16MnR 低合金钢钢板GB665410012045027515015014713812511310610093664315MnVR 低合金钢钢板GB665468550390183183183183183172159147---15MnVR 低合金钢钢板GB6654616530390177177177177177172159147---15MnVR 低合金钢钢板GB66541636510370170170170170170163150138---15MnVR 低合金钢钢板GB66543660490350163163163163163153141131---15MnVNR 低合金钢钢板GB6654616570440190190190190190190175163---15MnVNR 低合金钢钢板GB66541636550420183183183183183181169156---15MnVNR 低合金钢钢板GB66543660530400177177177177177172159147---18MnMoNbR 低合金钢钢板GB6654306059044019719719719719719719719719717711718MnMoNbR 低合金钢钢板GB66541610057041019019019019019019019019019017711713MnNiMoNbR 低合金钢钢板GB665430100570390190190190190190190190190---13MnNiMoNbR 低合金钢钢板GB6654100120570380190190190190190190190188---07MnCrMoVR 低合金钢钢板-1650610490203203203203203203203----16MnDR 低合金钢钢板GB3531616490315163163163156144131122----16MnDR 低合金钢钢板GB35311636470295157157156147134122113----16MnDR 低合金钢钢板GB35313660450275150150147138125113106----16MnDR 低合金钢钢板GB353160100450255150147138128116106100----07MnNiCrMoVDR 低合金钢钢板-1650610490203203203203203203203----15MnNiDR 低合金钢钢板GB3531616490325163163---------15MnNiDR 低合金钢钢板GB35311636470305157157---------15MnNiDR低合金钢钢板GB35313660460290153153---------09Mn2VDR 低合金钢钢板GB3531616440290147147---------09Mn2VDR 低合金钢钢板GB35311636430270143143---------09MnNiDR 低合金钢钢板GB3531616440300147147147147147147138----09MnNiDR 低合金钢钢板GB35311636430280143143143143143138128----09MnNiDR 低合金钢钢板GB35313660430260143143143141134128119----15CrMoR 低合金钢钢板GB665466045029515015015015014113112511811511211015CrMoR 低合金钢钢板GB66546010045027515015014713813112311611010710410314Cr1MoR 低合金钢钢板-161205153101721721691591531441381311271221160Cr13A1高合金钢钢板GB4237215--1181051011009997959087--0Cr13高合金钢钢板GB4237260--137126123120119117112109105100890Cr18Ni9高合金钢钢板GB4237260--1371371371301221141111071051031010Cr18Ni9高合金钢钢板GB4237260--13711410396908582797876750Cr18Ni10Ti 高合金钢钢板GB4237260--1371371371301221141111081061051040Cr18Ni10Ti 高合金钢钢板GB4237260--13711410396908582807978770Cr17Ni12Mo2高合金钢钢板GB4237260--1371371371341251181131111101091080Cr17Ni12Mo2高合金钢钢板GB4237260--13711710799938784828181800Cr18Ni12Mo2Ti 高合金钢钢板GB4237260--1371371371341251181131111101091080Cr18Ni12Mo2Ti 