ISO7438-2005金属材料弯曲试验
--`,,`,``-`-`,,`,,`,`,,`---
1
Scope ..................................................................................................................................................... 1
Not for Resale
ISO 7438:2005(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO member bodies). The work of preparing International Standards is normally carried out through ISO technical committees. Each member body interested in a subject for which a technical committee has been established has the right to be represented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization. International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2. The main task of technical committees is to prepare International Standards. Draft International Standards adopted by the technical committees are circulated to the member bodies for voting. Publication as an International Standard requires approval by at least 75 % of the member bodies casting a vote. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. ISO shall not be held responsible for identifying any or all such patent rights. ISO 7438 was prepared by Technical Committee ISO/TC 164, Mechanical testing of metals, Subcommittee SC 2, Ductility testing. This second edition cancels and replaces the first edition (ISO 7438:1985), which has been technically revised.
Not for Resale
Reference number ISO 7438:2005(E)
© ISO 2005
ISO 7438:2005(E)
PDF disclaimer This PDF file may contain embedded typefaces. In accordance with Adobe's licensing policy, this file may be printed or viewed but shall not be edited unless the typefaces which are embedded are licensed to and installed on the computer performing the editing. In downloading this file, parties accept therein the responsibility of not infringing Adobe's licensing policy. The ISO Central Secretariat accepts no liability in this area. Adobe is a trademark of Adobe Systems Incorporated. Details of the software products used to create this PDF file can be found in the General Info relative to the file; the PDF-creation parameters were optimized for printing. Every care has been taken to ensure that the file is suitable for use by ISO member bodies. In the unlikely event that a problem relating to it is found, please inform the Central Secretariat at the addryright International Organization for Standardization Reproduced by IHS under license with ISO No reproduction or networking permitted without license from IHS
