叠层片式铁氧体磁珠(通用型)
③
Nominal Impedance Example Nominal Value 31 Ω 31Ω 120 Ω 120 Ω 600 Ω 600 Ω 2500 Ω 2500 Ω
Shape and Dimensions
Recommended Pattern
Ferrite Terminal Electrode
Multilayer Chip Ferrite Beads WLCB Series
Electrical Characteristics
Part Number WL CB1608 - 10 Ω WL CB1608 - 11 Ω WL CB1608 - 30 Ω WL CB1608 - 31 Ω WL CB1608 - 60 Ω WL CB1608 - 80 Ω WL CB1608 - 120 Ω WL CB1608 - 220 Ω WL CB1608 - 300 Ω WL CB1608 - 470 Ω WL CB1608 - 600 Ω WL CB1608 - 1000 Ω WL CB1608 - 1500 Ω WL CB1608 - 1800 Ω WL CB1608 - 2000 Ω WL CB1608 - 2200 Ω WL CB1608 - 2500 Ω WL CB1608 - 2700 Ω Note: Operating temperature range－55℃～125℃(Including self - temperature rise) Rate Current：Applied the current to coils, the temperature rise shall not be more than 30℃ Measure Equipment： Z：HP4291A RDC：HP4338B or CHEN HWA 502 Impedance (Ω±25%) 10 11 30 31 60 80 120 220 300 470 600 1000 1500 1800 2000 2200 2500 2700 Test Frequency (MHz) 100 100 100 100 100 100 100 100 100 100 100 100 100 100 100 100 100 100 RDC (Ω) Max 0.30 0.30 0.30 0.30 0.30 0.30 0.30 0.30 0.30 0.45 0.45 0.60 0.90 0.90 1.00 1.00 1.00 1.00 Rated current (mA) Max 300 300 300 300 300 300 300 300 300 200 200 200 100 100 50 50 50 50
Dimensions in mm TYPE 1005 1608 2012 3216 A 0.4 0.7 ~ 0.8 1.0 ~ 1.2 2.0 B 1.2 ~ 1.4 1.8 ~ 2.0 2.6 ~ 4.0 4.2 ~ 5.2 C 0.5 0.6 ~ 0.8 1.0 ~ 1.2 1.2
Please be sure to request approval specifications that provide further details of the products. Kindly note that
B
D
D
A
C
C A B
Dimensions in mm TYPE 1005 1608 2012 3216 A 1.0 0.10 1.6 0.15 2.00.20 3.20.20 B 0.500.10 0.800.15 1.250.20 1.600.20 C 0.50.10 0.80.15 0.90.20 0.9 0.20 D 0.250.10 0.30.2 0.50.3 0.50.3
FREQUENCY (MHz)
WL CB1005 - 75 Ω
140
180 160
WL CB1005 - 100 Ω
IMPEDANCE(Ω)
IMPEDANCE(Ω)
120 100 80 60 40 20 0 1 10 100 1000
Z
IMPEDANCE(Ω)
140 120 100 80 60 40 20 0 1 10 100 1000
WL CB1005 - 1500 Ω
IMPEDANCE(Ω)
600 400 200 0 1 10 100 1000
Z
IMPEDANCE(Ω)
800
Z
1500
Z
1000
R
FREQUENCY (MHz)
X
500
R
0 1 10 100
X
R
1 10 100
X
1000 10000
1000
FREQUENCY (MHz)
Multilayer Chip Ferrite Beads WLCB Series
Electrical Characteristics
Part Number WL CB1005 - 10 Ω WL CB1005 - 30 Ω WL CB1005 - 60 Ω WL CB1005 - 75 Ω WL CB1005 - 100 Ω WL CB1005 - 120 Ω WL CB1005 - 220 Ω WL CB1005 - 300 Ω WL CB1005 - 470 Ω WL CB1005 - 600 Ω WL CB1005 - 1000 Ω WL CB1005 - 1500 Ω WL CB1005 - 1800 Ω Note: Operating temperature range－55℃～125℃(Including self - temperature rise) Rate Current：Applied the current to coils, the temperature rise shall not be more than 30℃ Measure Equipment： Z：HP4291A RDC：HP4338B or CHEN HWA 502 Impedance (Ω±25%) 10 30 60 75 100 120 220 300 470 600 1000 1500 1800 Test Frequency (MHz) 100 100 100 100 100 100 100 100 100 100 100 100 100 RDC (Ω) Max 0.25 0.25 0.35 0.35 0.40 0.40 0.70 0.80 1.00 0.70 1.00 1.50 1.50 Rated current (mA) Max 300 300 300 300 300 300 200 200 200 200 200 100 100
90
WL CB1005 - 60 Ω
IMPEDANCE(Ω)
12 10 8 6 4 2 0 1 10
Z
IMPEDANCE(Ω)
16 14
80 70 60 50 40 30 20 10 0 1 10 100 1000
Z X R
FREQUENCY (MHz)
R
100 1000
0
FREQUENCY (MHz)
Multilayer Chip Ferrite Beads WLCB Series
Test Instruments：Agilent E4991A Impedance / Material Analyzer
WL CB1005 - 220 Ω
IMPEDANCE(Ω)
400 350
IMPEDANCE(Ω)
the content of these specifications are subject to change or may be discontinued without advance notice. Please contact our sales department before ordering.
