布氏维氏硬度对照
洛氏硬度、布氏硬度、维氏硬度对照表
538 448 458 468 478 488 598 609 719 829 049 159 469 679 989 1001 5101 8201 2401 6501 0701 0801 0011 5111
0.942 0.252 0.552 0.852 0.162 0.462 0.862 0.172 0.472 0.872 0.182 0.582 0.982 0.292 0.692 0.003 0.403 0.803 0.213 0.613 0.023 0.423 0.923 0.333
0.833 0.243 0.743 0.253 0.753 0.263 0.763 0.273 0.773 0.283 0.883 0.393 0.993 0.504 0.114 0.714 0.324 0.924 0.634 0.344 0.944 0.654 0.364 0.074
723 233 633 143 543 053 553 063 563 073 573 083 583 193 693 104 704 314 424 034 634 244 944
7062 )aPM( σ 度强似近
0.317 0.627 0.937 0.257 0.667 0.087 0.597 0.018 0.528 0.048 0.658 0.278 0.988 0.609 0.329 0.149 0.959 0.879 0.799 0.7101 0.7301 VH 度硬氏维
2
ARH 度硬氏洛
度硬氏布
表 照 对 度 硬 氏 维 、 度 硬 氏布 、 度 硬 氏 洛
5361 2661 2961 2271 3571 5871 7181 1581 5881 1291 7591 5991 4302 4702 5112 7512 1022 7422 3922 1432 1932 3442 6942 1552
洛氏和布氏维氏硬度对照表
洛氏硬度、布氏硬度、维氏硬度对照表以下是洛氏硬度、布氏硬度、维氏硬度的常用范围值的对照表。
洛氏硬度HRC 洛氏硬度HRA 布氏硬度HB 30D2维氏硬度HV 近似强度σ(MPa)70.0 86.6 - 1037.0 --69.5 86.3 -1017.069.0 86.1 - 997.0 -68.5 85.8 - 978.0 -68.0 85.5 - 959.0 -67.5 85.2 - 941.0 -67.0 85 - 923.0 -66.5 84.7 - 906.0 -66.0 84.4 - 889.0 -65.5 84.1 - 872.0 -65.0 83.9 - 856.0 -64.5 83.6 - 840.0 -64.0 83.3 - 825.0 -63.5 83.1 - 810.0 -63.0 82.8 - 795.0 -62.5 82.5 - 780.0 -62.0 82.2 - 766.0 -61.5 82.0 - 752.0 -61.0 81.7 - 739.0 -60.5 81.4 - 726.0 -60.0 81.2 - 713.0 2607 59.5 80.9 - 700.0 2551 59.0 80.6 - 688.0 2496 58.5 80.3 - 676.0 2443 58.0 80.1 - 664.0 2391 57.5 79.8 - 653.0 2341 57.0 79.5 - 642.0 2293 56.5 79.3 - 631.0 2247 56.0 79.0 - 620.0 2201 55.5 78.7 - 609.0 2157 55.0 78.5 - 599.0 2115 54.5 78.2 - 589.0 2074 54.0 77.9 - 579.0 2034 53.5 77.7 - 570.0 1995 53.0 77.4 - 561.0 1957 52.5 77.1 551.0 1921 52.0 76.9 543.0 1885 51.5 76.6 534.0 1851 51.0 76.3 525.0 1817 50.5 76.1 517.0 1785 50.0 75.8 509.0 1753 49.5 75.5 501.0 1722 49.0 75.3 493.0 1692 48.5 75.0 485.0 1662 48.0 74.7 478.0 163547.5 74.5 470.0 1608 47.0 74.2 449 463.0 1581 46.5 