© ISO 2005
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means, electronic or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or ISO's member body in the country of the requester.
7
Interpretation of results........................................................................................................................ 7
8
Test report ............................................................................................................................................. 7
2
Symbols and designations .................................................................................................................. 1
3
Principle ................................................................................................................................................. 1
--`,,`,``-`-`,,`,,`,`,,`---
Not for Resale
© ISO 2005 – All rights reserved
ISO 7438:2005(E)
Contents
Page
Foreword............................................................................................................................................................ iv
Copyright International Org©anizIaStioOn fo2r0St0an5da–rdiAzatlilonrights reserved
iii
Reproduced by IHS under license with ISO
No reproduction or networking permitted without license from IHS
4
Test equipment ..................................................................................................................................... 2
金属材料力学性能试验方法和试验设备的新进展
目前没计划
GB/T 7314-2005 金属材料 室温压缩试验方法
2005-05-13 2005-10-01 无相应国际标准
2013 年修订，拟采标 ASTM E9-09
GB/T 8358-2006 GB/T 10128-2007 GB/T 13239-2006 GB/T 22315-2008 GB/T 24191-2009 GB/T 24584-2009
金属弯曲力学性能试验方法
1993-06-01 1993-10-01 无相应国际标准
2012 年修订
表 3 金属高温长时试验标准采标及制修订情况
标准编号 GB/T 2039-2012 GB/T 10120-1996
标准名称 金属拉伸蠕变及持久试验方法 金属应力松弛试验方法
批准日期 2012-06-29 1996-09-27
采标情况
1999-03-23 1999-10-01 尚未采标
1998-10-16 1999-08-01 采标 ISO377：1997 2008-05-13 2008-11-01 采标 ISO 23718：2007 2009-06-25 2010-04-01 采标 ISO 25679：2005
制修订计划 暂时没计划（ISO 正在制定国际 标准，待完成后立即转化）
GB/T
24171.2-2009
金属材料 薄板和薄带 成形极限曲线的测定 第 2 部分：实验室成形极限曲线的测定
2009-06-25
2010-04-01 采标 ISO 12004-2：2008 目前没计划
GB/T 24172-2009 GB/T 24183-2009 GB/T 24524-2009 YB/T 5293-2006 GB/T 25047-2010 GB/T 25048-2010
金属材料弯曲试验 欧洲
金属材料弯曲试验欧洲下载温馨提示：该文档是我店铺精心编制而成，希望大家下载以后，能够帮助大家解决实际的问题。