FREQUENCY (MHz)
3000
WL CB1005 - 1800 Ω
Z
IMPEDANCE(Ω)
2500 2000 1500 1000 500 0 1 10
R
100
X
1000
FREQUENCY (MHz)
Please be sure to request approval specifications that provide further details of the products. Kindly note that
300 250 200 150 100 50 0 1 10
Z
Z
IMPEDANCE(Ω)
X R
100 1000
500 450 400 350 300 250 200 150 100 50 0 1
WL CB1005 - 300 Ω
900 800 700 600 500 400 300 200 100 0 1
the content of these specifications are subject to change or may be discontinued without advance notice. Please contact our sales department before ordering.
Multilayer Chip Ferrite Beads WLCB Series
Features
Multilayer monolithic construction yields high reliability Excellent solderability and heat resistance for either
the content of these specifications are subject to change or may be discontinued without advance notice. Please contact our sales department before ordering.
叠层型片式磁珠的特性及其应用
1前言各种电子线路中，电磁干扰源产生的电磁干扰杂波，通过传导和辐射途经对线路其它部分或其它电子线路产生电磁干扰。
这一过程中导线起了重要作用，一英寸长的导线在100MHz频率下的电感量约为20nh，其感抗约为12．6Ω，这是不可忽视的。
为了消除电磁干扰，方法之一就是在有源和无源电子元器件的引线上套上一些很小的管形或环形的软磁铁氧体磁芯，利用铁氧体材料的电磁损耗机理有效地消除传导和辐射的电磁干扰噪声。
这种抗电磁干扰的方法既简便又有效，而且成本很低，所以获得了十分广泛的应用。
由于串在引线上用于抗电磁干扰的铁氧体小管或小环有些像一串珍珠，所以它们得到了一个很形象化的名称—磁珠（Bead）。
近年来表面贴装技术（SMT）迅速崛起，传统的插装电路逐步被SMT电路替代，绝大部分带引线的电子元器件均已片式化，变成了无引线或短引线的片式电子元器件。
这样一来，上述的传统磁珠（铁氧体小管或小环）已无法在SMT电路中应用。
为了解决这一困难，国外一些著名的电子元器件公司，如美国的AEM公司、Coilcraft公司、日本TDK、村田、太阳诱电、Tokin等公司，先后开发了片式磁珠（ChipBead）和片式电感器（ChipInductor），以满足SMT电路的需求。
实质上，磁珠就是一个填充磁芯的电感器，利用它的阻抗|Z|在高频下迅速增加的特性和磁性材料的电磁损耗机理来抑制和吸收高频噪声，从而达到抗电磁干扰的目的。
片式磁珠/电感器按结构可分为两大类，即叠层型片式磁珠／电感器（MultilayerChipBead/Inductor，简称MLCB/MLCI）和绕线型片式磁珠/电感器（WoundChipBead/Inductor）。
叠层型片式磁珠／电感器是近年来发展起来的一种高新技术产品，其结构如图1所示。
由图1可以看出，导体线圈完全被磁性铁氧体介质包围，形成一种独石结构。
当电流通过时，激励的磁力线几乎完全被屏蔽在其内部，而不会干扰邻近的其它电子元器件。
贴片物料规格书-风华磁珠
Part No.
