不同夹芯复合材料夹层结构的剪切破坏行为
不同夹芯复合材料夹层结构的剪切破坏行为
邹建胜;曾建江;童明波;蔡婧
【期刊名称】《机械工程材料》
【年(卷),期】2012(036)009
【摘要】对蜂窝和泡沫夹芯的复合材料夹层结构通过夹具用拉伸试验模拟剪切破坏行为，分析了试验载荷一应变曲线及失效模式，得出应变场分布情况及失效原因，并分别对不同夹层结构的剪切行为进行了有限元模拟。结果表明：夹层结构的失效模式均为沿加载方向的屈曲破坏，并且在中间区域与边界区域之间的区属于纯剪应力区；夹芯材料的横向剪切模量直接影响了复合材料夹层结构的屈曲破坏载荷和失效模式；有限元分析的屈曲模态与试验失效模式较为吻合。%Tensile test for honeycomb sandwich plates and foam sandwich plates was carried out by the tension of fixture to simulate shear damage behaviors. The distribution of strain field and the reason for failure were revealed by the analysis of the load-strain curves and failure mode. In addition, the shear behaviors of different composite sandwich plates were simulated by finite element software. The results show that the both failure modes were all buckling failure along the loading direction, and the region between the middle part and boundary part was a pure shear region. The horizontal shear modulus of different cores had a great influence on the buckling load and failure mode. And the finited element simulated buckling mode of sandwich plates fitted well with that from the experiment.
玻璃钢复合材料船舶夹层结构中的泡沫芯材
玻璃钢复合材料船舶夹层结构中的泡沫芯材 结构泡沫芯材的历史回顾 玻璃钢/复合材料（FRP/CM）中常用的泡沫芯材有聚氯乙烯（PVC）、聚苯乙烯（PS）、聚氨酯（PUR）、丙烯腈-苯乙烯（SAN）、聚醚酰亚胺（PEI）及聚甲基丙烯酰亚胺（PMI）等泡沫，其中PS和PUR泡沫通常仅作为浮力材料，而不是结构用途。目前PVC泡沫已几乎完全代替PUR泡沫而作为结构芯材，只是在一些现场发泡的结构中除外。 严格意义上讲，第一种用在承载构件夹层结构中的结构泡沫芯材是使用异氰酸酯改性的PVC泡沫，或称交联PVC。第一个采用PVC泡沫夹芯的夹层结构是保温隔热车厢。交联PVC的生产工艺是由德国人林德曼在上世纪30年代后期发明的。二次大战以后法国将该工艺列入战争赔偿中，由克勒贝尔蕾洛雷特塑料公司（Kleber Renolit）开始生产Klegecell?交联PVC泡沫，主要是一些用在保温隔热车厢中的低密度产品。 上世纪50－60年代，克勒贝尔蕾洛雷特塑料公司给几家欧洲公司发放了PVC泡沫的生产许可证。另外两家美国公司，B.F歌德雷奇（B.F Goodrich）和佳士迈威（Johns-Manville）也买到了许可证开始生产，但是几年以后就停产。当所有的生产许可证都过期以后，交联PVC 的生产工艺过程转为公开。进入70年代以后，多数原来的欧洲许可生产厂家也已停产。目前两个主要的生产厂家是戴博（Diab）公司的Divinycell?和Klegecell?系列PVC泡沫及爱瑞 柯斯（Airex）公司的Herex?系列PVC泡沫。 20世纪40年代后期，林德曼使用高压气体作为发泡剂，制造出未经过改性的PVC泡沫， 也叫线性PVC泡沫。 英国于1943年首先制成聚苯乙烯泡沫塑料，1944年美国道化学有限公司用挤出法大批量 的生产聚苯乙烯泡沫塑料。 第二次世界大战期间，德国拜尔的试验人员对二异氰酸酯及羟基化合物的反应进行研究，制得了PUR硬质泡沫塑料、涂料和粘合剂。1952年，拜尔公司报道了软质聚氨酯泡沫 塑料的研究成果。 1993年，加拿大的ATC公司开始生产SAN泡沫。其制造工艺和线性PVC相似。 PMI泡沫是由德国罗姆（Rohm）公司于1966年首先用丙烯腈、甲基丙烯腈、丙烯酰胺和甲基丙烯酸酯热塑性树脂在180oC下发泡并交联制作聚甲基丙烯酰亚胺泡沫的技术，接着日本的积水化学公司于1967年使用辐射交联方法制作聚甲基丙烯酰亚胺泡沫。 夹层结构的工作原理及优点
(完整word版)飞机夹层结构复合材料零部件的损伤形式及修理方法
常见飞机蜂窝板损伤形式及修理方法 航空器复合材料中的蜂窝板是由薄而强的两层面板中间胶接蜂窝材料而成的一种新型复合材料，也称蜂窝层合结构(见图1)。其面板选材有金属板、玻璃纤维、石英纤维、碳纤维等；夹心材料主要有芳纶、玻璃纤维、铝合金及发泡型结构。蜂窝可制成不同的形状。飞机上的蜂窝结构是由耐腐蚀夹心、面板、衬垫、隔板（假梁）、边肋等零件胶合而成。面板与夹芯之间用胶膜胶接，蜂窝夹芯用芯子胶和耐腐蚀胶根据实际需要形状施加真空压力后加温胶接成型。 图1 蜂窝夹心板结构 一、航空复合材料蜂窝结构损伤种类 根据航空复合材料蜂窝结构部件在使用过程中可能出现损伤的情况，我们可以大致将胶接蜂窝结构部件的损伤分以下5类： 1、表面损伤 图2 典型表面凹坑 此类损伤一般通过目视检查发现，包括表面擦伤、划伤、局部轻微腐蚀、表面蒙皮裂纹、表面小凹坑和局部轻微压陷等。这类损伤一般对结构强度不产生明显的削弱。 2、脱胶及分层损伤
