型钢厚度允许偏差
2020年XX有限公司C型钢质量执行标准
XX公司C型钢质量执行标准
作者：一气贯长空
为了确保本公司产品的质量与合格率，树立公司品牌形象，特制定本公司C型钢质量标准如下：
1.C型钢长度允许误差范围+5mm.
2.C型钢底边、腰高允许误差范围+2mm.
3.C型钢小边允许卷误差范围+4mm.
4.C型钢边与边须成直角，允许误差范围10。
，不许有很明显的喇叭
口或圆弧状。
5.C型钢冲孔：两边端允许孔心与孔心边左右误差+3mm.
6.C型钢中间拉条孔允许误差+5mm.
7.镀锌C型钢外表面不得有脱锌、氧化、锈蚀、开裂现象。
8.白色氧化擦拭的，可继续生产，白色氧化不能擦掉的且范围比手
掌大、有连续现象的做停机处理并及时通知采购业务部。
9.C型钢不得有肉眼能明显看出来的侧弯、挠曲现象。
10.C型钢冲孔位不得大面积重叠冲孔，允许少量纠偏。
11.C型钢厚度误差允许偏差+0.5mm.
1/ 2。
国标钢材尺寸允许偏差(2018)
[24a 240*78*7.0*12.0 [24b 240*80*9.0*12.0 [24c 240*82*11.0*12.0 [25a 250*78*7.0*12.0 [25b 250*80*9.0*12.0 [25c 250*82*11.0*12.0
[27a 270*82*7.5*12.5 [27b 270*84*9.5*12.5 [27c 270*86*11.5*12.5
不等边角钢每米弯曲≤3mm,6.3/4号以上总弯曲≤总长度的
0.30%,不等边角钢不得有明显扭转。③
mm
热 轧 钢 板允许偏差GB /T709-2006
DN6
in 1/8"
公称尺 寸/mm
φ10.2
允许偏差
壁厚t 公称尺 允许 寸/mm 偏差
2.0
理论质 量(kg/m)
0.39
壁厚t 公称尺 寸/mm
≥5~＜16,±1.0 ≥16~＜25,±1.5 ≥25~＜40,±1.7
≥40,±2.0 长度≤8m时允许偏差(0~+50),长度＞
8m时允许偏差（0~+80）
7.0
+0.6
-0.7
8.0
+0.6
-0.8
注：花纹纹高不小于基板
厚度的0.2倍
钢带（包括连轧钢板）GB/T709-2006
公称厚度
在下列宽度时厚度允许偏差（PT.A）mm
腰厚d
[5
50*37*4.5*7.0
I 10
100*68*4.5*7.6
[6.3 63*40*4.8*7.5
[6.5 65*40*4.3*7.5
[8
80*43*5.0*8.0
±1.5*±1.5*±0.4
钢结构偏差值
除锈等级 St2 Sa2
½ Sa2
钢结构分部工程竣工验收
二级、三级焊缝外观质量标准（mm）
项目 缺陷类型 未焊满（指不足设计要求）
根部收缩
咬边 弧坑裂纹 电弧擦伤 擦头不良 表面夹渣 表面气孔 注: 表内t为连接处较薄的板
允许偏差
二级
三级
≤0.2+0.2t，且≤1.0
≤0.2+0.4t，且≤2.0
项目 纵向、横向长度 支座中心偏移 周边支撑网架相邻支座高差 支座最大高差 多点支撑网架相邻支座高差 注： 1. L为纵向、横向长度 2. L1为相邻支座间距
允许偏差 L/2000，且不应大于30.0 -L/2000，且不应小于-30.0 L/3000，且不应大于30.0
L/400,且不应大于15.0
项目
允许偏差
图例
主体结构的整体垂直度
（H/2500＋10.0），且 不应大于50.0
主体结构的整体平面弯曲
L/1500，且不应大于25.0
钢网架结构安装工程
小拼单元的允许偏差（mm）
锥体型小拼单元
平面桁架型小拼单元
注： 1. L1为杆件长度 2. L为跨长
项目 节点中心偏移 焊接球节点与钢管中心的偏移 杆件轴线的弯曲矢高
b a
箱型柱身 板垂直度
H（b）/150且不应大 于5.0
用直角 尺和钢 尺检查
b
b
焊接实腹钢梁外形尺寸的允许偏差(mm)
项目
梁长度ι
端部有凸缘支座板 其他形式
端部高度h 拱度
h≤2000
h＞2000 设计要 求起拱 设计未要求起拱
侧弯矢高
扭曲
允许偏差
0 －5.0 ±ι/2500 ±10.0
焊接h型钢允许偏差
焊接H型钢允许偏差1. 引言焊接H型钢是一种常见的结构钢材，广泛应用于建筑、桥梁和机械制造等领域。
在焊接H型钢时，由于各种因素的影响，会产生一定的偏差。
本文将详细介绍焊接H 型钢的允许偏差范围及其相关要求。
2. 焊接H型钢的允许偏差范围焊接H型钢的允许偏差范围主要包括以下几个方面：2.1 尺寸偏差焊接H型钢的尺寸偏差是指焊接后的实际尺寸与设计尺寸之间的差异。
根据相关标准规定，焊接H型钢的尺寸偏差应满足以下要求：•焊接H型钢的高度偏差不应大于标准规定的允许偏差范围。
•焊接H型钢的腰板厚度偏差不应大于标准规定的允许偏差范围。
•焊接H型钢的腰板宽度偏差不应大于标准规定的允许偏差范围。
2.2 直线度偏差焊接H型钢的直线度偏差是指焊接后的H型钢与设计要求的直线之间的偏差。
根据相关标准规定，焊接H型钢的直线度偏差应满足以下要求：•焊接H型钢的腰板直线度偏差不应大于标准规定的允许偏差范围。