CBG160808U070 CBG160808U150 CBG160808U310 CBG160808U700 CBG160808U800 CBG160808U101 CBG160808U121 CBG160808U151 CBG160808U181 CBG160808U221 CBG160808U301 CBG160808U501 CBG160808U601 CBG160808U801 CBG160808U102 CBG160808U122 CBG160808U152 CBG160808U182 CBG160808U202
广东肇庆英达电感器件有限公司
GUANGDONG ZHAOQING YINGDA INDUCTOR CO。，LTD
铁氧体叠层片式磁珠（通用型）
表面贴装元件 SMD COMPONENTS
Ferrite chip beads
1005 :-55～125℃
OPEARATING TEMP.
Impedance(Ω)
At 100MHz 26±25% 31±25% 50±25% 80±25% 120±25% 150±25% 180±25% 220±25% 300±25% 500±25% 600±25% 800±25% 1000±25% 1200±25%
DCR (Ω) Max 0.10 0.10 0.15 0.15 0.25 0.30 0.30 0.40 0.45 0.50 0.50 0.60 0.60 0.70
Part No.
CBG321609U050 CBG321609U110
Impedance(Ω) At 100MHz 0~7 9~19 26±25% 31±25% 36±25% 60±25% 100±25% 120±25% 150±25% 200±25% 300±25% 500±25% 600±25% 800±25%
40铁氧体叠层片式磁珠(低频高阻型)Ferrite chip beads
Ｚ
R X
10
100
Frequency[MHz]
1000
Impedance[O]
400 300 200 100
0 1
Ｚ
R X
10
100
Frequency[MHz]
1000
Impedance[ Ω]
1000
CBH201209W601T
Impedance[O]
800 600 400 200
0 1
Ir (mA)Max
300 200 200 200 150 100 100 100
DCR (Ω)Max
0.25 0.25 0.25 0.30 0.35 0.40 0.45 0.50 0.60
DCR (Ω)Max
0.10 0.20 0.25 0.30 0.35 0.50
Ir (mA)Max
400 300 300 300 300 200 200 150 100
Appearance:
Thermal No significant abnormality.
5
shock
Impedance change: within ±20%
Inductor change: within±10%
Test methods
Solder temperature: 230±5℃ Duration: 4±1S Preheating temperature: 120 to 150℃ Preheating time: 60S Flux: immersion into methanol solution with colophony for 3 to 5 sec. Immersion speed: 25mm/sec Solder temperature: 260±5℃ Duration: 10±0.5S Preheating temperature: 120 to 150℃ Preheating time: 60S Flux: immersion into methanol solution with colophony for 3 to 5 sec. Immersion speed: 25mm/sec Temperature: -40℃ for 30±3min +85℃ for 30±3min Transforming interval :max 20 sec Number of cycles: 32
贴片磁珠
规格如有变更，不在另行通知。 在您订购前，烦请致电咨询确认。 电话：0755—36694521 传真：0755—33180992 网址： 邮箱：beimuo@ 工厂地址：深圳市宝安区松岗镇江边第三工业区