该损伤是指纤维层与层之间或面板与夹芯之间的树脂失效缺陷，主要通过敲击检查、超声波检测等手段发现。此类损伤一般不引起结构外观变化，大多是在生产过程中造成的初始缺陷，并在反复使用过程中缺陷不断扩展而导致的。脱胶或分层面积过大会引起整体复合材料强度的削弱，应及时予以修补。 3、单侧面板损伤 这类损伤包括单侧面板局部压陷、破裂或穿孔，一般通过目视检查即可发现。该类型损伤能使一侧面板和蜂窝夹芯都受到损伤（表面塌陷），对气动性能和结构强度影响较大。一旦发现该类损伤必须经过修理和检验确认后方能能重新使用。 4、穿透损伤 该类型损伤是指蜂窝部件出现穿透性损伤、严重压陷和较大范围的残缺损伤等。此类损伤对结构性能和强度有严重的影响，根据受损情况立即予以修理或按需更换新件。 5、内部积水 该损伤原因主要由于蜂窝结构边缘或蜂窝材料对接边缘密封不严或密封失效，在长期使用过程中由于雨水渗透、油液浸泡以及水汽冷凝而造成蜂窝夹芯出现积水。虽然一般情况蜂窝内部积水不会造成严重影响；但在冬季日夜气温变化较大的情况下，由于积液结冰膨胀将会会造成复合材料部件内部树脂基体脱胶；同时在积液的长期浸泡下也会使复合材料的树脂基体的胶接强度大幅降低而降低部件的整体性能；特别是各类复合材料制备的舵面、襟翼、翼身整流罩及发动机部件等，均应及时检查其内部蜂窝结构的积水情况并作出相应修理措施。目前该类损伤主要通过红外热成像、X-射线检测仪等手段进行检测。 二、蜂窝结构的检查方式 1、目视检查 目视检查法是使用最广泛、最直接的无损检测方法。主要借助放大镜和内窥镜观测结构表面和内部可达区域的表面，观察明显的结构变形、变色、断裂、螺钉松动等结构异常。它可以检查表面划伤、裂纹、起泡、起皱、凹痕等缺陷；尤其对透光的玻璃钢产品，可用透射光检查出内部的某些缺陷和定位，如夹杂、气泡、搭接的部位和宽度、蜂窝芯的位置和状态、镶嵌件的位置等。 2、手锤敲击法 用于单层蒙皮蜂窝结构。用手锤敲击蜂窝结构的蒙皮，根据不同的声响来判断蜂窝结构是否脱胶。敲击时，注意锤头与蒙皮垂直，力度适当，以能判断故障不损坏蒙皮表面为宜。为使判断准确，可先在试件上试验。敲击回声清脆是良好，沉闷是脱粘。 3、外场在位检测的便携式相控阵超声波C扫描检测系统
ANSYS结构分析指 复合材料
ANSYS结构分析指南第五章复合材料 5.1 复合材料的相关概念 复合材料作为结构应用已有相当长的历史。在现代，复合材料构件已被大量应用于飞行器结构、汽车、体育器材及许多消费产品中。 复合材料由一种以上具有不同结构性质的材料构成，它的主要优点是具有很高的比刚度(刚度与重量之比)。在工程应用中，典型复合材料有纤维和叠层型材料，如玻璃纤维、玻璃环氧树脂、石墨环氧树脂、硼环氧树脂等。 ANSYS程序中提供一种特殊单元--层单元来模拟复合材料。利用这些单元就可以作任意的结构分析了(包括非线性如大挠度和应力刚化等问题)。对于热、磁、电场分析，目前尚未提供层单元。 5.2 建立复合材料模型 与铁或钢等各向同性材料相比，建立复合材料的模型要复杂一些。由于各层材料性能为任意正交各向异性，材料性能与材料主轴取向有关，在定义各层材料的材料性能和方向时要特别注意。本节主要探讨如下问题： 选择合适的单元类型； 定义材料层； 确定失效准则； 应遵循的建模和后处理规则。 5.2.1 选择合适的单元类型 用于建立复合材料模型的单元类型有SHELL99、SHELL91、SHELL181、SOLID46和SOLID191 五种单元。但 ANSYS/Professional 只能使用 SHELL99 和 SHELL46 单元。具体应选择哪一类单元要根据具体应用和所需计算结果类型等来确定。所有的层单元允许失效准则计算。 1、SHELL99--线性层状结构壳单元 SHELL99 是一种八节点三维壳单元，每个节点有六个自由度。该单元主要适用于薄到中等厚度的板和壳结构，一般要求宽厚比应大于10。对于宽厚比小于10的结构，则应考虑选用 SOLID46 来建立模型。SHELL99 允许有多达 250 层的等厚材料层，或者 125 层厚度在单元面内呈现双线性变化的不等材料层。如果材料层大于 250，用户可通过输入自己的材料矩阵形式来建立模型。还可以通过一个选项将单元节点偏置到结构的表层或底层。 2、SHELL91--非线性层状结构壳单元 SHELL91 与 SHELL99 有些类似，只是它允许复合材料最多只有 100 层，而且用户不能输入自己的材料性能矩阵。但是，SHELL91 支持塑性、大应变行为
夹芯 复合材料夹心材料
【夹芯】夹芯材料简介 一、原理 自二十世纪四十年代低密度的夹芯材料就已用于复合材料，它可提高弯曲强度、降低重量。具有相同负荷能力的夹层结构要比实体层状结构轻好几倍。夹芯材料能够降低单位体积的成本、削弱噪音与震动、增加耐热、抗疲劳和防火性能等。夹芯材料的作用机理是将剪切力从表皮层传向内层，使两个表皮层在静态和动态载荷下都能保持稳定，并且吸收冲击能来提供抗破坏性能。 二、分类 用于复合材料夹层结构的夹芯材料主要有：硬质泡沫、蜂窝和轻木三类。 ①硬质泡沫主要有聚氯乙烯（PVC）、聚氨酯（PU）、聚醚酰亚胺（PEI）和丙烯腈-苯乙烯（SAN或AS）、聚甲基丙烯酰亚胺（PMI）、发泡聚酯（PET）等。 ②蜂窝夹芯材料有玻璃布蜂窝、NOMEX蜂窝、棉布蜂窝、铝蜂窝等。蜂窝夹层结构的强度高，刚性好，但蜂窝为开孔结构，与上下面板的粘接面积小，粘接效果一般没有泡沫好。 ③轻木夹芯材料是一种天然产品，市场常见的轻木夹芯主要产自南美洲的种植园，由于气候原因，轻木在当地生长速度特别快，所以比普通木材轻很多，且其纤维具有良好的强度和韧性，特别适合用于复合材料夹层结构。 三、应用领域 夹芯材料的应用领域广阔，涉及能源、航空航天、船舶、交通运输、建筑等领域。 航空航天 飞机的主要部件，如机身，机翼和尾翼可采用PVC泡沫夹芯材料复合结构，同时使用丁二烯。在生产中不必进行高压高温处理。飞机的重量得以减轻。直升飞机最新一代复合螺旋桨叶采用密度较低、可耐大多数溶剂且可经受高压蒸煮温度和压力的PMI泡沫夹芯材料。它采用传统预浸工艺制造。这种新型复合螺旋桨叶的寿命可达10000h/L，是先前金属桨叶
