的锈迹、氧化皮等异物，同时粗化表面，以利于后续沉积，包括含铬酸洗和

无铬酸洗两类[12-15]。

含铬酸洗液通常以CrO 3或铬酸盐为主要成分，具有较强的氧化性，刻蚀效果良好，且不会对镁合金

造成过腐蚀，技术工艺成熟，应用较多。但铬酐是剧毒物质，对环境安全和人体健康都存在较严重的危

害，故环保无铬酸洗成为酸洗工艺的研究趋势。

无铬酸洗液包括磷酸、焦磷酸、草酸等体系[11,13-20]，其中以磷酸及其与其他酸混合的体系居多。谢

治辉[16]的研究表明，与铬酸酸洗相比，采用磷酸?硝酸体系酸洗AZ91D 镁合金后所得Ni–P 合金镀层与

收稿日期：2017–09–18 修回日期：2017–12–18

基金项目：哈尔滨市科技创新人才研究专项资金（2016RAXXJ043）。

作者简介：宿辉（1971–），女，山东莱州人，博士，教授，主要研究方向为材料表面技术。