高合金钢钢板GB4237260--13711710799938784828181800Cr19Ni13Mo3高合金钢钢板GB4237260--1371371371341251181131111101091080Cr19Ni13Mo3高合金钢钢板GB4237260--137117107999387848281818000Cr19Ni10高合金钢钢板GB4237260--11811811811010398949189--00Cr19Ni10高合金钢钢板GB4237260--1189787817673696766--00Cr17Ni14Mo2高合金钢钢板GB4237260--1181181171081009590868584-00Cr17Ni14Mo2高合金钢钢板GB4237260--118978780747067646362-00Cr19Ni13Mo3高合金钢钢板GB4237260--118118118118118118113111110109-00Cr19Ni13Mo3高合金钢钢板GB4237260--11811710799938784828181-00Cr18Ni5Mo3Si2高合金钢钢板GB4237225--197197190173167163-----10碳素钢钢管GB8163103352051121121081019283777169614110碳素钢钢管GB9948163352051121121081019283777169614110碳素钢钢管GB6479163352051121121081019283777169614110碳素钢钢管GB64791740335195112110104988979746866614120碳素钢钢管GB816310390245130130130123110101928683614120碳素钢钢管GB994816410245137137132123110101928683614120G 碳素钢钢管GB647916410245137137132123110101928683614120G 碳素钢钢管GB6479174041023513713212611610495867978614116Mn 低合金钢钢管GB64791649032016316316315914713512611993664316Mn 低合金钢钢管GB6479174049031016316316315311112911911693664315MnV 低合金钢钢管GB647916510350170170170170166153141129---15MnV 低合金钢钢管GB64791740510340170170170170159147135126---09MnD 低合金钢钢管-164002401331331281191069788----12CrMo 低合金钢钢管GB9948164102051281131081019589837775747212CrMo低合金钢钢管GB6479164102051281131081019589837775747212CrMo 低合金钢钢管GB64791740410195122110104989286797472716915CrMo 低合金钢钢管GB994816440235147132123116110101958987868315CrMo 低合金钢钢管GB647916440235147132123116110101958987868315CrMo 低合金钢钢管GB6479174044022514112611611010495898684838112Cr1MoVG 低合金钢钢管GB5310164702551471441351261191101049896959210MoWVNb 低合金钢钢管GB64791647029515715715715615314714113513012612110MoWVNb 低合金钢钢管GB6479174047028515715715615014714113512912411911112Cr2Mo 低合金钢钢管GB64791645028015015015014714414113813413112811912Cr2Mo 低合金钢钢管GB647917404502701501501471411381341311281261231191Cr5Mo 低合金钢钢管GB647916390195122110104101989592898786831Cr5Mo 低合金钢钢管GB647917403901951161049895928986838179780Cr13高合金钢钢管GB/T1497618--137126123120119117112109105100890Cr18Ni9高合金钢钢管GB1329613--1371371371301221141111071051031010Cr18Ni9高合金钢钢管GB/T1497618--13711410396908582797876750Cr18Ni10Ti 高合金钢钢管GB1329613--1371371371301221141111081061051040Cr18Ni10Ti 高合金钢钢管GB/T1497618--13711410396908582807978770Cr17Ni12Mo2高合金钢钢管GB1329613--1371371371341251181131111101091080Cr17Ni12Mo2高合金钢钢管GB/T1497618--13711710799938784828181800Cr18Ni12Mo2Ti 高合金钢钢管GB1329613--1371371371341251181131111101091080Cr18Ni12Mo2Ti 