文档下载后可定制随意修改，请根据实际需要进行相应的调整和使用，谢谢!并且，本店铺为大家提供各种各样类型的实用资料，如教育随笔、日记赏析、句子摘抄、古诗大全、经典美文、话题作文、工作总结、词语解析、文案摘录、其他资料等等，如想了解不同资料格式和写法，敬请关注!Download tips: This document is carefully compiled by the editor. I hope that after you download them, they can help yousolve practical problems. The document can be customized and modified after downloading, please adjust and use it according to actual needs, thank you!In addition, our shop provides you with various types of practical materials, such as educational essays, diary appreciation, sentence excerpts, ancient poems, classic articles, topic composition, work summary, word parsing, copy excerpts,other materials and so on, want to know different data formats and writing methods, please pay attention!金属材料在工程领域中扮演着重要的角色，而其中的弯曲试验则是评估金属材料力学性能的一种重要方法。
金属材料 弯曲试验方法
金属材料弯曲试验方法
金属材料的弯曲试验方法分为静弯试验和动弯试验。
静弯试验是将金属材料制作成一定尺寸和形状的试样，在测试机上施加静态加载作用力，使其在跨度中弯曲，测量与控制加载力和试样变形，从而得到金属材料的抗弯强度、弯曲模量等力学性能指标。
动弯试验则是在金属材料试样上施加动态加载，如冲击加载或疲劳加载，使材料在动态载荷作用下发生弯曲，通过测量与控制加载力、位移、时间等参数反映材料的弯曲行为和耐久性能，如材料的动态弯曲寿命、断裂韧性等。
常用的金属材料弯曲试验方法有以下几种：
1. 三点弯曲试验：将试样放在两个支座上，施加力在试样中间点进行弯曲，常用于测量材料的弯曲强度和弯曲模量。
2. 四点弯曲试验：将试样放在四个支座上，施加力在试样两个中间点进行弯曲，可以获得更准确的材料弯曲性能指标。
3. 悬臂梁弯曲试验：将试样一端固定在支座上，施加力在另一端进行弯曲，适用于测量材料的断裂韧性和弯曲寿命。
以上是常见的金属材料弯曲试验方法，根据具体需要选择合适的试验方法进行金属材料的力学性能分析和评估。
NF 法国国家标准目录
NF 法国国家标准目录-第20页NF A 04.102-2003 晶粒度显微检验Steels - Micrographic determination of theapparent grain size1448NF A 05.150-1985 钢铁产品显微照相检查技术Steel products. Techniques of micrographic examination.931NF A 05.152-1984 钢产品用强无机酸的低倍检查Steel products. Macroscopic examination byetching with strong mineral acids290NF P 43.011-1985 建筑物的阀门不可控制范围内的不同压力的CB电动机起动器一般技术指标valves and taps for water supply in buildings CBdisconnectors with different Non controllablepressure ranges general technical Specifications782NF EN ISO 262-1999 螺钉,螺栓和螺母的选择尺寸General purpose metric screw threads -Tolerances210NF EN 571.1-1997 无损检验渗透探伤法检验第1部分一般原则Non-destructive testing - Penetrant testing - Part 1. General principles1007NF EN 895-1995 金属材料焊接的破坏性试验横向拉伸试验Destructive tests on welds in metallic materials. Transverse tensile test463NF EN ISO 898.1-1999碳钢和合金钢制紧固件的机械性能第1部分:螺栓、螺钉和双头螺栓Mechanical properties of fasteners made of carbonsteel and alloy steel -- Part 1: Bolts, screws andstuds2752NF EN ISO 898.5-1999 横向拉伸试验Mechanical properties of fasteners made of carbonsteel and alloy steel -- Part 5: Set screws andsimilar threaded fasteners not under tensilestresses796NF