GDPZ2012P300
规格如有变更，不在另行通知。 在您订购前，烦请致电咨询确认。 电话：0755—36694521 传真：0755—33180992 网址： 邮箱：beimuo@ 工厂地址：深圳市宝安区松岗镇江边第三工业区
Max. Rated
Current
额定电流 mA lr 4000 3000 2500 1500 1500 800 800 3000 3000 2500 2000 1500 1000 800
规格如有变更，不在另行通知。 在您订购前，烦请致电咨询确认。 电话：0755—36694521 传真：0755—33180992 网址： 邮箱：beimuo@ 工厂地址：深圳市宝安区松岗镇江边第三工业区
规格如有变更，不在另行通知。 在您订购前，烦请致电咨询确认。 电话：0755—36694521 传真：0755—33180992 网址： 邮箱：beimuo@ 工厂地址：深圳市宝安区松岗镇江边第三工业区
用途 APPLICATIONS ·电脑及周边设备，DVD、照相机、LCD TV 等音视频设备； 通讯设备，办公自动化等电子设备的电源线或大电流信号线的噪声抑制
产品型号 PRODUCT IDENTIFICATION
GDPZ
2012
P
300
①
②
③
④
①
分类 Type
-1A0 ⑤
T
F
⑥
⑦
GDPZ 叠层片式铁氧体大电流型磁珠
GDPZ 2012 TYPE
风华铁氧体叠层片式磁珠
风华铁氧体叠层片式磁珠一、引言风华铁氧体叠层片式磁珠是一种新型的磁性材料，具有高饱和磁感应强度、低磁滞损耗、高频响应等优点，被广泛应用于电子器件、电机、传感器等领域。
本文将从材料特性、制备工艺、应用领域等方面对该材料进行详细介绍。
二、材料特性1. 高饱和磁感应强度风华铁氧体叠层片式磁珠采用高纯度的Fe2O3和BaCO3为原料，通过化学共沉淀法制备得到。
由于该材料具有均匀的晶粒尺寸和优异的结晶形态，因此其饱和磁感应强度可达到5000Gs以上。
2. 低磁滞损耗风华铁氧体叠层片式磁珠具有较低的磁滞损耗，这是由于其微观结构中存在着大量的互相平行排列的晶粒。
这种排列方式可以减小晶粒之间的相互干扰，从而降低了材料的磁滞损耗。
3. 高频响应风华铁氧体叠层片式磁珠具有较好的高频响应特性，这是由于其微观结构中存在着大量的细小晶粒。
这些细小晶粒可以减小材料的磁滞损耗，并提高材料在高频下的磁性能。
三、制备工艺风华铁氧体叠层片式磁珠的制备工艺主要包括化学共沉淀法、水热法、溶胶-凝胶法等。
其中，化学共沉淀法是目前应用最广泛的一种制备方法。
1. 化学共沉淀法该方法主要包括以下步骤：将Fe2O3和BaCO3按一定比例混合，加入适量的水溶液中，进行搅拌和超声处理，使得两种物质充分混合；加入NH4HCO3作为络合剂，在温度控制下进行共沉淀反应；将共沉淀物洗涤干净后，在空气中干燥得到粉末；将粉末在氢气氛下还原，并在高温下进行烧结得到风华铁氧体叠层片式磁珠。
2. 水热法该方法主要包括以下步骤：将Fe2O3和BaCO3按一定比例混合，加入适量的水溶液中，进行搅拌和超声处理，使得两种物质充分混合；将混合物转移到高压釜中，在一定的温度和压力下进行水热反应；将反应产物洗涤干净后，在空气中干燥得到粉末；将粉末在氢气氛下还原，并在高温下进行烧结得到风华铁氧体叠层片式磁珠。
3. 溶胶-凝胶法该方法主要包括以下步骤：将Fe2O3和BaCO3按一定比例混合，加入适量的水溶液中，进行搅拌和超声处理，使得两种物质充分混合；加入适量的表面活性剂，并控制pH值，在温度控制下进行凝胶化反应；将凝胶体在空气中干燥得到粉末；将粉末在氢气氛下还原，并在高温下进行烧结得到风华铁氧体叠层片式磁珠。
磁珠的作用
磁珠的作用1、磁珠，其实就是单匝的线圈，而电感是多匝的。
有一匝以上的线圈习惯称为电感线圈，少于一匝（导线直通磁环）的线圈习惯称之为磁珠，其实磁珠就是单匝电感，因此电感量小，与其寄生电容的共振频率就高（在这个频率点上，阻抗最高），因而对高频的抑制作用就好。
2、磁珠，是能量消耗元件，可等效为一个电感和一个电阻串联，只是电阻和电感都随频率的增高而增大，低频时阻抗很小，信号可以通过，频率较高时，比如说外界的RF干扰，等效阻抗很大，射频干扰以热量的形式被消耗掉，达到EMC 的目的，常用于信号线和电源线入口，抑制高频干扰和尖峰干扰；而电感是储能元件，多用于电源的滤波。
3、磁珠主要对付环境中的电磁辐射干扰；电感用来对付传导性干扰。