高合金钢钢管GB/T1497618--13711710799938784828181800Cr19Ni13Mo3高合金钢钢管GB1329613--1371371371341251181131111101091080Cr19Ni13Mo3高合金钢钢管GB/T1497618--137117107999387848281818000Cr19Ni10高合金钢钢管GB1329613--11811811811010398949189--00Cr19Ni10高合金钢钢管GB/T1497618--1189787817673696766--00Cr17Ni14Mo2高合金钢钢管GB1329613--1181181171081009590868584-00Cr17Ni14Mo2高合金钢钢管GB/T1497618--118978780747067646362-00Cr19Ni13Mo3高合金钢钢管GB1329613--118118118118118118113111110109-00Cr19Ni13Mo3高合金钢钢管GB/T1497618--11811710799938784828181-20碳素钢锻件JB47261003702151231191131049586797472614135碳素钢锻件JB4726100510265166147141129116108989285614135碳素钢锻件JB4726100300490255159144138126113104958985614116Mn 低合金钢锻件JB472630045027515015014713512911611010493664315MnV 低合金钢锻件JB4726300470315157157157156147135126113---20MnMo 低合金钢锻件JB47263005303701771771771771771771711631561318420MnMo 低合金钢锻件JB47263005005103551701701701701701691631531471318420MnMo 低合金钢锻件JB47265007004903401631631631631631631591501441318420MnMoNb 低合金钢锻件JB472630062047020720720720720720720720717711720MnMoNb 低合金钢锻件JB472630050061046020320320320320320320320317711716MnD 低合金钢锻件JB4727300450275150150147135129116110---09Mn2VD 低合金钢锻件JB4727200420260140140---------09MnNiD 低合金钢锻件JB4727300420260140140140140134128119----16MnMoD低合金钢锻件JB4727300510355170170170170170169163----20MnMoD 低合金钢锻件JB4727300530370177177177177177177171----20MnMoD 低合金钢锻件JB4727300500510355170170170170170169163----20MnMoD 低合金钢锻件JB4727500700490340163163163163163163159----08MnNiCrMoVD 低合金钢锻件JB4727300600480200200200200200200200----10Ni3MoVD 低合金钢锻件JB4727300610490203203---------15CrMo 低合金钢锻件JB472630044027514714714713813212311611010710410315CrMo 低合金钢锻件JB47263005004302551431431351261191101049896959335CrMo 低合金钢锻件JB472630062044020720720720720720720720019415011135CrMo 低合金钢锻件JB472630050061043020320320320320320320320019415011112Cr1MoV 低合金钢锻件JB47263004402551471441351261191101049896959212Cr1MoV 低合金钢锻件JB47263005004302451431411311261191101049896959212Cr2Mo1低合金钢锻件JB472630051031017017016916315915615315014714411912Cr2Mo1低合金钢锻件JB47263005005003001671671661591561531501471441411191Cr5Mo 低合金钢锻件JB4726500590390197197197197197197197190136107830Cr13高合金钢锻件JB4728100--137126123120119117112109105100890Cr18Ni9高合金钢锻件JB4728200--1371371371301221141111071051031010Cr18Ni9高合金钢锻件JB4728200--13711410396908582797876750Cr18Ni10Ti 高合金钢锻件JB4728200--1371371371301221141111081061051040Cr18Ni10Ti 