73.9 442 456.0 1555 46.0 73.7 436 449.0 1529 45.5 73.4 430 443.0 1504 45.0 73.2 424 436.0 1480 44.5 72.9 413 429.0 1457 44.0 72.6 407 423.0 1434 43.5 72.4 401 417.0 1411 43.0 72.1 396 411.0 1389 42.5 71.8 391 405.0 1368 42.0 71.6 385 399.0 1347 41.5 71.3 380 393.0 1327 41.0 71.1 375 388.0 1307 40.5 70.8 370 382.0 1287 40.0 70.5 365 377.0 1268 39.5 70.3 360 372.0 1250 39.0 70.0 355 367.0 1232 38.5 69.7 350 362.0 1214 38.0 69.5 345 357.0 1197 37.5 69.2 341 352.0 1180 37.0 69.0 336 347.0 1163 36.5 68.7 332 342.0 1147 36.0 68.4 327 338.0 1131 35.5 68.2 323 333.0 111535.0 67.9 318 329.0 1100 34.5 67.7 314 324.0 1080 34.0 67.4 310 320.0 1070 33.5 67.1 306 316.0 1056 33.0 66.9 302 312.0 1042 32.5 66.6 298 308.0 1028 32.0 66.4 294 304.0 1015 31.5 66.1 291 300.0 1001 31.0 65.8 287 296.0 989 30.5 65.6 283 292.0 976 30.0 65.3 280 289.0 964 29.5 65.1 276 285.0 951 29.0 64.8 273 281.0 940 28.5 64.6 269 278.0 928 28.0 64.3 266 274.0 917 27.5 64.0 263 271.0 906 27.0 63.8 260 268.0 895 26.5 63.5 257 264.0 884 26.0 63.3 254 261.0 874 25.5 63.0 251 258.0 864 25.0 62.8 248 255.0 854 24.5 62.5 245 252.0 844 24.0 62.2 242 249.0 835 23.5 62.0 240 246.0 825 23.0 61.7 237 243.0 81622.5 61.5 234 240.0 80822.0 61.2 232 237.0 799以上数据摘自《实用五金手册》广东科技出版社，2004.3硬度试验是机械性能试验中最简单易行的一种试验方法。
布氏维氏硬度对照表
洛氏硬度、布氏硬度、维氏硬度对照表洛氏硬度（HRC）、布氏硬度（HB）等硬度对照区别和换算硬度是衡量材料软硬程度的一个性能指标。
硬度试验的方法较多，原理也不相同，测得的硬度值和含义也不完全一样。
最普通的是静负荷压入法硬度试验，即布氏硬度（HB）、洛氏硬度（HRA，HRB，HRC）、维氏硬度（HV），橡胶塑料邵氏硬度（HA,HD）等硬度其值表示材料表面抵抗坚硬物体压入的能力。
最流行的里氏硬度（HL）、肖氏硬度（HS）则属于回跳法硬度试验，其值代表金属弹性变形功的大小。
因此，硬度不是一个单纯的物理量，而是反映材料的弹性、塑性、强度和韧性等的一种综合性能指标。
钢材的硬度：金属硬度（Hardness）的代号为H。
按硬度试验方法的不同，•常规表示有布氏（HB）、洛氏（HRC）、维氏（HV）、里氏（HL）硬度等，其中以HB及HRC较为常用。
•HB应用范围较广，HRC适用于表面高硬度材料，如热处理硬度等。
两者区别在于硬度计之测头不同，布氏硬度计之测头为钢球，而洛氏硬度计之测头为金刚石。
•HV-适用于显微镜分析。
维氏硬度（HV）以120kg以内的载荷和顶角为136°的金刚石方形锥压入器压入材料表面，用材料压痕凹坑的表面积除以载荷值，即为维氏硬度值（HV）。
•HL手提式硬度计，测量方便，利用冲击球头冲击硬度表面后，产生弹跳；利用冲头在距试样表面1mm处的回弹速度与冲击速度的比值计算硬度，公式：里氏硬度HL=1000XVB（回弹速度）/VA（冲击速度）。
