超塑性的研究与发展精品PPT课件

processing in 1928.
In 1934, Pearson dramatically demonstrated, using a Bi-Sn sample that had been deformed to nearly 2000% and then coiled (as shown in Figure 2.4), that unusually large elongations could be achieved in certain fine-structured, twophase materials.
11
2 超塑性研究的发展概况
2.1 Before 1962
✓Work in the Soviet Union was underway to specifically address the phenomenon,
and Bochvar and Sviderskaya coined the term sverhplastichnost (ultrahigh plasticity)
3
一、超塑性的研究与发展
4
内容提要
1 超塑性的概念 2 超塑性研究的发展概况 3 超塑性的分类 4 超塑性成形的优点与问题 5 超塑成形应用实例
5
1 超塑性的概念
塑性：
是金属的重要属性之一，它指的是金属在外力作用下，无损而永久地改变形状的能力[1]。
超塑性：
（1）金属和合金在特定组织结构和变形温度速度条件下，可以呈现异常高的塑性，延伸率可 达百分之几百，甚至达百分之一千或二千以上，变形抗力也很小，这种现象称为超塑性[1]。
金属特种加工理论与技术
金属超塑性成形理论与技术
（16课时）
叶凌英
材料加工工程系
2015年4月
1
课程内容
一、超塑性的研究与发展 二、超塑性变形的力学特性 三、超塑性变形的组织特性 四、组织超塑性变形机理 五、金属材料的超塑性
2
参考书目
(1) Nieh T G, Wadsworth J, Sherby O D. Superplasticity in metals and ceramics, Cambridge: Cambridge University Press, 1997
9
2 超塑性研究的发展概况
2.1 Before 1962
10
2 超塑性研究的发展概况
2.1 Before 1962
Jenkins, for example, achieved

elongations of 300 to 400% in
Cd-Zn and Pb-Sn eutectics
after
thermomechanical
6
1 超塑性的概念
ICSAM：the 1991 International Conference on Superplasticity in Advanced Materials (ICSAM-91) held in Osaka, Japan
7
1 超塑性的概念
8
2 超塑性研究的发展概况
2.1 Before 1962
Ancient arsenic bronzes containing up to 10 wt% arsenic, which were used in Turkey in the early Bronze Age, could have been superplastic. This is because the materials are two-phase alloys that may have developed the required stable, fine grained structure during hand-forging of intricate shapes. Furthermore, the ancient steels of Damascus, in use from 300 B.C. to the late nineteenth century, are similar in composition to modern ultrahigh-carbon steels that have recently been developed, in large part, for their superplastic characteristics.
[1]吴诗惇. 金属超塑性变形理论，北京，国防工业出版社，1997 [2]Nieh T G, Wadsworth J, Sherby O D. Superplasticity in metals and ceramics, Cambridge: Cambridge University Press, 1997 [3]文九巴，杨蕴林，杨永顺，陈拂晓，张柯柯，张耀宗. 超塑性应用技术，北京，机械工业出版社，2005
（2）Superplasticity is the ability of a polycrystalline material to exhibit, in a generally isotropic manner, very high tensile elongations prior to failure[2].
（3）超塑性是指材料在拉伸条件下，表现出异常高的伸长率而不产生颈缩与断裂现象。当伸 长率大于100%时，即可称为超塑性[3]。一般金属伸长率（δ）均小于100%，如黑色金不大于 40%，有色金属不超过60—80%，即使在高温下也难达到100%，而具有超塑性的金属在超塑 性条件下δ可达100%以上，变形抗力还很小，如难变形材料Bi-44Sn及Ti-6Al-4V钛合金在超塑 性条件下δ值分别为1900%和500%以上，常用铝合金δ达到200-2000%；普碳钢δ为150-200%， 滚动轴承刚δ最大值约为500%，流动应力比常规变形的小到几分之一乃到几十分之一。
(2) 陈浦泉. 组织超塑性，哈尔滨，哈尔滨工业大学出版社，1988 (3) 吴诗惇. 金属超塑性变形理论，北京，国防工业出版社，1997 (4) 文九巴，杨蕴林，杨永顺，陈拂晓，张柯柯，张耀宗. 超塑性应用
技术，北京，机械工业出版社，2005 (5) 李云江，特种塑性成形，北京，机械工业出版社，2008