文档下载后可定制随意修改，请根据实际需要进行相应的调整和使用，谢谢!并且，本店铺为大家提供各种各样类型的实用资料，如教育随笔、日记赏析、句子摘抄、古诗大全、经典美文、话题作文、工作总结、词语解析、文案摘录、其他资料等等，如想了解不同资料格式和写法，敬请关注!Download tips: This document is carefully compiled by theeditor. I hope that after you download them,they can help yousolve practical problems. The document can be customized andmodified after downloading,please adjust and use it according toactual needs, thank you!In addition, our shop provides you with various types ofpractical materials,such as educational essays, diaryappreciation,sentence excerpts,ancient poems,classic articles,topic composition,work summary,word parsing,copy excerpts,other materials and so on,want to know different data formats andwriting methods,please pay attention!不锈钢 t 型螺栓的生产工艺流程一、准备工作阶段在开始生产不锈钢T 型螺栓之前，需要进行一系列的准备工作。
u型螺栓加工流程
u型螺栓加工流程
U型螺栓加工流程是指对U型螺栓进行生产加工的一系列工艺流程。
一般来说，U型螺栓的加工流程包括以下几个步骤：
一、铸造：首先将合适的材料熔化，然后倒入模具中进行铸造，待冷却后取出铸件。
二、锻造：对于需要高强度的U型螺栓，还需要进行锻造加工，这个过程可以提高U型螺栓的强度和韧性。
三、车削：铸造或锻造完成后，需要进行车削加工，将U型螺栓的外形加工成标准尺寸和形状。
四、切割：将车削好的U型螺栓进行切割，制成规定长度，然后进行钻孔等加工。
五、热处理：为了提高U型螺栓的性能，需要进行热处理，如淬火、回火等。
六、表面处理：为了提高U型螺栓的抗腐蚀性和外观质量，需要进行表面处理，如镀锌、喷涂等。
以上就是U型螺栓加工流程的主要内容，不同的生产厂家可能会有些微的差别，但整体流程基本类似。
- 1 -。
双头螺栓生产工艺
双头螺栓生产工艺
双头螺栓是一种常见的机械连接件，具有两个螺纹头，可以在需要定位和固定的位置上使用。
双头螺栓的生产工艺需要经过多个步骤，包括原材料准备、冷锻、热处理、机加工、表面处理等。
首先，双头螺栓的原材料通常是高强度合金钢，选材要求高质量、统一规格。
原材料要进行切割、整形等处理，以便于后续的冷锻和热处理。
冷锻是双头螺栓生产中的重要工艺，其目的是通过机械加工使材料变形并提高材料的强度和韧性。
冷锻后，双头螺栓的外形已基本成型，但其强度和硬度还不足以满足使用要求。
接下来进行热处理，即将冷锻后的双头螺栓加热至一定温度，然后通过冷却使其达到所需的强度和硬度。
热处理的过程中需要控制温度、时间等参数，以确保产品质量。
机加工是双头螺栓生产的另一个重要环节，包括车削、钻孔、铣削等操作，以便于制造出标准尺寸和精度的双头螺栓。
最后，针对双头螺栓的表面处理是为了提高其防腐、耐磨等性能。
表面处理通常包括镀锌、镀铬、喷漆等工艺，以满足不同的使用需求。
总之，双头螺栓的生产工艺需要掌握多种技术和工艺，以生产出高品质、高精度的产品。
- 1 -。
螺栓冷镦工艺流程
螺栓冷镦工艺流程下载温馨提示：该文档是我店铺精心编制而成，希望大家下载以后，能够帮助大家解决实际的问题。
文档下载后可定制随意修改，请根据实际需要进行相应的调整和使用，谢谢!并且，本店铺为大家提供各种各样类型的实用资料，如教育随笔、日记赏析、句子摘抄、古诗大全、经典美文、话题作文、工作总结、词语解析、文案摘录、其他资料等等，如想了解不同资料格式和写法，敬请关注!Download tips: This document is carefully compiled by the editor. I hope that after you download them, they can help yousolve practical problems. The document can be customized and modified after downloading, please adjust and use it according to actual needs, thank you!In addition, our shop provides you with various types of practical materials, such as educational essays, diary appreciation, sentence excerpts, ancient poems, classic articles, topic composition, work summary, word parsing, copy excerpts,other materials and so on, want to know different data formats and writing methods, please pay attention!螺栓冷镦工艺流程是一项重要的金属加工工艺，用于制造各种螺栓和螺母等产品。