•目前最常用的便携式里氏硬度计用里氏（HL）测量后可以转化为：布氏（HB）、洛氏（HRC）、维氏（HV）、肖氏（HS）硬度。
或用里氏原理直接用布氏（HB）、洛氏（HRC）、维氏（HV）、里氏（HL）、肖氏（HS）测量硬度值。
时代公司生产的TH系列里氏硬度计就有此功能，是传统台式硬度机的有益补充！”（详细情况请点击《里氏硬度计TH140/TH160/HLN-11A/HS141便携式系列》）1、HB-布氏硬度：布氏硬度（HB）—般用于材料较软的时候，如有色金属、热处理之前或退火后的钢铁。
维布硬度转换表
维布硬度转换表
维氏硬度和布氏硬度对照表
一、维氏硬度（Vickers Hardness）
维氏硬度是一种通过测量材料表面抵抗压痕的能力来评估其硬度的测试方法。
它使用相对较小的力来产生压痕，通常在1-10公斤之间。
维氏硬度值的计算基于压痕的对角线长度。
单位：HV（维氏）
二、布氏硬度（Brinell Hardness）
布氏硬度测试是通过测量材料在一定压力下留下的凹痕直径来评估其硬度。
测试力较大，通常在200-3000公斤之间。
布氏硬度值的计算基于凹痕的直径。
单位：HBW（布氏）
三、单位换算
1HV = 10HBW
例如：如果一个材料的维氏硬度为600HV，那么它的布氏硬度就是6000HBW。
四、硬度转换表
由于维氏和布氏硬度的测量原理不同，它们之间没有直接的转换公式。
然而，可以通过比较已知硬度的标准物质的测试结果来建立转换表。
五、应用范围
维氏硬度测试主要用于测试较薄或较软的材料的硬度，如金属箔、镀层和涂层等。
而布氏硬度测试主要用于测试大块或较硬的材料，如铸铁、钢材和热处理后的金属等。
六、实验原理
1.维氏硬度：在固定的载荷下，将相对较小的金刚石锥压入试样表面，并保
持一定时间。
然后测量压痕的对角线长度，并根据公式计算维氏硬度值。
2.布氏硬度：在固定的载荷下，将一个硬质钢球压入试样表面，并保持一定
时间。
然后测量压痕的直径，并根据公式计算布氏硬度值。
七、实验步骤
1.准备样品：选择适合的样品，并确保其表面平整、无油污和氧化层。
洛氏硬度、布氏硬度、维氏硬度对照表
洛氏硬度、布氏硬度、维氏硬度对照表洛氏硬（HRC）洛氏硬(HRA) 布氏硬(HB 30D2)维氏硬(HV) 近似强度σ(MPa)70.0 86.6 -1037.0-69.5 86.3 -1017.0-69.0 86.1 -997.0-68.5 85.8 -978.0-68.0 85.5 -959.0-67.5 85.2 -941.0-67.0 85 -923.0-66.5 84.7 -906.0-66.0 84.4 -889.0-65.5 84.1 -872.0-65.0 83.9 -856.0-64.5 83.6 -840.0-64.0 83.3 -825.0-63.5 83.1 -810.0-63.0 82.8 -795.0-62.5 82.5 -780.0-62.0 82.2 -766.0-61.5 82.0 -752.0-61.0 81.7 -739.0-60.5 81.4 -726.0-60.0 81.2 -713.0260759.5 80.9 -700.0255159.0 80.6 -688.0249658.5 80.3 -676.0244358.0 80.1 -664.0239157.5 79.8 -653.0234157.0 79.5 -642.0229356.5 79.3 -631.0224756.0 79.0 -620.0220155.5 78.7 -609.0215755.0 78.5 -599.0211554.5 78.2 -589.0207454.0 77.9 -579.0203453.5 77.7 -570.0199553.0 77.4 -561.0195752.5 77.1 551.01921 洛氏硬（HRC）洛氏硬(HRA) 布氏硬(HB 30D2)维氏硬(HV) 近似强度σ(MPa)52.0 76.9 543.0188551.5 76.6 534.0185151.0 76.3 525.0181750.5 76.1 517.0178550.0 75.8 509.0175349.5 75.5 501.0172249.0 75.3 493.0169248.5 75.0 485.0166248.0 74.7 478.0163547.5 74.5 470.0160847.0 74.2 449463.0158146.5 73.9 442456.0155546.0 