•焊接H型钢的翼缘直线度偏差不应大于标准规定的允许偏差范围。
2.3 弯曲度偏差焊接H型钢的弯曲度偏差是指焊接后的H型钢与设计要求的曲线之间的偏差。
根据相关标准规定，焊接H型钢的弯曲度偏差应满足以下要求：•焊接H型钢的腰板弯曲度偏差不应大于标准规定的允许偏差范围。
•焊接H型钢的翼缘弯曲度偏差不应大于标准规定的允许偏差范围。
3. 焊接H型钢允许偏差的相关要求焊接H型钢允许偏差的相关要求主要包括以下几个方面：3.1 施工质量控制在焊接H型钢时，施工方应严格按照相关标准和规范进行施工，确保焊接质量符合要求。
施工过程中应注意以下几点：•使用符合要求的焊接设备和焊接材料。
•控制焊接参数，确保焊接过程中的温度、速度等参数符合要求。
•采用合适的焊接工艺，避免产生过大的热变形和应力集中。
3.2 检验与评定焊接H型钢完成后，应进行检验与评定，以确保其满足设计要求。
检验与评定应包括以下几个方面：•尺寸测量：对焊接H型钢的尺寸进行测量，与设计要求进行比对。
型钢规格
HK360 a 342 203 7.7 13.5 27 b 345 204 8.5 15.0 27 c 347 205 9.6 16.5 27 d 351 255 10.8 18.0 27 e 359 257 12.8 22.0 27 f 350 300 10.0 17.5 27 g 360 300 12.5 22.5 27 k 395 308 21.0 40.0 27
H 型钢柱
+不规定 0
4 标记示例 用 A3 钢生产的 HK400bH 型钢的标记为
热轧 H 型钢 HK400b GB 11263-89 A3 GB 700-79
金属材料有关知识 铸造性 金属浇注成铸件时反映出来的难易程度 叫铸造性或可铸性 金属铸造性能包括 流动性 收缩性 偏析性等 流动性是指液态金属充满铸模的能力 流动性愈好 愈易铸造细薄精致 的铸件和减少铸造缺陷 收缩性是指铸件凝固时体积收缩的程度 金属的收缩会引起铸件产 生缩孔 疏松 收缩应力 弯曲变形和开裂等缺陷 偏析性是指金属在凝固过程中 因结晶 先后差异而造成金属内部化学成分和组织上的不均匀性 偏析愈大 金属铸件各部位性能差 异愈大 这就降低了铸件的质量 这种情况对于大的铸件更是不应有的
热轧 H 型钢
2.5H 型钢桩尺寸及允许偏差 项目
高度 H
宽度 B
GB 11263-89
尺寸 H 400 400<H 见下表 B
厚度
见下表 t1 和 t2
翼缘斜度 k
腹板偏心度 m=│b2-b1│
│ 2│
H 300 300<H
建筑钢材厚度允许偏差标准
建筑钢材厚度允许偏差标准英文回答：Tolerances for Structural Steel Thickness.The tolerances for structural steel thickness are specified in ASTM A6/A6M, Standard Specification for General Requirements for Rolled Structural Steel Bars, Plates, Shapes, and Sheet Piling. The allowable deviations from the specified thickness are as follows:For plates up to and including 1/2 inch in thickness, the allowable deviation is ±0.010 inch.For plates over 1/2 inch to and including 3/4 inch in thickness, the allowable deviation is ±0.015 inch.For plates over 3/4 inch to and including 1 inch in thickness, the allowable deviation is ±0.020 inch.For plates over 1 inch to and including 2 inches in thickness, the allowable deviation is ±0.025 inch.For plates over 2 inches to and including 4 inches in thickness, th e allowable deviation is ±0.030 inch.For plates over 4 inches to and including 6 inches in thickness, the allowable deviation is ±0.035 inch.For plates over 6 inches in thickness, the allowable deviation is ±0.040 inch.For shapes, the allowable deviations from the specified thickness are as follows:For angles up to and including 1/2 inch in thickness, the allowable deviation is ±0.010 inch.For angles over 1/2 inch to and including 3/4 inch in thickness, the allowable deviat ion is ±0.015 inch.For angles over 3/4 inch to and including 1 inch inthickness, the allowable deviation is ±0.020 inch.For angles over 1 inch to and including 2 inches in thickness, the allowable deviation is ±0.025 inch.For angles over 2 inches to and including 4 inches in thickness, the allowable deviation is ±0.030 inch.For angles over 4 inches to and including 6 inches in thickness, the allowable deviation is ±0.035 inch.For angles over 6 inches in thickness, the allowable deviation is ±0.040 inch.For channels, the allowable deviations from thespecified thickness are as follows:For channels up to and including 1/2 inch in thickness, the allowable deviation is ±0.010 inch.For channels over 1/2 inch to and including 3/4 inchin thickness, the allowable deviation is ±0.015 inch.For channels over 3/4 inch to and including 1 inch in thickness, the allowable deviation is ±0.020 inch.For channels over 1 inch to and including 2 inches in thic kness, the allowable deviation is ±0.025 inch.For channels over 2 inches to and including 4 inches in thickness, the allowable deviation is ±0.030 inch.For channels over 4 inches to and including 6 inches in thickness, the allowable deviation is ±0.035 inch.For channels over 6 inches in thickness, the allowable deviation is ±0.040 inch.For beams, the allowable deviations from the specified thickness are as follows:For beams up to and including 1/2 inch in thickness, the all owable deviation is ±0.010 inch.For beams over 1/2 inch to and including 3/4 inch in thickness, the allowable deviation is ±0.015 inch.For beams over 3/4 inch to and including 1 inch in thickness, the allowable deviation is ±0.020 inch.For beams over 1 inch to and including 2 inches in thickness, the allowable deviation is ±0.025 inch.For beams over 2 inches to and including 4 inches in thickness, the allowable