高合金钢锻件JB4728200--13711410396908582807978770Cr17Ni12Mo2高合金钢锻件JB4728200--1371371371341251181131111101091080Cr17Ni12Mo2高合金钢锻件JB4728200--137117107999387848281818000Cr19Ni10高合金钢锻件JB4728200--11711711711010398949189--00Cr19Ni10高合金钢锻件JB4728200--1179787817673696766--00Cr17Ni14Mo2高合金钢锻件JB4728200--1171171171081009590868584-00Cr17Ni14Mo2高合金钢锻件JB4728200--117978780747067646362-00Cr18Ni5Mo3Si2高合金钢锻件JB4728100--197197178163156153-----℃）下的许用应力，MPa---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98885837------GB150-98885837------GB150-98885837------GB150-98---------GB150-987253382616----GB150-981009891796452423227GB150-98允许产生微量变形场合747371676252423227GB150-9810310183584433251813GB150-98允许产生微量变形场合767574584433251813GB150-98107106105968165503830GB150-98允许产生微量变形场合797878767365503830GB150-98107--------GB150-98允许产生微量变形场合79--------GB150-98107106105968165503830GB150-98允许产生微量变形场合797878767365503830GB150-98---------GB150-98允许产生微量变形场合---------GB150-98---------GB150-98允许产生微量变形场合---------GB150-98---------GB150-98允许产生微量变形场合---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-987150-------GB150-987150-------GB150-986850-------GB150-98815837------GB150-98815837------GB150-98795837------GB150-9889825735-----GB150-9897--------GB150-9897--------GB150-9889614637-----GB150-9889614637-----GB150-986246352618----GB150-986246352618----GB150-987253382616----GB150-981009891796452423227GB150-98允许产生微量变形场合747371676252423227GB150-9810310183584433251813GB150-98允许产生微量变形场合767574584433251813GB150-98107106105968165503830GB150-98允许产生微量变形场合797878767365503830GB150-98107--------GB150-98允许产生微量变形场合79--------GB150-98107106105968165503830GB150-98允许产生微量变形场合797878767365503830GB150-98---------GB150-98允许产生微量变形场合---------GB150-98---------GB150-98允许产生微量变形场合---------GB150-98---------GB150-98允许产生微量变形场合---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-9849--------GB150-9849--------GB150-9849--------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98---------GB150-98885837------GB150-98885837------GB150-987950-------GB150-987950-------GB150-9889825735-----GB150-9889825735-----GB150-9889614637-----GB150-9889614637-----GB150-986246352618----GB150-987253382616----GB150-981009891796452423227GB150-98允许产生微量变形场合747371676252423227GB150-9810310183584433251813GB150-98允许产生微量变形场合767574584433251813GB150-98107106105968165503830GB150-98允许产生微量变形场合797878767365503830GB150-98---------GB150-98允许产生微量变形场合---------GB150-98---------GB150-98允许产生微量变形场合---------GB150-98---------GB150-98。
PA66 聚酰胺66或尼龙66 典型应用范围
PA66 聚酰胺66或尼龙66 典型应用范围:同PA6相比，PA66更广泛应用于汽车工业、仪器壳体以及其它需要有抗冲击性和高强度要求的产品。
注塑模工艺条件:干燥处理：如果加工前材料是密封的，那么就没有必要干燥。
然而，如果储存容器被打开，那么建议在85C的热空气中干燥处理。
如果湿度大于0.2%，还需要进行105C，12小时的真空干燥。