73.7 436449.0152945.5 73.4 430443.0150445.0 73.2 424436.0148044.5 72.9 413429.0145744.0 72.6 407423.0143443.5 72.4 401417.0141143.0 72.1 396411.0138942.5 71.8 391405.0136842.0 71.6 385399.0134741.5 71.3 380393.0132741.0 71.1 375388.0130740.5 70.8 370382.0128740.0 70.5 365377.0126839.5 70.3 360372.0125039.0 70.0 355367.0123238.5 69.7 350362.0121438.0 69.5 345357.0119737.5 69.2 341352.0118037.0 69.0 336347.0116336.5 68.7 332342.0114736.0 68.4 327338.0113135.5 68.2 323333.0111535.0 67.9 318329.0110034.5 67.7 314324.0108034.0 67.4 310320.0107033.5 67.1 306316.0105633.0 66.9 302312.01042 洛氏硬（HRC）洛氏硬(HRA) 布氏硬(HB 30D2)维氏硬(HV) 近似强度σ(MPa)32.5 66.6 298308.0102832.0 66.4 294304.0101531.5 66.1 291300.0100131.0 65.8 287296.098930.5 65.6 283292.097630.0 65.3 280289.096429.5 65.1 276285.095129.0 64.8 273281.094028.5 64.6 269278.092828.0 64.3 266274.091727.5 64.0 263271.090627.0 63.8 260268.089526.5 63.5 257264.088426.0 63.3 254261.087425.5 63.0 251258.086425.0 62.8 248255.085424.5 62.5 245252.084424.0 62.2 242249.083523.5 62.0 240246.082523.0 61.7 237243.081622.5 61.5 234240.080822.0 61.2 232237.0799以上数据摘自 《实用五金手册》 广东科技出版社，2004.3硬度试验是机械性能试验中最简单易行的一种试验方法。
布氏维氏硬度对照表
洛氏硬度、布氏硬度、维氏硬度对照表洛氏硬度（HRC）、布氏硬度（HB）等硬度对照区别和换算硬度是衡量材料软硬程度的一个性能指标。
硬度试验的方法较多，原理也不相同，测得的硬度值和含义也不完全一样。
最普通的是静负荷压入法硬度试验，即布氏硬度(HB)、洛氏硬度(HRA，HRB，HRC)、维氏硬度(HV)，橡胶塑料邵氏硬度(HA,HD)等硬度其值表示材料表面抵抗坚硬物体压入的能力。
最流行的里氏硬度（HL）、肖氏硬度(HS)则属于回跳法硬度试验，其值代表金属弹性变形功的大小。
因此，硬度不是一个单纯的物理量，而是反映材料的弹性、塑性、强度和韧性等的一种综合性能指标。
钢材的硬度：金属硬度(Hardness)的代号为H。
按硬度试验方法的不同，●常规表示有布氏（HB）、洛氏（HRC）、维氏（HV）、里氏（HL）硬度等，其中以HB及HRC较为常用。
●HB应用范围较广，HRC适用于表面高硬度材料，如热处理硬度等。
两者区别在于硬度计之测头不同，布氏硬度计之测头为钢球，而洛氏硬度计之测头为金刚石。
●HV-适用于显微镜分析。
维氏硬度(HV)以120kg以内的载荷和顶角为136°的金刚石方形锥压入器压入材料表面，用材料压痕凹坑的表面积除以载荷值，即为维氏硬度值(HV)。
●HL手提式硬度计，测量方便，利用冲击球头冲击硬度表面后，产生弹跳；利用冲头在距试样表面1mm处的回弹速度与冲击速度的比值计算硬度，公式：里氏硬度HL=1000×VB（回弹速度）/ VA（冲击速度）。
●目前最常用的便携式里氏硬度计用里氏（HL）测量后可以转化为：布氏（HB）、洛氏（HRC）、维氏（HV）、肖氏（HS）硬度。
或用里氏原理直接用布氏（HB）、洛氏（HRC）、维氏（HV）、里氏（HL）、肖氏（HS）测量硬度值。