deviation is ±0.030 inch.For beams over 4 inches to and including 6 inches in thickness, the allowable deviation is ±0.035 inch.For beams over 6 inches in thickness, the allowable deviation is ±0.040 inch.It is important to note that these tolerances are only applicable to structural steel that is rolled to the specified thickness. If the steel is not rolled to the specified thickness, the allowable deviations may bedifferent.中文回答：建筑钢材厚度允许偏差标准。
型钢检验规范
型钢检验规范1、目的通过对型钢原材料的检验确保本公司生产的产品符合生产工艺及顾客的要求。
2、范围适用于本公司生产用的所有型钢类原材料的检验。
3、验收规则3.1型钢的质量由供方技术监督部门检查和验收；3.2供方必须保证交货的型钢符合有关标准的规定，本公司有权按相应标准的规定进行复查。
3.3型钢的标志可采用打钢印、喷印、盖印、挂标牌、粘标签、放置卡片或涂色等方式。
标志应字迹清楚、牢固可靠。
3.4型钢到厂应附有证明该批型钢符合标准要求和订货合同的质量证明书。
4、热轧圆钢和方钢4.1外观要求4.4.1圆钢和方钢以直条交货。
4.4.2方钢不得有显著扭转。
4.4.3圆钢和方钢两端的切斜度不得大于该圆钢直径、方钢边长的30%。
4.4.4圆钢和方钢端头允许有局部变形。
4.4.5圆钢和方钢不允许有明显的爆铁、烂铁现象。
4.2圆钢直径和方钢边长的允许偏差圆钢直径和方钢边长＞5.5～20mm 允许偏差±0.4mm＞20～30mm 允许偏差±0.50mm＞30～50mm 允许偏差±0.60mm＞50～80mm 允许偏差±0.80mm＞80～110mm 允许偏差±1.1mm。
4.3长度及允许偏差圆钢直径和方钢边长≤25mm钢材长度4-10m＞25mm钢材长度3-9m。
5、热轧扁钢5.1外形5.1.1扁钢不得有明显的扭转。
5.1.2扁钢的端头应剪切正直，切斜不得大于以下规定：宽度＞100mm的扁钢，不得大于8mm。
5.1.3扁钢外形不允许有明显爆铁、烂铁现象。
5.2扁钢截面尺寸允许偏差宽度尺寸：10～50mm+0.5/-1.0＞50～75mm+0.6/-1.3＞75～100mm+0.9/-1.8厚度尺寸：3～16mm+0.3/-0.5。
5.3扁钢的理论重量宽度(mm)×厚度(mm)×7.85÷1000(kg/m)。
5.4长度及允许偏差通常长度(理论重量≤19kg/m扁钢)3-9m，本公司要求不低于4m。
c型钢国标厚度
c型钢国标厚度C型钢国标厚度C型钢是一种常见的钢材，其国标厚度是指根据国家标准规定的C 型钢的标准厚度范围。
C型钢主要用于建筑、桥梁、机械制造等领域，其厚度的选择对于其使用效果和结构稳定性具有重要影响。
根据国标规定，C型钢的国标厚度主要有以下几种规格：6mm、8mm、10mm、12mm、14mm、16mm、18mm、20mm、22mm、24mm、26mm、28mm、30mm等。
这些规格可以满足不同的工程需求，使得C型钢能够适应不同的应力和负荷。
在实际应用中，选择适当的C型钢国标厚度非常重要。
首先，要根据工程设计的需要和所承受的荷载情况来确定C型钢的国标厚度。
如果负荷较大，需要选择较厚的C型钢，以保证结构的强度和稳定性。
其次，要考虑C型钢的经济性和可行性。
较厚的C型钢会增加工程成本，而较薄的C型钢则可能不满足结构要求，因此需要综合考虑各种因素来确定最佳的国标厚度。
C型钢国标厚度还需要符合相关的国家标准和规范要求。
国家标准对C型钢的厚度范围进行了明确规定，以确保其质量和安全性能。
在进行施工和使用时，必须按照国家标准进行选择和验收，并严格控制其质量和尺寸。
对于C型钢的国标厚度，还需要考虑其与其他材料的配合使用。
在建筑和桥梁工程中，C型钢常常与混凝土、砖石等材料配合使用，需要考虑它们的相互作用和协调性。
合理选择C型钢国标厚度，可以保证结构的稳定性和安全性，避免出现材料失效和结构倒塌的情况。
在实际工程中，为了提高C型钢的使用效果和延长其使用寿命，还可以采取一些措施。
例如，可以进行防腐处理，以防止腐蚀和氧化；可以进行防火处理，以提高其耐火性能；可以进行加强加固，以增加其受力能力。
这些措施可以进一步保证C型钢的质量和安全性能。
C型钢国标厚度是根据国家标准规定的C型钢的标准厚度范围。
选择适当的国标厚度对于保证结构的强度和稳定性至关重要。
在实际应用中，需要综合考虑工程需求、负荷情况、经济性和可行性等因素，确保选择最佳的国标厚度。