寿命的十倍。今天超轻型竞赛飞机、飞机模型和现代"超级风车"的桨叶都使用了轻质木质夹芯材料。 船舶 常规的交联PVC泡沫己在船舶中广泛应用。瑞士海军的护卫舰使用了28、13.5、0.09m片状构造的丁二烯蜂窝夹芯材料。聚氨酯（PU）发泡夹芯材料也常用于船舶的建造。80kg/m3高密度泡沫可应用于承载部件如船舷等；80～120kg/m3的泡沫专门用作甲板和上部构造的芯材。硬质PU泡沫广泛用于水槽、绝缘板、结构性填料和充空填料。大型冷藏拖网鱼船很多是整体成型的夹芯构，用玻璃布制作内外蒙皮，夹芯材料的厚度为100mm。该类船具有轻质、高强、耐海水腐蚀、抗微生物附着以及吸收撞击能。很多游艇的船底、表面使用了标准的轻质木，以保证最大的剪切和挤压强度；船前部和甲板使用了密度较低的轻质木；隔壁面板室内地板和家具也使用了轻质木夹芯材料。 在多杂物（浮木等）漂浮的巴拿马运河中营运的快速渡轮，其抗破坏能力应是首先考虑的，其次是总重量轻以保证渡轮的速度。由于这些原因，一种线型PVC泡沫芯材被选作船壳底材，另一类型的PVC泡沫芯材作船壳侧面材料和舷侧突出部。部件使用玻纤增强表皮层和真空袋膜工艺；甲板和船舱侧面使用横纹轻质木夹芯材料，其表面用交联环氧树脂/玻纤板材做舱房表皮层，以保证渡轮达到ABS标准。 交通运输 交联的PVC夹芯材料在铁路运输中得到广泛应用，并用于公共汽车和有轨电车及摩托车等。一级方程式赛车模仿自然蜂窝结构，使用空心六边形管相互作用增强原理制作芯材。赛车具有高的抗冲击强度和能量吸收能力。比赛用自行车也采用这种蜂窝结构芯材。法国制造的铁路冷藏车采用PVC泡沫夹芯材料提高隔热效果。其它夹芯材料用于运输车辆主要是利用它们的绝缘性，如聚异氰酸酯绝缘泡沫塑料等。 建筑 夹芯材料在建筑上的应用十分广泛。在内外墙上使用纤维板、胶合板等各种夹芯材料，使墙壁具有隔音、隔热、轻质、高强等优点。由于顶棚强度要求不太高，只要求重量轻、刚性好，有一定防火、保温性能，其次是美观和价格便宜，安装方便，因此通常采用各种纤维芯材和PE钙塑泡沫芯材等。其它夹芯材料用在建筑上主要是利用它们的绝缘性。
复合材料结构
复合材料结构设计的特点 (1) 复合材料既是一种材料又是一种结构 (2) 复合材料具有可设计性 (3) 复合材料结构设计包含材料设计 复合材料区别于传统材料的根本特点之一可设计性好（设计人员可根据所需制品对力学及其它性能的要求，对结构设计的同时对材料本身进行设计） 具体体现在两个方面1力学设计——给制品一定的强度和刚度、2功能设计——给制品除力学性能外的其他性能 复合材料力学性能的特点 (1) 各向异性性能材料弹性主方向：模量较大的一个主方向称为纵向，用字母L表示，与其垂直的另一主方向称为横向，用字母T表示。通常的各向同性材料中，表达材料弹 )和ν(泊松比)或剪切弹性模量G。 对于复合材料中的每个单层，纵向弹性模量E L、横向弹性模量E T、纵向泊松比νL (或横向泊松比νT)、面内剪切弹性模量G LT。 耦合现象：拉剪耦合与剪拉耦合、弯扭耦合与扭弯耦合 (2) 非均质性 耦合变形：层合结构复合材料在一种外力作用下，除了引起本身的基本变形外，还可能引起其他基本变形。 (3)层间强度低 在结构设计时，应尽量减小层间应力，或采取某些构造措施，以避免层间分层破坏。 研究复合材料的刚度和强度时，基本假设： (1) 假设层合板是连续的。由于连续性假设，使数学分析中的一些连续性概念、极限概念以及微积分等数学工具都能应用于力学分析中。 (2）假设单向层合板是均匀的，多向层合板是分段均匀的。 (3) 假设限于单向层合板是正交各向异性的：即认为单向层合板具有两个相互垂直的弹性对称面。 (4) 假设限于层合板是线弹性的：即认为层合板在外力作用下产生的变形与外力成正比关系，且当外力移去后，层合板能够完全恢复其原来形状。 (5) 假设层合板的变形是很小的。 上述五个基本假设，只有多向层合板的分段均匀性假设和单向层合板的正交各向异性假设，与材料力学中的均匀性假设和各向同性假设有区别。 平面应力状态与平面应变状态 平面应力状态：单元体有一对平面上的应力等于0。（σz＝0，τzx＝0，τzy ＝0） 平面应变状态（平面位移）：εz＝0（即ω＝0），τzx＝0(γ31＝0)，τzy ＝0(γ32＝0 )， σz一般不等于0。 复合材料连接方式 复合材料连接方式主要分为两大类：胶接连接与机械连接。胶接连接：受力不大的薄壁结构，尤其是复合材料结构；机械连接：连接构件较厚、受力大的结构。
复合材料夹层结构基本原理