EN ISO 910-1996 金属材料焊接的破坏性试验弯曲试验Destructive tests on welds in metallic materials - Bend tests744NF EN ISO 965.2-1998 公差General Purpose Metric Screw Threads -Tolerances - Part 2: Limits of Sizes for GeneralPurpose External and Internal Screw Threads -Medium Quality806NF EN 1043.1-96 金属材料焊接的破坏性试验硬度试验第1部分电弧焊接头的硬度试验Destructive Tests on Welds in Metallic MaterialsHardness Testing Part 1: Hardness Test on ArcWelded Joints544NF EN ISO 2081-2008 金属覆盖层镍＋铬和铜＋镍＋铬电镀层Metallic and other inorganic coatings.Electroplated coatings of zinc with supplementary treatments oniron or steel1443NF EN ISO 3452.2-2007 无损检验渗透剂检验第2部分渗透剂材料试验Non-destructive testing - Penetrant testing - Part 2:Testing of penetrant materials2459NF EN ISO 3452.3-2007 无损检验渗透剂检验第3部分校准试验块Non-destructive testing - Penetrant testing - Part 3:Reference test blocks512NF EN ISO 3452.4-2007 无损检验渗透剂检验第4部分设备Non-destructive testing - Penetrant testing - Part 4:Equipment629NF EN ISO 3506.1-1998 耐腐蚀不锈钢紧固件的机械性能第1部分：螺栓、螺钉和螺柱Mechanical properties of corrosion-resistantstainless steel fasteners -- Part 1: Bolts, screwsand studs1920NF EN ISO 3506.2-1998 抗腐蚀不锈钢紧固件的机械性能第2部分Mechanical properties of corrosion-resistantstainless-steel fasteners -- Part 2: Nuts1560NF EN ISO 3506.3-1997 抗腐蚀不锈钢紧固件的机械性能第3部分Mechanical properties of corrosion-resistantstainless-steel fasteners -- Part 3: Set screws andsimilar fasteners not under tensile stress1258NF EN ISO 4759.1-2005 紧固件公差.第1部分:螺栓、螺钉和垫圈和螺母.产品等级A和CTolerances for fasteners -- Part 1: Bolts, screws,studs and nuts -- Product grades A, B and C1852NF EN ISO6157.2-1995紧固件表面不均匀性Fasteners -- Surface discontinuities -- Part 2: Nuts 702NF EN ISO 6506.1-2006 金属材料布氏硬度试验第1部分试验方法Metallic materials - Brinell hardness test - Part 1:Test method982NF EN ISO 6506.2-2006 金属材料布氏硬度试验第2部分试验机器的认证和校准Metallic materials - Brinell hardness test - Part 2:Verification and calibration of testing machines838NF EN ISO 6506.3-2006 金属材料布氏硬度试验第3部分参考块的校准Metallic materials - Brinell hardness test - Part 3:Calibration of reference blocks563NF EN ISO 6506.4-2006 金属材料布氏硬度试验第4部分硬度值表Metallic materials - Brinell hardness test - Part 4:Table of hardness values339NF EN ISO 6507.1-2006 金属材料维氏硬度试验第1部分试验方法Metallic materials - Vickers hardness test - Part 1:Test method961NF EN ISO 6507.2-2006 金属材料维氏硬度试验第2部分试验机器的认证和校准Metallic materials - Vickers hardness test - Part 2:Verification of testing machines1039NF EN ISO 