熔化温度：260~290C。
对玻璃添加剂的产品为275~280C。
熔化温度应避免高于300C。
模具温度：建议80C。
模具温度将影响结晶度，而结晶度将影响产品的物理特性。
对于薄壁塑件，如果使用低于40C的模具温度，则塑件的结晶度将随着时间而变化，为了保持塑件的几何稳定性，需要进行退火处理。
注射压力：通常在750~1250bar，取决于材料和产品设计。
注射速度：高速（对于增强型材料应稍低一些）。
流道和浇口:由于PA66的凝固时间很短，因此浇口的位置非常重要。
浇口孔径不要小于0.5*t （这里t为塑件厚度）。
如果使用热流道，浇口尺寸应比使用常规流道小一些，因为热流道能够帮助阻止材料过早凝固。
如果用潜入式浇口，浇口的最小直径应当是0.75mm。
化学和物理特性: PA66在聚酰胺材料中有较高的熔点。
它是一种半晶体-晶体材料。
PA66在较高温度也能保持较强的强度和刚度。
PA66在成型后仍然具有吸湿性，其程度主要取决于材料的组成、壁厚以及环境条件。
在产品设计时，一定要考虑吸湿性对几何稳定性的影响。
为了提高PA66的机械特性，经常加入各种各样的改性剂。
玻璃就是最常见的添加剂，有时为了提高抗冲击性还加入合成橡胶，如EPDM和SBR等。
PA66的粘性较低，因此流动性很好（但不如PA6）。
这个性质可以用来加工很薄的元件。
它的粘度对温度变化很敏感。
PA66的收缩率在1%~2%之间，加入玻璃纤维添加剂可以将收缩率降低到0.2%~1% 。
收缩率在流程方向和与流程方向相垂直方向上的相异是较大的。
PA66对许多溶剂具有抗溶性，但对酸和其它一些氯化剂的抵抗力较弱。
Nylon66
NYLON-66基本資料英文全名：NYLON-66中文名稱：尼龍66顏色：乳白色透明特性：1.機械性佳但不易加工。
2.對於烴類具有特別良好之抗性。
3.在低溫和滴溼度狀態下為相當良好之絕緣體。
機械特性降服點抗拉應力：80MPa斷裂伸長率：80～100%拉身模數：3000MPa衝擊強度（乾燥）：1.3熱物性質熱膨脹係數：10×10^-5cm-cm℃^-1熔點：250℃成形加工性黏度表現：黏度隨剪切速率增加而減少。
比重：1.14機械加工性：不易用途說明機械方面：齒輪、凸輪、軸承、軸襯及閥座。
日用品方面：直徑小於0.0035in粗細毛刷。
其他方面：釣魚之釣線。
NYLON-66加工問題處理方法成型品的黏膜1.增加脫模黏度。
2.整成型時間（降低模具溫度、延長冷卻時間、降低射出壓力、減短保壓時間等）。
收縮翹曲1.設計多點的料門。
2.模具溫度均一。
3.調整成型條件(提高樹指溫度、模具溫度、降低射出壓力)。
4.脫模頂出力要平均。
色班1.顏料要充分混合(通過押出機等)。
2.料門變化，色班位置也會變化。
3.改變顏料的配色。
熱處理條件成型品常有應力殘留的問題，是因為射出時的配向級等卻過程時的收縮不均一，必須要經過適當的熱處理(annealing)；主要技術是退火處理，即將產品放置在較熱變形溫度低10~15℃的環境下放置3~5小時，並控制退火爐內溫度的平均分佈。
NYLON66流變性質暨熱物性質一、流變性質黏度(viscosity)是一種流對流體所產生抵抗的指標。
在牛頓黏度定律中，黏度的定義為:對牛頓流體而言(例如:水)，黏度為一常數。
然而，對高分子熔液來說，黏度卻隨其分子受到剪應變率的增加而減少，此種現象，稱為高分子的「剪稀薄特性(Shear Thinning)」。
為何高分子黏度會隨剪應變率的增加而減少？這是由於高分子在不受外力的作用下，分子鏈以隨機(random)方式纏在一起，此時高分子對流動的抵抗較大，同時高分子也會呈現較大的黏度。
材料许用应力表A
表A.1钢管材料许用应力单位为MPa
表A.1钢管材料许用应力表（续）单位为MPa
表A.1钢管材料许用应力表（续）单位为MPa
表A.1钢管材料许用应力表（续）单位为MPa
表A.2 钢板材料许用应力单位为MPa
表A.2 钢板材料许用应力表（续）单位为MPa
表A.3 螺栓材料许用应力表单位为MPa
精品文档
表B.6 符合ASME B31.1标准材料的许用应力表单位为MPa
表B.6 符合ASME B31.1标准材料的许用应力表(续) 单位为MPa
表B.6 符合ASME B31.1标准材料的许用应力表(续) 单位为MPa
表B.7 符合ASME B31.1标准材料的许用应力表(续) 单位为MPa
表B.7 符合EN 10216-2标准材料的许用应力表
表B.7 符合EN 10216-2标准材料的许用应力表
精品文档。
尼龙66
尼龙66化工本1202班18号冯旭楞Ⅰ简介中文别名：锦纶66短纤维；聚己二酰己二胺；尼龙-66；尼龙66树脂；聚酰胺-66；聚已二酰己二胺；锦纶-66。
尼龙66疲劳强度和钢性较高，耐热性较好，摩擦系数低，耐磨性好，但吸湿性大，尺寸稳定性不够。
通常应用于中等载荷，使用温度<100-120度无润滑或少润滑条件下工作的耐磨受力传动零件。
Ⅱ热性质熔点（Tm）熔点即结晶熔解时的温度，对结晶性高分子尼龙-66，显示清晰的熔点，根据采用的测试方法，熔点在259~267℃的范围内波动。
通常采用差热分析（DTA）法测出的尼龙-66的熔点为264℃。
实际上，尼龙-66的熔点可以根据结晶的熔融热（ΔH）和熔融熵（ΔS）计算出来：尼龙-66的ΔH为4390.3J/mol，ΔS为8.37J/kmol，Tm的理论值为259.3℃[ ]。
如果将体积膨胀系数显示极大值的温度当作熔点，则尼龙-66的熔点温度范围为246~263℃。
接近理论熔解温度259℃。