复合材料夹层结构基本原理 前言我国复合材料工业的发展起始于20世纪50年代，经过50余年的发展，由于“轻质高强”的优异性能，其应用领域已由最初的航空航天和国防业渗透到了当今国民经济的各个领域，如化工管罐，运动器材，汽车部件，建筑，船艇，轨道交通，风力发电叶片等等。随着复合材料应用领域的扩展，产品的尺寸不断变大，夹层结构的应用也越来越广泛。 1 复合材料夹层结构基本原理 复合材料夹层结构由强度很高的面层和强度较低的轻质夹芯材料组成，在弯曲荷载下，上下面层承担主要的拉应力和压应力，芯材主要承担剪切应力。芯材的力学作用机理是连接面层使之成为整体构件，让薄而强的面层在承担较高拉压应力的同时不发生屈曲，并将剪切力从面层传向内层。以面层厚度相等的单夹层结构在弯曲载荷作用下的响应为例，来说明夹层结构的基本原理。 1.1 面层和芯材的拉、压应力分布 在弯曲载荷作用下，假设面层和芯材的界面没有损坏，即在界面处的变形是连续的，且材料处于线弹性范围内，则夹层结构产生的拉压应变分布如图1所示。 由于面层和芯材的弹性模量不同，所以其应力分布会发生突变，面层的拉、压应力远大于芯材的拉、压应力，如图2所示。 图2 截面拉、压应力分布 根据材料力学梁的弯曲理论，根据夹层结构的几何数据和各部分材料的弹性模量可以算出结构的等效刚度（EI）eq，则面层和芯材部位产生的拉、压应力如下： （1）
（2） 式中，M：夹层结构承受的弯矩 y：离中性轴的距离 Ef：面层的弹性模量 Ec：夹芯材料的弹性模量 1.2 面层和芯材的剪应力分布 根据材料力学梁的弯曲理论，夹层结构中的剪应力分布如图3所示。 图3 剪应力分布图4简化后的剪应力分布 在工程实践中，为便于计算，可以对其进行线性简化，如图4所示。那么剪应力可按下式进行简化计算： （3） （4） 式中，Q：截面承受的剪力 b：夹层结构梁的宽度 c：芯材的高度 1.3 面层和芯材的匹配 从上面的分析可以看到，面层承担了大部分的拉、压力，芯材承担了大部分的剪力。而面层的强度和刚度都远大于夹芯材料，对于夹层结构设计人员来说，如何能够使这两种力学性能大相径庭的材料完美的结合在一起，充分发挥各自的优点，即满足使用要求，又不浪费材料？ 在夹层结构受弯情况下，夹层结构主要是靠芯材的剪切来传递直接施加在面层上的力，在复合材料夹层结构中，FRP面层的模量和强度都很高，只有高剪切强度和大剪切断裂延伸率的芯材才适用，如常用的PVC、PET、SAN、PEI、PMI等泡沫芯材。要根据夹层结构在使用中可能的受力状况，选用适当种类和密度的芯材，合理设计面层和芯材的厚度，按照前面介绍的应力计算方法，或用相关的有限元分析软件，进行反复的计算验证，最终达到较优的设计方案。 若选用剪切强度低，或是剪切断裂延伸率小的芯材，则芯材破坏时，面层可能只发挥了1%不到的强度，则会造成材料的浪费。
复合材料力学
复合材料力学 论文题目：用氧化铝填充导热和电绝缘环氧 复合材料的无缺陷石墨烯纳米片 院系班级：工程力学1302 姓名：黄义良 学号： 201314060215
用氧化铝填充导热和电绝缘环氧复合材料的无缺陷石墨烯纳米片 孙仁辉1 ，姚华1 ，张浩斌1 ，李越1 ，米耀荣2 ，于中振3 （1.北京化工大学材料科学与工程学院，有机无机复合材料国家重点实验室北京 100029;2.高级材料技术中心（CAMT ），航空航天，机械和机电工程学院J07，悉尼大学;3.北京化工大学软件物理科学与工程北京先进创新中心，北京100029） 摘要：虽然石墨烯由于其高纵横比和优异的导热性可以显着地改善聚合物的导热性，但是其导致电绝缘的严重降低，并且因此限制了其聚合物复合材料在电子和系统的热管理中的广泛应用。为了解决这个问题，电绝缘Al 2O 3用于装饰高质量（无缺陷）石墨烯纳米片（GNP ）。借助超临界二氧化碳（scCO 2），通过Al(NO 3)3 前体的快速成核和水解，然后在600℃下煅烧，在惰性GNP 表面上形成许多Al 2O 3纳米颗粒。或者，通过用缓冲溶液控制Al 2(SO 4)3 前体的成核和水解，Al 2(SO 4)3 缓慢成核并在GNP 上水解以形成氢氧化铝，然后将其转化为Al 2O 3纳米层，而不通过煅烧进行相分离。与在scCO2的帮助下的Al 2O 3@GNP 混合物相比，在缓冲溶液的帮助下制备的混合物高度有效地赋予具有优良导热性的环氧树脂，同时保持其电绝缘。具有12％质量百分比的Al 2O 3@GNP 混合物的环氧复合材料表现出1.49W /（m ·K ）的高热导率，其比纯环氧树脂高677％，表明其作为导热和电绝缘填料用于基于聚合物的功能复合材料。 关键词：聚合物复合基材料（PMCs ） 功能复合材料 电气特性 热性能 Decoration of defect-free graphene nanoplatelets with alumina for thermally conductive and electrically insulating epoxy composites Renhui Sun 1，Hua Yao 1， Hao-Bin Zhang 1，Yue Li 1，Yiu-Wing Mai 2，Zhong-Zhen Yu 3 (1.State Key Laboratory of Organic-Inorganic Composites, College of Materials Science and Engineering, Beijing University of Chemical Technology, Beijing 100029, China; 2.Centre for Advanced Materials Technology (CAMT), School of Aerospace, Mechanical and Mechatronic Engineering J07, The University of Sydney, Sydney, NSW 2006, Australia; 3.Beijing Advanced Innovation Center for Soft Matter Science and Engineering, Beijing University