季铵化改性聚醚聚硅氧烷的合成及应用

印染助剂TEXTILE AUXILIARIES Vol.32No.6Jun.2015第32卷第6期2015年6月徐新，安秋凤，赵洁，魏元博，秦文

（陕西科技大学教育部轻化工助剂化学与技术重点实验室，陕西西安710021）

摘要：以侧含氢硅油(PHMS)、

烯丙基环氧基聚氧乙烯聚氧丙烯醚(APEE)和三乙醇胺为原料,合成了季铵化改性聚醚聚硅氧烷柔软剂(QPESO),用红外光谱(IR)对产物结构进行了表征.用非离子表面活性剂异构醇聚氧乙烯醚(XL)将其乳化,制得外观半透明的QPESO 乳液,并考察了QPESO 乳液在棉织物上的应用性能.结果表明:经该产品整理后的棉织物具有良好的亲水性和柔软性,白度基本保持不变.

关键词：季铵化;聚醚型聚硅氧烷;棉织物;整理剂

中图分类号:TQ264.1+7文献标识码:B 文章编号:1004-0439(2015)06-0044-03

Synthesis and application of quaternary ammonium

modified polyether polysiloxane

XU Xin,AN Qiu ?feng,ZHAO Jie,WEI Yuan ?bo,QIN Wen

(Key Laboratory of Auxiliary Chemistry ＆Technology for Chemical Industry,Ministry of Education,Shaanxi University of Science ＆Technology,Xi′an 710021,China)

Abstract:Quaternary ammonium modified polyether polysiloxane (QPESO)was prepared using side-chain

hydrogen-containing polysiloxane,polyalkylene glycol allyl glycidyl ether (APEE)and triethanolamine as materi ?als.Chemical structure of QPESO was characterized by IR.Then,QPESO was emulsified with nonionic surfac ?tant isomeric alcohol ethoxylates (XL)in order to achieve a translucent QPESO microemulsion,and the applica ?tion performance of QPESO emulsion in cotton fabric was investigated.The cotton fabric treated with QPESO emulsion acquired favorable hydrophilicity and softness,and the whiteness remained the same.

Key words:quaternary ammonium;polyether polysiloxane;cotton fabric;finishing agent

收稿日期：2014-03-21

作者简介：徐新(1989-),男,湖北咸宁人,硕士研究生,主要从事亲水性有机硅柔软剂的合成.聚醚型聚硅氧烷分子中含有亲水的聚醚链段和

疏水的聚硅氧烷链段,使其既具有良好的水溶性又具

有低的表面张力,而且这类共聚物还具有生物相容

性、良好的适应性和低的玻璃化温度等,因此,聚醚型

聚硅氧烷广泛用作织物亲水抗静电整理剂、消泡剂、

个人护肤用品原料及助剂等[1-3].然而,聚醚型聚硅氧烷具有非离子型表面活性剂的通病——浊点低.在织物整理中,单一聚醚改性的

聚硅氧烷柔软性能不佳,故聚醚型聚硅氧烷柔软剂的