时代公司生产的TH系列里氏硬度计就有此功能，是传统台式硬度机的有益补充！”（详细情况请点击《里氏硬度计TH140/TH160/HLN-11A/HS141便携式系列》）1、HB - 布氏硬度:布氏硬度(HB)一般用于材料较软的时候，如有色金属、热处理之前或退火后的钢铁。
布氏维氏硬度对照
洛氏硬度、布氏硬度、维氏硬度对照表洛氏硬度（HRC）、布氏硬度（HB）等硬度对照区别和换算硬度是衡量材料软硬程度的一个性能指标。
硬度试验的方法较多，原理也不相同，测得的硬度值和含义也不完全一样。
最普通的是静负荷压入法硬度试验，即布氏硬度(HB)、洛氏硬度(HRA，HRB，HRC)、维氏硬度(HV)，橡胶塑料邵氏硬度(HA,HD)等硬度其值表示材料表面抵抗坚硬物体压入的能力。
最流行的里氏硬度（HL）、肖氏硬度(HS)则属于回跳法硬度试验，其值代表金属弹性变形功的大小。
因此，硬度不是一个单纯的物理量，而是反映材料的弹性、塑性、强度和韧性等的一种综合性能指标。
钢材的硬度：金属硬度(Hardness)的代号为H。
按硬度试验方法的不同，●常规表示有布氏（HB）、洛氏（HRC）、维氏（HV）、里氏（HL）硬度等，其中以HB及HRC较为常用。
●HB应用范围较广，HRC适用于表面高硬度材料，如热处理硬度等。
两者区别在于硬度计之测头不同，布氏硬度计之测头为钢球，而洛氏硬度计之测头为金刚石。
●HV-适用于显微镜分析。
维氏硬度(HV)以120kg以内的载荷和顶角为136°的金刚石方形锥压入器压入材料表面，用材料压痕凹坑的表面积除以载荷值，即为维氏硬度值(HV)。
●HL手提式硬度计，测量方便，利用冲击球头冲击硬度表面后，产生弹跳；利用冲头在距试样表面1mm处的回弹速度与冲击速度的比值计算硬度，公式：里氏硬度HL=1000×VB（回弹速度）/ VA（冲击速度）。
●目前最常用的便携式里氏硬度计用里氏（HL）测量后可以转化为：布氏（HB）、洛氏（HRC）、维氏（HV）、肖氏（HS）硬度。
或用里氏原理直接用布氏（HB）、洛氏（HRC）、维氏（HV）、里氏（HL）、肖氏（HS）测量硬度值。
时代公司生产的TH系列里氏硬度计就有此功能，是传统台式硬度机的有益补充！”（详细情况请点击《里氏硬度计TH140/TH160/HLN-11A/HS141便携式系列》）1、HB - 布氏硬度:布氏硬度(HB)一般用于材料较软的时候，如有色金属、热处理之前或退火后的钢铁。
洛氏硬度、布氏硬度、维氏硬度对照表
洛氏硬度、布氏硬度、维氏硬度对照表
以上数据摘自《实用五金手册》广东科技出版社，2004.3
硬度试验是机械性能试验中最简单易行的一种试验方法。
为了能用硬度试验代替某些机械性能试验，生产上需要一个比较准确的硬度和强度的换算关系。
实践证明，金属材料的各种硬度值之间，硬度值与强度值之间具有近似的相应关系。
因为硬度值是由起始塑性变形抗力和继续塑性变形抗力决定的，材料的强度越高，塑性变形抗力越高，硬度值也就越高。
- 1、下载文档前请自行甄别文档内容的完整性，平台不提供额外的编辑、内容补充、找答案等附加服务。
- 2、"仅部分预览"的文档,不可在线预览部分如存在完整性等问题,可反馈申请退款(可完整预览的文档不适用该条件!)。
- 3、如文档侵犯您的权益，请联系客服反馈,我们会尽快为您处理(人工客服工作时间：9:00-18:30)。
洛氏硬度、布氏硬度、维氏硬度对照表
洛氏硬度（HRC）、布氏硬度（HB）等硬度对照区别和换算
硬度是衡量材料软硬程度的一个性能指标。
硬度试验的方法较多，原理也不相同，测得的硬度值和含义也不完全一样。
最普通的是静负荷压入法硬度试验，即布氏硬度(HB)、洛氏硬度(HRA，HRB，HRC)、维氏硬度(HV)，橡胶塑料邵氏硬度(HA,HD)等硬度其值表示材料表面抵抗坚硬物体压入的能力。
最流行的里氏硬度（HL）、肖氏硬度(HS)则属于回跳法硬度试验，其值代表金属弹性变形功的大小。
因此，硬度不是一个单纯的物理量，而是反映材料的弹性、塑性、强度和韧性等的一种综合性能指标。
钢材的硬度：金属硬度(Hardness)的代号为H。
按硬度试验方法的不同，
●常规表示有布氏（HB）、洛氏（HRC）、维氏（HV）、里氏（HL）硬度等，其中以HB及HRC较为常用。
●HB应用范围较广，HRC适用于表面高硬度材料，如热处理硬度等。
两者区别在于硬度计之测头不同，布
氏硬度计之测头为钢球，而洛氏硬度计之测头为金刚石。
●HV-适用于显微镜分析。
维氏硬度(HV)以120kg以内的载荷和顶角为136°的金刚石方形锥压入器压入材