6507.3-2006 金属材料维氏硬度试验第3部分参考块的校准Metallic materials - Vickers hardness test - Part 3:Calibration of the reference blocks777NF EN ISO 6507.4-2006 金属材料维氏硬度试验第4部分硬度值表Metallic materials - Vickers hardness test - Part 4:Tables of hardness values635NF EN ISO 6508.1-2006 金属材料洛氏硬度试验第1部分试验方法Metallic materials - Rockwell hardness test - Part1: Test method1300NF EN ISO 6508.2-2006 金属材料洛氏硬度试验第2部分试验机器的认证和校准Metallic materials - Rockwell hardness test - Part2: Verification and calibration of testing machines1292NF EN ISO 6508.3-2006 金属材料洛氏硬度试验第3部分参考块的校准Metallic materials - Rockwell hardness test - Part3: Calibration of reference blocks884NF EN ISO 7438-2005 金属材料弯曲试验Metallic materials - Bend test 411 NF EN ISO 8493-2004 金属材料管材扩口试验Metallic materials - Tube - Drift-expanding test 285NF EN ISO10484-2004螺母扩孔试验Widening test on nuts 370 NF EN ISO10485-2004螺母锥形保证载荷试验Cone proof load test on nuts 317NF EN 12223-2000 无损检验超声波检验1号校准块规范Non-destructive testing. Ultrasonic examination. Specification for calibration block No.1376NF EN10216.2.A2-2007 承压用无缝钢管交货技术条件Seamless steel tubes for pressure purposes -Technical delivery conditions - Part 2: Non alloyand alloy steel tubes with specified elevatedtemperature properties; German version3074NF EN10217.1.A1-2005 承压用焊接钢管规定室温性能的非合金钢管Welded steel tubes for pressure purposes -Technical delivery conditions - Part 1: Non-alloysteel tubes with specified room temperatureproperties362NF F 18-001-1988 铁路运输车辆.锰钢磨耗板.性能.焊接规定Rolling stock. Wearing plates made ofmanganeses steel. Characteristics. Welding prescriptions950NF F 19-290-2002 铁路设施保护和装饰用的室外涂料系统Railway applications - Outdoor paint systems for conservation and ornementation1380NF E 25.100.0-92 Mechanical properties of fasteners made ofcarbon steel and alloy steelMechanical properties of fasteners made of carbonsteel and alloy steel1666NF E 25.400.0-93 Mechanical properties of corrosion-resistantstainlessMechanical properties of corrosion-resistantstainless983NF E 25-135-1986 固定部件。
常见的弯曲测试应用及测试标准有哪些
常见的弯曲测试应用及测试标准有哪些弯曲试验弯曲试验使试验材料在中点发生变形，导致形成凹面或弯曲而不绝裂，通常用于确定材料的延展性或抗断裂性。
弯曲测试不是加载材料直到它失效，而是将样品变形为特定形状。
弯曲试验与拉伸试验、压缩试验和疲乏试验一样流行。
通常，弯曲测试是在金属或金属材料上进行的，但可以应用于任何可以发生塑性变形的物质，例如聚合物和塑料。
这些材料可以接受任何可行的形状，但在用于弯曲测试时，最常见的是片材、条材、棒材、外壳和管材。
弯曲试验通常用于具有可接受的高延展性的材料。