of Chemical Technology, Beijing 100029, China) Abstract:Although graphene can significantly improve the thermal conductivity of polymers due to its high aspect ratio and excellent thermal conductance, it causes serious reduction in electrical insulation and thus limits the wide applications of its polymer composites in the thermal management of electronics and systems. To solve this problem, electrically insulating Al 2O 3is used to decorate high quality (defect-free) graphene nanoplatelets (GNPs). Aided by supercritical carbon dioxide (scCO 2), numerous Al 2O 3 nanoparticles are formed
复合材料泡沫夹层结构的材料和应用
复合材料夹层结构芯材 夹层结构的最初应用从上世纪初的航空航天业开始，逐步发展到今天的船舶、交通运输、运动器材、风力发电、医疗器材等领域。德固赛（中国）投资有限公司上海分公司的胡培先生全面综述了各种芯材的特性、应用、市场分布及前景。
常用芯材及其应用 玻璃钢/复合材料中常用的芯材有泡沫、巴萨木和蜂窝等多孔固体材料。 巴萨木目前主要的用途集中在风电、船舶、铁路车辆等行业。相对而言，因为其密度选择范围小，面层破坏以后，吸水腐烂的缺点，已经逐步被PVC泡沫取代。但是因为其价格优势，目前还有一定的市场。 蜂窝主要有NOMEX纸蜂窝和铝蜂窝，蜂窝材料具有各向异性的特点。另外，因为蜂窝存在开孔结构，不适用一些湿法工艺或树脂注射工艺，例如船舶和风电等领域。铝蜂窝因为和碳纤维面板之间存在电腐蚀的问题，一般不能和碳纤维一同使用。另外，蜂窝结构在使用过程中，会因为面层破坏，发生渗水问题。 玻璃钢/复合材料中常用的泡沫芯材有聚氯乙烯（PVC）、聚苯乙烯（PS）、聚氨酯（PUR）、丙烯腈-苯乙烯（SAN）、聚醚酰亚胺（PEI）及聚甲基丙烯酰亚胺（PMI）等。 硬质聚氨酯PUR泡沫与其他泡沫相比，其力学性能一般，树脂/芯材界面易产生老化，从而导致面板剥离。作为结构材料使用时，常用作层合板的纵、横桁条或加强筋之芯材。有时PUR泡沫也能用于受载较小的夹层板中，起到隔热或隔音的作用。该类泡沫的使用温度为150℃左右，吸声性能良好，成型非常简单，但是机械加工过程中易碎或掉渣。PUR泡沫价格相对便宜，发泡工艺也比较简单，采用液体发泡。目前主要在运动器材，例如网球拍、冰球棒中用做工艺芯材，并起到一定的阻尼作用。另外在冲浪板中也普遍使用PUR泡沫或EPS泡沫作为芯材。
不同夹芯复合材料夹层结构的剪切破坏行为
不同夹芯复合材料夹层结构的剪切破坏行为 邹建胜;曾建江;童明波;蔡婧 【期刊名称】《机械工程材料》 【年(卷),期】2012(036)009 【摘要】对蜂窝和泡沫夹芯的复合材料夹层结构通过夹具用拉伸试验模拟剪切破坏行为，分析了试验载荷一应变曲线及失效模式，得出应变场分布情况及失效原因，并分别对不同夹层结构的剪切行为进行了有限元模拟。结果表明：夹层结构的失效模式均为沿加载方向的屈曲破坏，并且在中间区域与边界区域之间的区属于纯剪应力区；夹芯材料的横向剪切模量直接影响了复合材料夹层结构的屈曲破坏载荷和失效模式；有限元分析的屈曲模态与试验失效模式较为吻合。%Tensile test for honeycomb sandwich plates and foam sandwich plates was carried out by the tension of fixture to simulate shear damage behaviors. The distribution of strain field and the reason for failure were revealed by the analysis of the load-strain curves and failure mode. In addition, the shear behaviors of different composite sandwich plates were simulated by finite element software. The results show that the both failure modes were all buckling failure along the loading direction, and the region between the middle part and boundary part was a pure shear region. The horizontal shear modulus of different cores had a great influence on the buckling load and failure mode. And the finited element simulated buckling mode of sandwich plates fitted well with that from the experiment.