4、两者在电路中的符号虽然相同，但是单位却不同，磁珠的单位是欧姆，因为磁珠的单位是按照它在某一频率产生的阻抗来标称的，阻抗的单位也是欧姆。
磁珠的DATASHEET上一般会提供频率和阻抗的特性曲线图，一般以100MHz为标准，比如1000R@100MHz，意思就是在100MHz频率的时候磁珠的阻抗相当于600欧姆；电感的单位是亨利(H)。
不过两者贴片的封装差不多，顺便贴出贴片的公制封装与英制封装名称对比：下面主要说说磁珠：现在用的最多的是铁氧体磁珠(Ferrite Bead) 。
1、磁珠的分类：通用型、大电流型、低频高阻型及尖峰型。
并分别用代号来表示：CBG的含义叠层片式通型磁珠，CBW为大电流型，CBY为尖峰型、CBH为低频高阻型。
2、磁珠的参数：以我们选用的村田的BLM15AG102SN1为例：阻抗1000ohm@100MHz，100MHz时的等效阻抗位1000欧姆；直流电阻DC Resistance (1.0 ohm)，直流阻抗1.0欧姆，表示对直流信号的衰减，越低越好；还可以发现一个现象：阻抗越大，其直流阻抗也越大，例如，BLM15AG100SN1100MHz阻抗仅为10ohm，直流阻抗为0.05ohm。
PBY100505T-121Y-N叠层片式铁氧体磁珠规格书
Dimensions in mm TYPE 060303 100505 160805 160808 201209 321611 ＊ A 0.2 ~ 0.3 0.4 0.7 ~ 0.8 0.7 ~ 0.8 1.0 ~ 1.2 2.0 B 0.75 ~ 1.05 1.2 ~ 1.4 1.8 ~ 2.0 1.8 ~ 2.0 2.6 ~ 4.0 4.2 ~ 5.2 C 0.3 0.5 0.6 ~ 0.8 0.6 ~ 0.8 1.0 ~ 1.2 1.2
IMPEDANCE(Ω)
120 100 80 60 40 20 0
60 40
Z X
Z X R
1 10 100 10
20
X R
FREQUENCY (MHz) RDC<0.23 Ω Rated Current :450 mA
R
0 1 10 100 1000
FREQUENCY (MHz) RDC<0.12 Ω Rated Current :500 mA
Test Instruments：Agilent E4991A Impedance / Material Analyzer
PBY060303T-100Y-N
IMPEDANCE(Ω)
18 16
40 35
PBY060303T-220Y-N
IMPECANCE(Ω)
100 80 60 40 20 0
PBY060303T-330Y-N
FREQUENCY (MHz) RDC<0.05Ω Rated Current :1700 mA
FREQUENCY (MHz) RDC<0.075Ω Rated Current :1500 mA
PBY100505T-800Y-N
PBY160808T-100Y-N叠层片式铁氧体磁珠规格书
Z
X R
100 1000
FREQUENCY (MHz) RDC<0.18Ω Rated Current :1100mA
Electrical Characteristics
Part Number PBY160808T-100Y-N PBY160808T-300Y-N PBY160808T-400Y-N PBY160808T-600Y-N PBY160808T-121Y-N PBY160808T-151Y-N PBY160808T-181Y-N PBY160808T-221Y-N PBY160808T-301Y-N PBY160808T-471Y-N PBY160808T-601Y-N PBY160808T-102Y-N PBY160808T-122Y-N PBY160808T-152Y-N Impedance (Ω±25%) 10 30 40 60 120 150 180 220 300 470 600 1000 1200 1500 Test Frequency (MHz) 100 100 100 100 100 100 100 100 100 100 100 100 100 100 RDC (Ω) Max 0.020 0.030 0.035 0.040 0.080 0.085 0.090 0.100 0.120 0.150 0.200 0.250 0.250 0.400 Rated current (mA) Max 4000 3000 3000 3000 2500 2000 2000 2000 1500 1200 1000 800 800 500