双头螺栓制造工艺流程
双头螺栓制造工艺流程简介双头螺栓是一种常见的紧固件，具有两个螺纹头的特点，可用于连接零件或材料。
本文将详细介绍双头螺栓的制造工艺流程，包括原材料选取、加工制造、热处理、表面处理等环节。
原材料选取1.材料选择：双头螺栓通常由碳钢或合金钢制成，根据使用要求选择不同材料等级。
2.精选原材料：从供应商处采购合格的圆钢材料，要求无裂纹、气孔和夹杂物。
加工制造1.锯断切割：将原材料的圆钢锯断为合适的长度，以供后续加工。
2.粗车工序：–手动车削：使用车床将圆钢两端车削成螺纹的外径和长度。
–铣削：使用铣床铣削两端的螺纹深度和设置好的螺纹形状。
3.热镦成型：将加工好的圆钢加热到一定温度后放入成型设备中，通过压力和模具的作用，使圆钢两端形成双头螺栓的螺纹形状。
4.冷镦校直：将成型后的双头螺栓放入冷镦机中进行校直，以保证尺寸和形状的一致性。
热处理1.固溶处理：将制造好的双头螺栓放入高温炉中进行固溶处理，使晶体结构均匀化，提高螺栓的强度和韧性。
2.淬火处理：在固溶后，将双头螺栓迅速冷却，使晶体结构发生相变，提高螺栓的硬度。
3.回火处理：在淬火后，将双头螺栓加热到适当温度保持一段时间，使其获得一定的韧性和可靠性。
表面处理1.清洗：将双头螺栓进行清洗，去除表面的油污和其他杂质。
2.酸洗：将清洗后的螺栓浸泡在酸性溶液中，去除氧化物和表面锈蚀。
3.磷化处理：在酸洗后，将螺栓浸泡在含有磷化剂的溶液中，形成一层磷化膜，提高螺栓的抗腐蚀性能。
4.镀层处理：根据需求，可以在双头螺栓表面进行镀层处理，如镀锌、镀镍等，增加螺栓的耐腐蚀能力和美观度。
检验与包装1.外观检验：对表面处理后的螺栓进行外观检查，确保无明显缺陷和损伤。
2.尺寸检验：测量螺栓各个尺寸的精度，检查是否符合规定要求。
3.强度检验：通过拉伸试验等方法，检测螺栓的强度和延展性能。
4.包装：对合格的双头螺栓进行包装，并贴上标签，以便流通和销售。
结论双头螺栓的制造工艺流程包括原材料选取、加工制造、热处理、表面处理以及检验与包装等环节。
10.9级高强度螺栓加工工艺流程
10.9级高强度螺栓加工工艺流程下载温馨提示:该文档是我店铺精心编制而成，希望大家下载以后，能够帮助大家解决实际的问题。
文档下载后可定制随意修改，请根据实际需要进行相应的调整和使用，谢谢!并且，本店铺为大家提供各种各样类型的实用资料，如教育随笔、日记赏析、句子摘抄、古诗大全、经典美文、话题作文、工作总结、词语解析、文案摘录、其他资料等等，如想了解不同资料格式和写法，敬请关注!Download tips: This document is carefully compiled by theeditor.I hope that after you download them,they can help yousolve practical problems. The document can be customized andmodified after downloading,please adjust and use it according toactual needs, thank you!In addition, our shop provides you with various types ofpractical materials,such as educational essays, diaryappreciation,sentence excerpts,ancient poems,classic articles,topic composition,work summary,word parsing,copy excerpts,other materials and so on,want to know different data formats andwriting methods,please pay attention!10.9级高强度螺栓的精密加工工艺流程详解在工业生产中，10.9级高强度螺栓因其卓越的承载能力和耐疲劳性能被广泛应用。
螺栓加工标准工艺
螺丝生产工艺(一)--退火一、目旳：把线材加热到合适旳温度，保持一定期间，再慢慢冷却，以调节结晶组织，减少硬度，改良线材常温加工性。
二、作业流程：（一）、入料：将需要解决旳产品吊放炉内，注意炉盖应盖紧。
一般一炉可同步解决7卷（约1.2吨/卷）。