玻璃化温度（Tg）高分子的比容和比热容等温度特性值在某一温度可出现不规则的变化，这一温度就是玻璃化转变温度，是分子链的链段克服分子间力开始运动的温度。
在这一温度附近，模量、振动频率、介电常数等也开始发生变化。
尼龙-66的玻璃化温度，与测试方法、试样中的水分含量、单体浓度、结晶度等因素有关。
Wilhoit和Dole等从比热容的温度变化分析，认为尼龙-66的玻璃化温度为47℃[ ]，而Rybnikar则在低温下测定了尼龙-66的比容，发现在尼龙-66在-65℃也有一个转变温度[ ]。
物理性能比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米成型收缩率：PA6 0.8-2.5% ，PA66 1.5-2.2%干燥条件：100-110℃/12小时坚韧、耐磨、耐油、,耐水、抗酶菌、但吸水大燃烧鉴别方法：火焰上端黄色，下端蓝色，燃烧后塑料熔滴落，起泡，离火后特殊的羊毛，指甲烧焦味和带芹菜味尼龙6：弹性好，冲击强度，吸水较大尼龙66：性能优于尼龙6，强度高，耐磨性好尼龙610：与尼龙66相似，但吸水小，刚度低尼龙1010：半透明，吸水小。
许用应力
钢号
钢板标准 使用状态
厚度 mm
常温强度指标
在下列温度下的许用应力，MPa
备注
σb MPa
σs MPa
《20 100
150 200 250 300 350
400 425 450 475
500 525
550 575
600
碳素钢钢板
GB 912
3～4 375 235 113 113 113 105 94 86 77 — — — — — — — — — 1）
0Cr18Ni10Ti GB 4237 固溶
2～60
137 137 137 130 122 114 111 108 106 105 104 103 101 83 58 44 2） 137 114 103 96 90 85 82 80 79 78 77 76 75 74 58 44
0Cr17Ni12Mo2 GB 4237 固溶
2～25
197 197 190 173 167 163 — — — — — — — — — —
钢号
钢板标准
10
GB 8163
10
GB 9948
10
GB 6479
20
GB 8163
20
GB 9948
20G
GB 6479
16Mn
GB 6479
0Cr13 0Cr18Ni9
GB 14976 GB 13296 GB 14976
≤16 335 205 112 112 108 101 92 83 77 71 69 61 41 — — — — —
≤16 335 205 112 112 108 101 92 83 77 71 69 61 41 — — — — —
尼龙66／MWGF复合材料的力学性能研究
尼龙66／MWGF复合材料的力学性能研究以硅烷偶联剂（KH550）为粘合剂，将酸化后的多壁碳纳米管接枝到玻璃纤维表面，制备出玻纤/碳纳米管复合填料（MWGFs）。
将不同含量的玻纤和复合填料添加到尼龙66中，分别制备出PA66/GF和PA66/MWGF复合材料，然后对复合材料的力学性能，热性能进行了测试分析。
结果表明，GF和MWGF都能够显著增强尼龙66的力学性能。
在拉伸性能方面，PA66/MWGF复合材料要高于PA66/GF复合材料，但PA66/GF复合材料缺口冲击性能则明显好于PA66/MWGF复合材料。
在热性能研究中，我们发现GF和MWGF都能够提高尼龙66的结晶温度。
但在结晶度影响上，GF的添加能够提高尼龙66的结晶度，而MWGF则相反，它的加入略微降低了尼龙66的结晶度。
标签：尼龙66；复合材料；碳纳米管；玻纤；力学性能Abstract：With silane coupling agent （KH550）as binder，glass fiber/carbon nanotube composite fillers （MWGFs）were prepared by grafting acidified multi-walled carbon nanotubes onto glass fiber surface. PA66/GF and PA66/MWGF composite materials were prepared by adding different contents of glass fiber and composite fillers into nylon 66. The mechanical and thermal properties of PA66/GF and PA66/MWGF composites were tested and analyzed. The results showed that both GF and MWGF could significantly enhance the mechanical properties of nylon 66. The tensile strength of PA66/MWGF composite is higher than that of PA66/GF composite materials，but the notched impact strength of PA66/GF composite is better than that of PA66/MWGF composite. In the study of thermal properties，we found that both GF and MWGF could increase the crystallization temperature of nylon 66. However，the addition of GF can improve the crystallinity of nylon 66，while MWGF can decrease the crystallinity of nylon 66 slightly.Keywords：nylon 66；composite materials；carbon nanotubes；glass fiber；mechanical properties由于具有良好的力学性能及独特的电性能、热性能，碳纳米管一经发现就受到各国科研人員的广泛关注[1]。