：SBY / SBJ / NB / PB ：SBK / GB / PB / UPB
：SBY / SBJ / NB / PB / UPB / HF ：SBY / SBK / PBY / UPB
磁珠选型与应用知识
磁珠选型与应用知识磁珠的全称为铁氧体磁珠滤波器(另有一种是非晶合金磁性材料制作的磁珠)，是一种抗干扰元件，滤除高频噪声效果显著。
磁珠的主要原料为铁氧体。
铁氧体是一种立方晶格结构的亚铁磁性材料。
铁氧体材料为铁镁合金或铁镍合金，它的制造工艺和机械性能与陶瓷相似，颜色为灰黑色。
磁珠有很高的电阻率和磁导率，他等效于电阻和电感串联，但电阻值和电感值都随频率变化。
他比普通的电感有更好的高频滤波特性，在高频时呈现阻性，所以能在相当宽的频率范围内保持较高的阻抗，从而提高调频滤波效果。
磁珠的电路符号就是电感，但是型号上可以看出使用的是磁珠。
在电路功能上，磁珠和电感是原理相同的，只是频率特性不同而已。
一、磁珠的型号命名方法（风化高科系列磁珠为例）磁珠的型号一般由下列五部分组成:第一部分:类别，多用字母表示.第二部分:尺寸，用数字表示（英制）第三部分:材料，用字母表示，其中X代表小型。
第四部分:阻抗，100MHz时阻抗第五部分:包装方式，用字母表示如某型号磁珠命名如下铁氧叠层片式磁珠（普通型）Ferrite chip beads尺寸：1005 （0402）1608（0603）2012（0805）产品规格命名方法：CBG 100505/、160808/ 201209、V 121 T叠层片式规格尺寸材料阻抗包装方式通用型磁珠应指出的是，目前磁珠型号命名方法各生产厂有所不同，尚无统一的标准。
二、磁珠的结构特点铁氧体磁珠 (Ferrite Bead) 是目前应用发展很快的一种抗干扰组件，廉价、易用，滤除高频噪声效果显着。
在电路中只要导线穿过它即可（我用的都是象普通电阻模样的，导线已穿过并胶合，也有表面贴装的形式，但很少见到卖的）。
当导线中电流穿过时，铁氧体对低频电流几乎没有什么阻抗，而对较高频率的电流会产生较大衰减作用。
高频电流在其中以热量形式散发，其等效电路为一个电感和一个电阻串联，两个组件的值都与磁珠的长度成比例。
磁珠种类很多，制造商应提供技术指标说明，特别是磁珠的阻抗与频率关系的曲线。
开关电源中磁珠的特性与选用原则
开关电源中磁珠的特性与选用原则1、磁珠的特性开关电源尤其是大功率开关电源，它们的工作频率一般为100kHz，有的高达1MHz。
在高频的作用下，电源的输出整流管，在关断期间反向恢复过程中，会产生噪声和反向峰值电流，非常容易击穿整流二极管或MOS管，还容易在二极管或MOS管导通期间向外辐射高频率的干扰信号。
人们虽然在整流二极管的两端并联阻容元件组成高频旁路电路，但作用效果不太理想。
相反，由于增加了电阻、电容，在高频率的作用下造成损耗。
近年来，研发人员找到在二次侧滤波器输出线上套上一只磁珠，有力地抑制了噪声和干扰信号，还具有静电脉冲吸收能力。
磁珠的主要原料为铁氧体，是一种晶体结构亚铁磁性材料，它在低频时呈现电感特性，损耗很小；在高频时呈现电抗特性抵抗高频辐射。
它的性能参数与铁氧体磁心一样，为磁导率和磁通密度。
当导体穿过铁氧体磁心时，所形成的电抗是随着频率升高而增加，不同的频率其受理作用不一样。
磁珠在高频下的磁导率较低，电感量也小，干扰电磁波吸收很大；在低频时作用相反。
总而言之，磁珠器件具有低损耗、高品质因数的特性，可防止电磁辐射。
2、磁珠的主要参数（1）标准值磁珠的单位是按照在某一频率下所产生的阻抗来标定的，它的单位是Ω，一般以100MHz为标准。
如2012B601是指100MHz磁珠的阻抗为600Ω。
（2）额定电流是保证电路正常工作允许通过的电流。
（3）感抗磁珠在100MHz的高频下，在一闭环电路里，磁珠的两端所产生的电感量。
电感量的大小表示储能的能力大小。
（4）Q值品质因数。
（5）自谐振频率由于电感有分布电容的作用，将形成LC振荡电路而起振，称之为自谐振频率。
（6）超载电流表示电感器正常工作时的最大电流的2.2倍。
（7）封装形式及尺寸在PCB上多使用表贴封装元器件，这种形式具有良好的闭合磁路和电磁特性。
（8）磁通量磁珠在低频下承受电流越大，感抗随交流变化而呈容抗，磁珠发热而造电路损耗。
初始磁通量与品质因数Q得不到平衡。