（二）、升温：将炉内温度缓慢（约3-4小时）升至规定温度。
（三）、保温：材质1018、1022线材在680℃-715℃下保持4-6h，材质为10B21，1039，CH38F线材在740℃-760℃下保持5.5-7.5 h。
（四）、降温：将炉内温度缓慢（约3-4小时）降至550℃如下，然后随炉冷却至常温。
三、品质控制：1、硬度：材质为1018、1022线材退火后硬度为HV120-170，材质为中碳线材退火后硬度为HV120-180。
2、外观：表面不得有氧化膜及脱碳现象。
螺丝生产工艺(二)--酸洗一、目旳：除去线材表面旳氧化膜，并且在金属表面形成一层磷酸盐薄膜，以减少线材抽线以及冷墩或成形等加工过程中，对工模具旳擦伤。
二、作业流程：（一）、酸洗：将整个盘元分别浸入常温、浓度为20-25%旳三个盐酸槽数分钟，其目旳是除去线材表面旳氧化膜。
（二）、清水：清除线材表面旳盐酸腐蚀产物。
（三）、草酸：增长金属旳活性，以使下一工序生成旳皮膜更为致密。
（四）、皮膜解决：将盘元浸入磷酸盐，钢铁表面与化成解决液接触，钢铁溶解生成不溶性旳化合物（如Zn2Fe（Po4）2·4H2o），附着在钢铁表面形成皮膜。
（五）、清水：清除皮膜表面残存物。
（六）、润滑剂：由于磷酸盐皮膜旳摩擦系数并不是很低，不能赋予加工时充足旳润滑性，但与金属皂（如钠皂）反映形成坚硬旳金属皂层，可以增长其润滑性能。
螺丝生产工艺(三)--抽线一、目旳：将盘元冷拉至所需线径。
实用上针对部分产品又可分粗抽（剥壳）和精抽两个阶段。
二、作业流程盘元经酸洗之后，通过抽线机冷拉至所需线径。
合用于大螺丝、螺帽、牙条所用线材。
航空螺栓制造工艺
高強度螺栓製造工藝高强度螺栓加工工艺为：热轧盘条－（冷拨）－球化（软化）退火－机械除鳞－酸洗－冷拨－冷锻成形－螺纹加工－热处理－检验一，钢材设计在紧固件制造中，正确选用紧固件材料是重要一环，因为紧固件的性能和其材料有着密切的关系。
如材料选择不当或不正确，可能造成性能达不到要求，使用寿命缩短，甚至发生意外或加工困难，制造成本高等，因此紧固件材料的选用是非常重要的环节。
冷镦钢是采用冷镦成型工艺生产的互换性较高的紧固件用钢。
由于它是常温下利用金属塑性加工成型，每个零件的变形量很大，承受的变形速度也高，因此，对冷镦钢原料的性能要求十分严格。
在长期生产实践和用户使用调研的基础上，结合GB/T6478-2001《冷镦和冷挤压用钢技术条件》GB/T699-1999《优质碳素结构钢》及目标JISG3507-1991《冷镦钢用碳素钢盘条》的特点，以8.8级，9.8级螺栓螺钉的材料要求为例，各种化学元素的确定。
C含量过高，冷成形性能将降低；太低则无法满足零件机械性能的要求，因此定为0.25％－0.55％。
Mn能提高钢的渗透性，但添加过多则会强化基体组织而影响冷成形性能；在零件调质时有促进奥氏体晶粒长大的倾向，故在国际的基础上适当提高，定为0.45％－0.80％。
Si能强化铁素体，促使冷成形性能降低，材料延伸率下降定为Si小于等于0.30％。
S.P.为杂质元素，它们的存在会沿晶界产生偏析，导致晶界脆化，损害钢材的机械性能，应尽可能降低，定为P小于等于0.030％，S小于等于0.035％。
B.含硼量最大值均为0.005％，因为硼元素虽然具有显著提高钢材渗透性等作用，但同时会导致钢材脆性增加。
含硼量过高，对螺栓，螺钉和螺柱这类需要良好综合机械性能的工件是十分不利的。
二，球化（软化）退火沉头螺钉，内六角圆柱头螺栓采用冷镦工艺生产时，钢材的原始组织会直接影响着冷镦加工时的成形能力。
冷镦过程中局部区域的塑性变形可达60％－80％，为此要求钢材必须具有良好的塑性。
螺栓螺母的加工工艺流程
螺栓螺母的加工工艺流程英文回答：The manufacturing process of bolts and nuts involves several steps to ensure their quality and functionality. Here, I will outline the general process in both English and Chinese.1. Material Selection:First, the appropriate materials for the bolts and nuts need to be selected. Common materials include carbon steel, stainless steel, and alloy steel. The choice of material depends on the application and specific requirements of the product.2. Cutting:The selected material is cut into appropriate lengths for the bolts. This can be done using various cuttingmethods such as sawing or shearing. The