料表面，用材料压痕凹坑的表面积除以载荷值，即为维氏硬度值(HV)。
●HL手提式硬度计，测量方便，利用冲击球头冲击硬度表面后，产生弹跳；利用冲头在距试样表面1mm处的回弹速度与冲击速度的比值计算硬度，公式：里氏硬度HL=1000×VB（回弹速度）/ VA（冲击速度）。
●目前最常用的便携式里氏硬度计用里氏（HL）测量后可以转化为：布氏（HB）、洛氏（HRC）、维氏（HV）、肖氏（HS）硬度。
或用里氏原理直接用布氏（HB）、洛氏（HRC）、维氏（HV）、里氏（HL）、肖氏（HS）测量硬度值。
时代公司生产的TH系列里氏硬度计就有此功能，是传统台式硬度机的有益补充！”（详细情况请点击《里氏硬度计TH140/TH160/HLN-11A/HS141便携式系列》）
1、HB - 布氏硬度:
布氏硬度(HB)一般用于材料较软的时候，如有色金属、热处理之前或退火后的钢铁。
洛氏硬度(HRC)一般用于硬度较高的材料，如热处理后的硬度等等。
布式硬度(HB)是以一定大小的试验载荷，将一定直径的淬硬钢球或硬质合金球压入被测金属表面，保持规定时间，然后卸荷，测量被测表面压痕直径。
布式硬度值是载荷除以压痕球形表面积所得的商。
一般为：以一定的载荷(一般3000kg)把一定大小(直径一般为10mm)的淬硬钢球压入材料表面，保持一段时间，去载后，负荷与其压痕面积之比值，即为布氏硬度值(HB)，单位为公斤力/mm2(N/mm2)。
（关于布式硬度(HB)详细情况请点击《布氏硬度机(计)HB-3000B/TH600》）
2、HR-洛式硬度
洛式硬度（HR-）是以压痕塑性变形深度来确定硬度值指标。
以0.002毫米作为一个硬度单位。
当HB>450或者试样过小时，不能采用布氏硬度试验而改用洛氏硬度计量。
它是用一个顶角120°的金刚石圆锥体或直径为1.59、3.18mm的钢球，在一定载荷下压入被测材料表面，由压痕的深度求出材料的硬度。
根据试验材料硬度的不同，分三种不同的标度来表
示：
HRA：是采用60kg载荷和钻石锥压入器求得的硬度，用于硬度极高的材料(如硬质合金等)。
HRB：是采用100kg载荷和直径1.59mm淬硬的钢球，求得的硬度，用于硬度较低的材料(如退火钢、铸铁等)。
HRC：是采用150kg载荷和钻石锥压入器求得的硬度，用于硬度很高的材料(如淬火钢等)。
另外：
(1)HRC含意是洛式硬度C标尺，
(2)HRC和HB在生产中的应用都很广泛
(3)HRC适用范围HRC 20－－67，相当于HB225－－650
若硬度高于此范围则用洛式硬度A标尺HRA。
若硬度低于此范围则用洛式硬度B标尺HRB。
布式硬度上限值
HB650,不能高于此值。
(4)洛氏硬度计C标尺之压头为顶角120度的金刚石圆锥，试验载荷为一确定值，中国标准是150公斤力。
布氏硬度计之压头为淬硬钢球（HBS)或硬质合金球（HBW），试验载荷随球直径不同而不同，从3000到31.25
公斤力。
(5)洛式硬度压痕很小，测量值有局部性，须测数点求平均值，适用成品和薄片，归于无损检测一类。
布式硬度压痕较大，测量值准，不适用成品和薄片，一般不归于无损检测一类。
(6)洛式硬度的硬度值是一无名数，没有单位。
（因此习惯称洛式硬度为多少度是不正确的。
）
布式硬度的硬度值有单位，且和抗拉强度有一定的近似关系。
(7)洛式硬度直接在表盘上显示、也可以数字显示，操作方便，快捷直观，适用于大量生产中。
布式硬度需要用显微镜测量压痕直径，然后查表或计算，操作较繁琐。
(8)在一定条件下，HB与HRC可以查表互换。
其心算公式可大概记为：1HRC≈1/10HB。
（关于洛氏硬度
机详细情况请点击《洛氏硬度机(计)HR-150A/TH300/TH500/TH320/TH301/TH310系列》）下面是几种常见的对照关系表：1<<国家标准硬度HLD/HRC/HRB/HV/HB/HSD转换换算表副本>>
2根据德国标准DIN50150,以下是常用范围的钢材抗拉强度与维氏硬度、布氏硬度、洛氏硬度的对照表：
[注]表三来源：美国巴勃·考曼(Baber Colman)公司4其他硬度对照表:
■钢的布氏硬度的近似换算值
硬度试验是机械性能试验中最简单易行的一种试验方法。
为了能用硬度试验代替某些机械性能试验，生产上需要一个比较准确的硬度和强度的换算关系。
实践证明，金属材料的各种硬度值之间，硬度值与强度值之间具有近似的相应关系。
因为硬度值是由起始塑性变形抗力和继续塑性变形抗力决定的，材料的强度越高，塑性变形抗力越高，硬度
值也就越高。