复合材料结构与力学设计复结习题(本科生)
《复合材料结构设计》习题 §1 绪论 1.1 什么是复合材料？ 1.2 复合材料如何分类？ 1.3 复合材料中主要的增强材料有哪些？ 1.4 复合材料中主要的基体材料有哪些？ 1.5 纤维复合材料力学性能的特点哪些？ 1.6 复合材料结构设计有何特点？ 1.7 根据复合材料力学性能的特点在复合材料结构设计时应特别注意到哪些问题? §2 纤维、树脂的基本力学性能 2.1 玻璃纤维的主要种类及其它们的主要成分的特点是什么？ 2.2 玻璃纤维的主要制品有哪些？玻璃纤维纱和织物规格的表示单位是什么？2.3 有一玻璃纤维纱的规格为2400tex，求该纱的横截面积（取玻璃纤维的密度 为2.54g/cm3）？ 2.4 有一玻璃纤维短切毡其规格为450 g/m2，求该毡的厚度（取玻璃纤维的密 度为2.54g/cm3）？ 2.5 无碱玻璃纤维（E-glass）的拉伸弹性模量、拉伸强度及断裂伸长率的大致 值是多少？ 2.6 碳纤维T-300的拉伸弹性模量、拉伸强度及断裂伸长率的大致值是多少？密 度为多少？ 2.7 芳纶纤维（kevlar纤维）的拉伸弹性模量、拉伸强度及断裂伸长率的大致值 是多少？密度为多少？ 2.8 常用热固性树脂有哪几种？它们的拉伸弹性模量、拉伸强度的大致值是多 少？密度为多少？热变形温度值大致值多少？ 2.9 简述单向纤维复合材料抗拉弹性模量、抗拉强度的估算方法。 2.10 试比较玻璃纤维、碳纤维单向复合材料顺纤维方向拉压弹性模量和强度值，指出其特点。 2.11 简述温度、湿度、大气、腐蚀质对复合材料性能的影响。 2.12 如何确定复合材料的线膨胀系数？ 2.13已知玻璃纤维密度为ρf=2.54g/cm3，树脂密度为ρR=1.20g/cm3，采用规格 为450 g/m2的玻璃纤维短切毡制作内衬时，其树脂含量为70％，这样制作一层其GFRP的厚度为多少? 2.14 采用2400Tex的玻璃纤维（ρf=2.54g/cm3）制造管道，其树脂含量为35％ （ρR=1.20g/cm3），缠绕密度为3股/10 mm，试求缠绕层单层厚度? 2.15 试估算上题中单层板顺纤维方向和垂直纤维方向的抗拉弹性模量和抗拉强度。 2.16已知碳纤维密度为ρf=1.80g/cm3，树脂密度为ρR=1.25g/cm3，采用规格为300 g/m2的碳纤维布制作复合材料时，其树脂含量为32％，这样制作一层其CFRP的厚度为多少?其纤维体积含量为多少？ 2.17 某拉挤构件的腹板，厚度为5mm，采用±45°的玻璃纤维多轴向织物（面密
复合材料结构及其成型原理
碳纤维复合材料 (西北工业大学机电学院, 陕西西安710072) 摘要：碳纤维复合材料与金属材料相比，其密度小、比强度、比模量高，具有优越的成型性和其他特性，具有极大的发展潜力。本文介绍了碳纤维复合材料的特点及其应用，总结了碳纤维复合材料的成型工艺及每种成型工艺的特点，并从材料和成型两个方面指出了它的发展方向。 关键词：复合材料；碳纤维；成型工艺；工艺流程 Carbon Fiber Reinforce Plastic (School of Mechatronics, Northwes tern Polytechnical University, Xi’an 710072, China) Abstract: Compared to metals, carbon fiber reinforce plastic has great potential for development with lower density, higher specific strength and modulus, and excellent moldability and other characteristics. This article describes the characteristics and applications of carbon fiber reinforce plastic and sum up the manufacturing process of carbon fiber reinforce plastic and their characteristics. Finally, this article points out the development of carbon fiber reinforce plastic from two aspects: material and manufacturing process. Key words: composites; carbon fiber; manufacturing process; process
复合材料力学沈观林编着清华大学出版社