常见的弯曲测试应用有哪些？硅片材料等距弯曲试验|拉力试验机木制品弯曲试验用三点弯曲夹具|拉力试验机电子产品柔性弯曲试验|拉力试验机金属焊缝导向弯曲试验|拉力试验机金属延展性弯曲试验|拉力试验机焊缝延性弯曲试验|拉力试验机使用导向弯曲和拉伸夹具进行焊接强度测试|拉力试验机木制品的静态弯曲试验|ASTMD1037木材静态弯曲试验|ASTMD143常见的弯曲测试标准有哪些？ASTMA370钢产品机械测试的测试方法和定义ASTMC1018纤维加强混凝土的弯曲韧性和首裂强度ASTMC1161高级陶瓷在环境温度下的弯曲强度ASTMC1499高级陶瓷在环境温度下的单调等双轴弯曲强度ASTMC158玻璃弯曲强度测试方法ASTMC393用梁弯曲测定夹心结构的核心剪切性能的测试方法ASTMC580耐化学砂浆、灌浆、整体铺面和聚合物混凝土的弯曲强度和弹性模量的测试方法ASTMC947薄截面玻璃纤维加强混凝土弯曲性能的测试方法ASTMD143小型透亮木材试样的测试方法ASTMD2344聚合物基复合材料及其层压材料的短束强度ASTMD6272四点弯曲非加强和加强塑料和电绝缘材料弯曲性能的测试方法ASTMD7249长梁弯曲夹层结构面层性能的测试方法ASTMD747通过悬臂梁测量塑料的表观弯曲模量ASTMD7774塑料弯曲疲乏性能测试方法ASTMD790非加强和加强塑料和电绝缘材料弯曲性能的测试方法ASTMF394钢制输电塔螺栓、镀锌和暴露的标准规范ISO6872牙科–陶瓷材料（包含修订A1：2023）ISO7438金属材料弯曲试验IPCJEDEC9702单调弯曲测试互连板级。
金属材料弯曲试验操作规程
金属材料弯曲试验操作规程金属材料（非金属管）弯曲试验操作规程（ISO9001-2015）1.0 目的和范围1.1本文件规定了测定金属材料弯曲塑性变形能力的试验方法。
1.2本文件适用于金属材料相关产品标准规定试样的弯曲试样。
1.3本文件不适用于金属管材和金属焊接接头的弯曲试样。
2.0 规范性应用文件下列文件对于本文件的作用是必不可少的。
凡是注日期的应用文件，仅注日期的版本适用于本文件。
凡是不注日期的应用文件，其最新版本（包括所有的修改单）适用于本文件。
2.1 GB/T 2975 钢及钢产品力学性能试验取样位置和试样制备2.2 GB/T 232 金属材料弯曲试验方法3.0 符号和说明本文件使用的符号，名称和单位在下表中规定。
符号名称单位a 试样厚度或直径（或多边形横截面内切圆直径）mmb 试样宽度mmL 试样长度mml 支辊间距离mmD 弯曲压头直径mmα弯曲角度（o）r 试样弯曲后的弯曲半径mmf 弯曲压头的移动距离mmc 试验前支辊中心轴所在水平面与弯曲压头中心轴所在水平面之mm 间的距离P 试验后支辊中心轴所在垂直面与弯曲压头中心轴所在垂直面之mm 间的距离（1）在钢管标准中也用符号T表示此参数4.0 原理弯曲试样是以圆形，方形，矩形或多边形横截面试样在弯曲装置上经受弯曲塑性变形，不改变加力方向，直至达到规定的弯曲角度。
弯曲试验时，试样两臂的轴线保持在垂直于弯曲轴的平面内，如为弯曲180o角的弯曲试验，按照相关产品标准的要求，可以将试样弯曲至两臂直接接触或两臂相互平行且相距固定距离，可使用垫块控制固定距离。
5.0 试验设备5.1一般要求弯曲试验应百配备下列弯曲装置之一的试验机或压力机上完成：a）配有两个支辊和一个弯曲压头的支辊式弯曲装置；b）配有一个V型模具和一个弯曲压头的V型模具式弯曲装置；c）虎钳式弯曲装置。
5.2支辊式弯曲装置5.2.1支辊长度和弯曲压头的宽度应大于试样宽度减去直径。
弯曲压头的直径由产品标准规定。
弯曲试验方法 标准
弯曲试验方法标准
弯曲试验是一种测定材料承受弯曲载荷时的力学特性的试验，主要应用于材料科学和工程领域。
根据不同的材料类型和测试标准，弯曲试验的方法和标准也有所不同。
以下是一些常见的弯曲试验方法和标准：
1. 金属材料弯曲试验方法（GB/T：该标准规定了金属材料弯曲试验方法，包括试样的形状、尺寸、制备方法和试验步骤等。
该标准适用于金属材料弯曲性能的测定，包括弯曲强度、弯曲模量等指标。
2. 塑料弯曲试验方法（GB/T：该标准规定了塑料弯曲试验方法的原理、试样形状和尺寸、试验环境、试验步骤和结果处理等。
该标准适用于塑料弯曲性能的测定，包括弯曲强度、弯曲模量等指标。
3. 玻璃弯曲试验方法（GB/T：该标准规定了玻璃弯曲试验方法的原理、试样形状和尺寸、试验环境、试验步骤和结果处理等。
该标准适用于玻璃弯曲性能的测定，包括弯曲强度、弯曲模量等指标。
4. 纸和纸板弯曲试验方法（GB/T：该标准规定了纸和纸板弯曲试验方法的原理、试样形状和尺寸、试验环境、试验步骤和结果处理等。
该标准适用于纸和纸板弯曲性能的测定，包括弯曲强度、弯曲模量等指标。
除了以上常见的弯曲试验方法和标准，还有许多其他针对特定材料的弯曲试验方法和标准，如木材、复合材料、橡胶等。
在进行弯曲试验时，应根据所测材料的类型和测试目的选择合适的试验方法和标准。
金属材料弯曲试验方法之欧阳理创编
金属材料弯曲试验方法1．范围本标准规定了弯曲试验方法的原理、符号、试验设备、试样、试验程序、试验结果评定和试验报告本标准适用于金属材料相关产品标准规定试样的弯曲试验，测定其弯曲塑性变形能力。
但小适用金属管材和金属焊接接头的弯曲试验。
2试验设备应在配备下列弯曲装置之一的试验机或压力机上完成试验。
a)支辊式弯曲装置；b)V形模具式弯曲装置；c)虎钳式弯曲装置；2.1支辊式弯曲装置2.1.1 支辊长度应大于试样宽度或直径。
支辊半径应为1-10倍试样厚度支辊应具有足够的硬度。
2.1.2 除非另有规定，支辊间距离应按照式(1)确定:a( 1 )l= (d + 3a ) ±2此距离在试验期间应保持不变。
2.1.3 弯曲压头直径应在相关产品标准中规定。
弯曲压头宽度应大于试样宽度或直径弯曲压头应具有足够的硬度2.2 V形模具式弯曲装置模具的V形槽其角度应为1800-α。