常用塑料的注塑工艺参数――尼龙66(精)
常用塑料的注塑工艺参数——尼龙66（PA66）尼龙66（PA66）熔料温度：250-290℃料筒恒温：240℃模具温度：60-100℃注射压力：100-160MPa（1000-1600bar），如果是加工薄面长流道制品（如电线扎带），则需要达到180MPa（180bar）。
保压压力：注射压力的50%；由于材料凝结相对较快，短的保压时间已足够。
降低保压压力可减少制品内应力。
背压：2-8MPa（20-80bar），需要准确调节，因为背压太高会造成塑化不均。
注射速度：建议采用相对较快的注射速度；模具有好的通气性否则制品上已出现焦化现象。
螺杆转速：螺杆转速高，线速度为1m/s；然而，最好将螺杆转速设置低一点，只要能在冷却时间结束前完成塑化过程即可；要求较低的螺杆转矩。
计量行程：0.5-3.5D 残料量：2-6mm却决于计量行程和螺杆直径。
预烘干：在80℃温度下烘干4h，除了直接从装料容器内喂料；尼龙有吸水性，应该保存在防潮容器内和封闭的料斗内；水含有超过0.25%就会造成成型改变。
回收率：可加入10%回料。
收缩率：0.7%-2.0%；或者加了30%的玻璃纤维，收缩率为0.4%-0.7%；如果提供的温度超过60℃，制品应该为逐渐冷却；逐渐冷却可降低成型后收缩。
即制品表现为更好的尺寸稳定性和小的内应力；建议采用蒸汽法；尼龙制品可以通过熔液焊剂来检查应力。
浇口系统：点式，潜伏式，片式和直浇口都可以；建议使用盲孔和浇口窝来段冷料点；可使用热流道；由于熔料可加工温度范围窄，热流道应提供闭环温度控制。
料筒设备：标准螺杆，特殊几何尺寸有较高塑化能力；止逆环，直通喷嘴；对加入了玻璃纤维的增强材料，则需要高耐磨的双金属料筒机器停工时间段：无需用其它料清洗；熔料残留在料桶内时间可达20min，此后热降解容易发生。
- 1、下载文档前请自行甄别文档内容的完整性，平台不提供额外的编辑、内容补充、找答案等附加服务。
- 2、"仅部分预览"的文档,不可在线预览部分如存在完整性等问题,可反馈申请退款(可完整预览的文档不适用该条件!)。
- 3、如文档侵犯您的权益，请联系客服反馈,我们会尽快为您处理(人工客服工作时间：9:00-18:30)。
尼龙66许用应力
尼龙66材料是一种具有广泛应用的热塑性合成树脂，具有高强度、优异的耐磨性和耐化学腐蚀性能。
在实际应用中，尼龙66材料的许用
应力是非常重要的一个参数。
本文将详细介绍尼龙66材料的许用应力
以及其影响因素。
1. 尼龙66材料的许用应力定义
尼龙66材料的许用应力是指在特定工作条件和环境中，尼龙66材
料能够承受的最大应力值。
超过这个许用应力的值，尼龙66材料会发
生变形、破裂甚至失效。
2. 尼龙66材料的许用应力计算方法
尼龙66材料的许用应力需要通过实验获得。
一般来说，可以采用
静态拉伸实验、弯曲实验、冲击实验等方法来测试尼龙66材料在不同
工况下的应力-应变性能。
根据实验数据，可以通过公式计算出尼龙66
材料的许用应力值。
3. 影响尼龙66材料许用应力的因素
尼龙66材料的许用应力受到多个因素的影响，包括温度、湿度、
加载速率、应力集中等。
a) 温度
温度是影响尼龙66材料许用应力的重要因素之一。
一般来说，尼龙66材料在高温下其强度会降低，从而许用应力也会相应减小。
b) 湿度
湿度是另一个关键因素。
尼龙66材料对水分的吸湿性较强，会导致材料的强度和刚度下降，进而影响许用应力的数值。
c) 加载速率
尼龙66材料的许用应力还与加载速率相关。
在高速加载下，材料的许用应力可能会降低，因为高速加载会导致材料不能充分强化。
d) 应力集中
尼龙66材料的许用应力还受到应力集中的影响。
材料表面或其它部分的几何形状、薄弱部位等都可能导致应力集中，从而降低许用应力。
4. 应用案例：尼龙66材料在工程实践中的许用应力
尼龙66材料广泛应用于机械零件、汽车部件、电子设备等领域。
在机械零件方面，尼龙66材料的许用应力需要根据具体的工程要求来确定，以确保零件在使用过程中不会发生失效。
例如，对于一个承受拉力的零件，根据对尼龙66材料的拉伸试验数据可以计算出在给定的工作条件下，该零件能够承受的最大拉力。
5. 尼龙66材料的许用应力管理与控制
为了确保尼龙66材料的可靠性，对许用应力进行管理与控制是非常重要的。
在实际应用中，可以采取以下措施来管理和控制尼龙66材料的许用应力：
a) 通过设计优化，减少应力集中的可能性，降低许用应力值。
b) 控制工作环境的温度和湿度，以减小温度和湿度对尼龙66材料强度的影响。
c) 控制加载速率，避免过快的加载速度对材料性能的不良影响。
d) 定期检测和监测尼龙66材料的应力状态，及时发现和解决潜在的问题。
综上所述，尼龙66材料的许用应力是确保其工程应用安全可靠的重要参数。
在实际使用中，需要考虑多个因素的影响，并采取相应的管理和控制措施，以保证尼龙66材料的性能和可靠性。