《复合材料力学》沈观林编著清华大学出版社 第一章复合材料概论 1.1复合材料及其种类 1、复合材料是由两种或多种不同性质的材料用物理和化学方法在宏观尺度上组成的具有新性能的材料。 2、复合材料从应用的性质分为功能复合材料和结构复合材料两大类。功能复合材料主要具有特殊的功能。 3、结构复合材料由基体材料和增强材料两种组分组成。其中增强材料在复合材料中起主要作用，提供刚度和强度，基本控制其性能。基体材料起配合作用，支持和固定纤维材料，传递纤维间的载荷，保护纤维。根据复合材料中增强材料的几何形状，复合材料可分为三大类：颗粒 复合材料、纤维增强复合材料（fiber-reinforced composite）、层禾口 复合材料。 （1）颗粒：非金属颗粒在非金属基体中的复合材料如混凝土；金属颗粒在非金属基体如固体火箭推进剂；非金属在金属集体中如金属陶 '瓷O （2）层合（至少两层材料复合而成）：双金属片；涂覆金属；夹层玻璃。 （3）纤维增强：按纤维种类分为玻璃纤维（玻璃钢）、硼纤维、碳纤维、碳化硅纤维、氧化铝纤维和芳纶纤维等。 按基体材料分为各种树脂基体、金属基体、陶瓷基体、和碳基体。按纤维形状、尺寸可分为连续纤维、短纤维、纤维布增强复合材料。 还有两种或更多纤维增强一种基体的复合材料。如玻璃纤维和碳纤维增强树脂称为混杂纤维复合材料。 5、常用纤维（性能表见P7表1-1） 玻璃纤维（高强度、高延伸率、低弹性模量、耐高温） 硼纤维（早期用于飞行器，价高）碳纤维（主要以聚丙烯腈PAN纤维或沥青为原料，经加热氧化，碳化、石墨化处理而成；可分为高强度、高模量、极高模量，后两种成为石墨纤维（经石墨化2500~3000°C）；密度比玻璃纤维小、弹性模
复合材料力学
目录 复合材料细观力学 (1) 简支层合板的自由振动 (9) 不同条件下对称层合板的弯曲分析 (14)
复合材料细观力学 ——混凝土细观力学 一、研究背景 复合材料细观力学 复合材料细观力学是20世纪力学领域重要的科学研究成果之一，是连续介质力学和材料科学相互衍生形成的新兴学科。 近20年来，我国科技工作者应用材料细观力学的理论和方法，成功研究了许多复合材料的增强，断裂和破坏问题，给出了一些特色和有价值的研究成果。 混凝土细观力学 混凝土作为一种重要的建筑材料已有百余年的历史，它广泛应用于房屋、桥梁、道路、矿井、及军工等诸多方面。在水工建筑方面，混凝土也被大量使用，特别是大体积混凝土，它是重力坝和拱坝的主要组成部分，对混凝土各项力学性能的准确把握及应用，在一定程度上决定了水工建筑物的质量和安全性能。 二、研究目的 长期以来，在混凝土应用的各个领域里，人们对混凝土的力学特性进行了大量的研究。如何充分的利用混凝土的力学性能，建造出更经济、更安全和更合理的建筑物或工程结构，一直都是结构工程设计领域研究的重要课题。 三、研究现状 混凝土是由粗骨料和水泥砂浆组成的非均质材料，它的力学性能
受到材料的品质、组分、施工工艺和使用条件等因素的影响。过去，人们对混凝土力学性能的研究很大程度上是依靠实验来确定的。随着实验技术的发展，混凝土各种力学性能被揭示出来。但由于实验需要花费大量的人力、物力和财力，而且所得到的实验成果往往由于实验条件的限制也是很有限的。 现代科学的一个重要的思维方式与研究方法就是层次方法，在对客观世界的研究中，当停留在某一层次，许多问题无法解决时，深入到下一个层次，问题就会迎刃而解。 对混凝土断裂问题的研究归纳为如下四个研究层次： 1)宏观层次：混凝土这种非均质材料存在着一个特征体积，经验的 特征体积相应于3～4倍的最大骨料体积。当混凝土体积大于这种特征体积时，材料被假定为均质的，当小于这种特征体积时，材料的非均质性将会十分明显。有限元计算结果反映了一定体积内的平均效应，这个特征体积的平均应力和平均应变称之谓宏观应力和宏观应变。 2)细观层次：在这个层次中，混凝土被认为是一种由骨料、砂浆和 它们之间的粘结带组成的三相非均质复合材料，细观内部裂隙的发展将直接影响混凝土的宏观力学性。细观层次的模型一般是毫米或厘米量级。 3)微观层次：在这个层次上，认为砂浆的非均质性是由浆体中的孔 隙所产生的。由于砂浆中孔隙很小而且量多，随机分布，水泥砂
蜂窝夹层结构复合材料
1.1.夹层结构 一种复合构造的板、壳结构，它的两个表面由很薄的板材做成,中间夹以较轻的夹芯层。前者称为表板,要求强度高；后者称为夹层，要求重量轻。第二次世界大战时,为了充分利用木材资源,英国的“蚊式”轰炸机上就采用了全木质夹层结构。一般夹层结构用于机翼、尾翼、机身、箭体、箭头、减速板、发动机短舱、隔音装置、防火隔板等。与薄壁结构的薄蒙皮相比，夹层板的厚度大得多，抵抗失稳能力强，重量还可减小，而且表面光滑，气动外形良好。但它的制造工艺复杂，工艺质量又不易检验，所以应用受到限制。夹层结构表板的材料有铝合金、不锈钢、钛合金和各种复合材料。夹层材料有轻质木材、泡沫塑料等，也可用金属材料或复合材料制成波纹板夹层或蜂窝型夹层（见蜂窝结构）。夹层与表板一般用胶粘结在一起,也可用熔焊、焊接连接,形成整体。在总体受力分析中，认为上、下两表板只承受表板面内的拉、压力和剪切力,不能承受弯矩和扭矩,而中间夹层只承受垂直于夹层中面的切力。夹层结构与一般板壳结构受力分析的唯一差别在于挠度计算中除了考虑弯曲力矩产生的挠度外，还要考虑剪力的影响。夹层结构的两表板之间距离较大，所以夹层结构的弯曲刚度比一般板壳结构大得多，失稳临界应力显著提高。夹层结构自身不用铆钉,免除了钉孔引起的应力集中,提高了疲劳强度。夹层结构与相邻结构的连接较为复杂，夹层本身的局部接触强度较弱,又需承受连接的集中力,因此必须妥善进行接头设计。 1.1.类型、特点及应用 类型： 按面层分类：玻璃钢、金属、绝缘纸、胶合板、塑料板等 按芯层分类：泡沫夹层结构、波板夹层结构、蜂窝夹层结构等。特点：轻质夹芯 高强度面层
泡沫夹层结构的夹芯材料是泡沫塑料其质量轻、刚度大、保温隔热性能好。但是强度不高 蜂窝夹层结构的夹芯材料是蜂窝材料(玻璃布蜂窝、纸蜂窝、棉布蜂窝等) 特点：质量轻、强度大、刚度大 应用：构件尺寸较大、强度要求较高的部件。如图： 波板夹层结构 波板夹层结构的夹芯材料是波纹板(玻璃钢波纹板、纸基波纹板和棉布波纹板)。 特点：制作简单，节省材料，但不适用于曲面形状的制品，质量轻、刚度大。
复合材料的结构及作用