弯曲角度应在相关产品标准中规定。
弯曲压头的圆角半径为d/2。
模具的支承棱边应倒圆，其倒圆半径应为1~10倍试样厚度。
模具和弯曲压头宽度应大于试样宽度或直径。
弯曲压头应具有足够的硬度。
2.3 虎钳式弯曲装置装置由虎钳配备足够硬度的弯心组成。
可以配置加力杠杆。
弯心直径应按照相关产品标准要求，弯心宽度应人于试样宽度或直径。
2.4.3 弯曲压头直径应在相关产品标准中规定弯曲压头宽度应大于试样宽度或直径。
弯曲压头的压杆其厚度应略小于弯曲压头直径。
弯曲压头应具有足够的硬度。
3试样3.1 试验使用圆形、方形、矩形或多边形横截面的试样样坯的切取位置和方向应按照相关产品标准的要求。
如未具体规定，对于钢产品，应按照GB/T 2975的要求试样应通过机加工去除由于剪切或火焰切割等影响了材料性能的部分。
3.2 试样表面不得有划痕和损伤。
方形、矩形和多边形横截面试样的棱边应倒圆，倒圆半径不超过以下数值：----1mm，当试件厚度小于10mm----1.5mm 当试件厚度大于或等于10mm且小于50mm-----3mm 当试件厚度不小于50mm棱边倒圆时不应形成影响试验结果的横向毛刺、伤痕或刻痕。
弯曲试验方法
金属弯曲试验方法 GB232–2010 本标准参照采用国际标准lSO 7438–1985《金属材料–弯曲试验》。
1 主题内容与适用范围本标准规定了金属材料弯曲试验方法的适用范围、试验原理、试样、试验设备、试验程序及试验结果评定。
本标准适用于检验金属材料承受规定弯曲角度的弯曲变形性能。
2 引用标准GB 2975钢材力学及工艺性能试验取样规定3 试验原理将一定形状和尺寸的试样放置于弯曲装置上，以规定直径的弯心将试样弯曲到所要求的角度后，卸除试验力检查试样承受变形性能。
4 符号和名称弯曲试验中使用的符号和名称如下表和图1、图2所示。
符号名称单位a 试样厚度或直径mmb 试样宽度mmL 试样长度mml 支辊间距离mmd 弯心直径mmx 弯曲角度度F 试验力N5 试验设备5．1弯曲试验可在压力机或万能试验机上进行。
试验机应具备下列装置。
5．1．1应有足够硬度的支承辊，其长度应大于试样的宽度或直径。
支辊间的距离可以调节。
5．1．2具有不同直径的弯心，弯心直径由有关标准规定，其宽度应大于试样的宽度或直径，弯心应有足够的硬度。
5．2厚度不大于4mm的试样，可在虎钳上进行弯曲试验，弯心直径按有关标准规定。
6 试样6．1试验时用圆形、方形、长方形或多边形横截面的试样。
弯曲外表面不得有划痕。
方形和长方形试样的棱边应锉圆，其半径不应大于2mm。
6．2试样加工时，应去除剪切或火焰切割等形成的影响区域。
6．3圆形或多边形横截面的材料作弯曲试验时，如果圆形横截面直径或多边形横截面的内切圆直径不大于35mm，试样与材料的横截面相同。
若试验机能量允许时，直径不大于50mm的材料亦可用全截面的试样进行试验。
当材料的直径大于35mm，则加工成直径为25mm的试样，或如图3加工成试样。
并保留一侧原表面。
弯曲试验时，原表面应位于弯曲的外侧。
6．4当有关标准未作具体规定时，板材厚度不大于3mm，试样宽度为20±5mm。
6．5板(带)材、型材和方形横截面材料的厚度不大于25mm时，试样厚度与材料厚度相同，试样宽度为试样厚度的2倍，但不得小于10mm；当材料厚度大于25mm时，试样厚度应加工成25mm，并保留一个原表面，其宽度应加工成30mm。
金属材料弯曲试验方法之欧阳育创编
金属材料弯曲试验方法1．范围本标准规定了弯曲试验方法的原理、符号、试验设备、试样、试验程序、试验结果评定和试验报告本标准适用于金属材料相关产品标准规定试样的弯曲试验，测定其弯曲塑性变形能力。
但小适用金属管材和金属焊接接头的弯曲试验。
2试验设备应在配备下列弯曲装置之一的试验机或压力机上完成试验。
a)支辊式弯曲装置；b)V形模具式弯曲装置；c)虎钳式弯曲装置；2.1支辊式弯曲装置2.1.1 支辊长度应大于试样宽度或直径。
支辊半径应为1-10倍试样厚度支辊应具有足够的硬度。
2.1.2 除非另有规定，支辊间距离应按照式(1)确定:a( 1 )l= (d + 3a ) ±2此距离在试验期间应保持不变。
2.1.3 弯曲压头直径应在相关产品标准中规定。
弯曲压头宽度应大于试样宽度或直径弯曲压头应具有足够的硬度2.2 V形模具式弯曲装置模具的V形槽其角度应为1800-α。
弯曲角度应在相关产品标准中规定。
弯曲压头的圆角半径为d/2。
模具的支承棱边应倒圆，其倒圆半径应为1~10倍试样厚度。
模具和弯曲压头宽度应大于试样宽度或直径。
弯曲压头应具有足够的硬度。
2.3 虎钳式弯曲装置装置由虎钳配备足够硬度的弯心组成。
可以配置加力杠杆。
弯心直径应按照相关产品标准要求，弯心宽度应人于试样宽度或直径。
2.4.3 弯曲压头直径应在相关产品标准中规定弯曲压头宽度应大于试样宽度或直径。
弯曲压头的压杆其厚度应略小于弯曲压头直径。
弯曲压头应具有足够的硬度。
3试样3.1 试验使用圆形、方形、矩形或多边形横截面的试样样坯的切取位置和方向应按照相关产品标准的要求。
如未具体规定，对于钢产品，应按照GB/T 2975的要求试样应通过机加工去除由于剪切或火焰切割等影响了材料性能的部分。
3.2 试样表面不得有划痕和损伤。
方形、矩形和多边形横截面试样的棱边应倒圆，倒圆半径不超过以下数值：----1mm，当试件厚度小于10mm----1.5mm 当试件厚度大于或等于10mm且小于50mm-----3mm 当试件厚度不小于50mm棱边倒圆时不应形成影响试验结果的横向毛刺、伤痕或刻痕。