复合材料的结构及作用 一、复合材料的结构及作用 是由两种或两种以上不同性质的材料，通过物理或化学的方法，在宏观上组成具有新性能的材料。各种材料在性能上互相取长补短，产生协同效应，使复合材料的综合性能优于原组成材料而满足各种不同的要求。 复合包装材料一般由基层、功能层和热封层组成。 a.基层也是材料的外层，从商品对包装性能的要求出发，外层应具有良好的光学性能、良好的印刷适性、耐磨、耐热、一定的强度和刚度，这样使包装外观具有极佳的表现力，增加了对消费者的吸引力； b.功能层也是材料的中间层，从商品对包装性能的要求出发，应具有很高的阻隔性以及特殊性能，如防潮性、阻气性、阻氧性、保香性、耐化学性、防紫外线、防静电、防锈等，使内装物得到保护，延长其货架寿命，这是包装功能性的体现； c.热封层也是材料的内层，从商品对包装性能的要求出发，内层与内装物直接接触，起适应性、耐渗透性要好，特别的包装食品的复合材料，内层还应符合食品安全的要求，卫生、无毒、无味，要对其进行封合，因此还要有良好的热封性和粘合性。 复合包装一般要满足以下性能： a.强度性能，包括抗张(拉伸)强度，范围一般在40-100MPa，撕裂强度，范围一般在 0.3-3N，破裂强度范围一般在30-50MPa，热封强度范围一般在20-80N/20mm，另外根据不同使用场合，还要求刚性、耐磨性、断裂伸长率； b.阻隔性能，包括透气性能（透空气、O2、CO2、N2）、防潮性能、透湿性能、透光性能(尤其对特定波长的光线)、保香性能； c.耐候与稳定性能，包括抗油性能、抗化学介质、耐温性能、耐候性能、抗降解性能； d.加工性能，包括自动化包装适性、印刷适性、防静电性能、热收缩与尺寸稳定性； e.安全卫生性能，包括材料成分是否安全，细菌微生物的种类和含量多少，其它一些影响安全卫生的成分； f.其它性能，包括光学性能、透明度、白度、光泽度、废弃物处理的难易、展示性等。 被包物不同，对复合包装材料性能的要求也不同，应从被包物对包装功能的要求出发，选择和设计复合包装材料，使用最少的材料，达到保护内装物的目的，节约成本和资源。二、举例说明 聚乳酸/纳米碳管防静电复合材料。此材料是以纳米碳管为导电料通过球磨和密炼2种方法添加到聚乳酸基体中制备的防静电复合材料。具体工艺流程如下：纳米碳管的纯化处理(p-CNT)——纳米碳管功能化(f-CNT)——球磨法或密炼法混合——热压——成型。 聚乳酸可以看做复合材料的基层，是复合材料的基材框架。PLA是一种新型的生物可降解材料，有较好的生物相容性，属于环境友好型材料，符合绿色环保的要求，并且具有良好的透气性及拉伸强度，但抗冲击性能差，对热不稳定。
复合材料铺层设计说明书
复合材料铺层设计 复合材料制件最基本的单元是铺层。铺层是复合材料制件中的一层单向带或织物形成的复合材料单向层。由两层或多层同种或不同种材料铺层层合压制而成的复合材料板材称为层合板。复合材料层压结构件的基本单元正是这种按各种不同铺层设计要素组成的层合板。 本章主要介绍由高性能连续纤维与树脂基体材料构成的层合结构和夹层结构设计的基本原理和方法，也介绍复合材料结构在导弹结构中的应用。 一、层合板及其表示方法 (1) 铺层及其方向的表示 铺层是层合板的基本结构单元，其厚度很薄，通常约为～。铺层中增强纤维的方向或织物径向纤维方向为材料的主方向（1向：即纵向）；垂直于增强纤维方向或织物的纬向纤维方向为材料的另一个主方向（2向：即横向）。1—2坐标系为材料的主坐标系，又称正轴坐标系， x-y坐标系为设计参考坐标系，如图所示。 铺层是有方向性的。铺层的方向用纤维的铺向角（铺层角）θ表示。所谓铺向角（铺层角）就是铺层的纵向与层合板参考坐标X轴之间的夹角，由X轴到纤维纵向逆时针旋转为正。参考坐标系X-Y与材料主方向重合则为正轴坐标系。X-Y 方向与材料主方向不重合则称偏轴坐标系，如图（b）所示。铺层的正轴应力与偏轴应力也在图中标明。 （2）层合板的表示方法 为了满足设计、制造和力学性能分析的需要，必须简明地表示出层合板中各铺层的方向和层合顺序，故对层合板规定了明确的表示方法，如表所示。
二、单层复合材料的力学性能 单层的力学性能是复合材料的基本力学性能，即材料工程常数。由于单层很薄，一般仅考虑单层的面内力学性能，故假设为平面应力状态。单层在材料主轴坐标系中通常是正交各向异性材料，在其主方向上某一点处的正应变ε1、ε2只与该、σ2有关，而与剪应力τ12无关；同时，该点处剪应变γ12也仅点处的正应力σ 1 与剪应力τ12有关，而与正应力无关。 材料工程常数共9个：纵向和横向弹性模量Ε1和Ε2、主泊松比ν 、纵横剪切 12 弹性模量 G12，共四个弹性常数；还有纵向拉伸和压缩强度X1、X2，横向拉伸与压缩强度Y1、Y2，纵横剪切强度S共五个强度参数。这9个工程常数是通过单向层合板的单轴试验确定的。通常情况下，单层力学性能有明显的方向性，与增强纤维的方向密切相关，即Ε1>>Ε2，X>>Y；而且拉伸与压缩强度不相等，即X1≠X2，Y1≠Y2；纵横剪切性能与拉伸、压缩性能无关，即 S 与 X 、Y 无关。 由于单层复合材料是复合材料的基础，故往往用它的性能来说明复合材料的性能。但应当指出：单层的性能不能替代实际使用的层合复合材料的性能。一般说，实际使用的层合复合材料性能要低于单向复合材料的纵向性能。复合材料的性能与材料中含有的纤维数量有很大的关系，所以在规定性能数据时，一般还应给定材料所含的纤维量，通常用纤维所占的体积百分比V来表示。V称为纤维体积分数或纤维体积含量，其值通常控制在60%左右。 三、复合材料结构的制造与成形工艺 （1）制造与成形工艺的分类、特点与适用范围 树脂基复合材料结构成形工艺方法多种多样，各有所长。工艺方法的分类见图各种工艺方法的特点与适用范围见表。