nuts are usually formed from pre-cut hexagonal or round bars.3. Heating and Forging:The cut bolts and nuts are then heated to a specific temperature to make them malleable. They are then forged into the desired shape using a forging press or hammer. This process helps to improve the strength and durability of the fasteners.4. Threading:After forging, the bolts and nuts undergo the threading process. Threads are created on the bolts using a thread-cutting machine or a tapping process. The nuts are usually threaded using a thread-rolling machine. This step is crucial as it ensures the proper fit and engagement between the bolt and nut.5. Heat Treatment:To enhance the mechanical properties of the bolts and nuts, they undergo heat treatment. This involves heating them to a specific temperature and then cooling themrapidly or gradually. Heat treatment helps to improve the strength, hardness, and overall performance of the fasteners.6. Surface Treatment:After heat treatment, the bolts and nuts may undergo surface treatment processes such as plating, coating, or galvanizing. These treatments protect the fasteners from corrosion, improve their appearance, and provide additional resistance to wear and tear.7. Quality Inspection:Throughout the manufacturing process, quality inspections are conducted to ensure that the bolts and nuts meet the required standards. This can include dimensional checks, hardness tests, and visual inspections. Any defective products are identified and removed from theproduction line.8. Packaging and Shipping:Once the bolts and nuts pass the quality inspection, they are packaged according to customer requirements. This can include bulk packaging or individual packaging. Finally, the finished products are shipped to customers or distributors.中文回答：螺栓螺母的加工工艺流程包括多个步骤，以确保其质量和功能。
螺栓生产工艺流程
螺栓生产工艺流程退火一、目的：把线材加热到适当的温度，保持一定时间，再慢慢冷却，以调整结晶组织，降低硬度，改良线材常温加工性。
二、作业流程：（一）入料：将需要处理的产品吊放炉内。
（二）升温：将炉内温度缓慢（约3-4 小时）升至规定温度。
（三）保温：材质1018、1022 线材在680℃-715℃下保持4-6h ，材质为10B21，1039，CH38F 线材在740℃-760 ℃下保持5.5-7.5 h 。
（四）降温：将炉内温度缓慢（约3-4 小时）降至550℃以下，然后随炉冷却至常温。
三、品质控制：1、硬度：材质为1018、1022 线材退火后硬度为HV120-170，材质为中碳线材退火后硬度为HV120-180。
2、外观：表面不得有氧化膜及脱碳现象。
酸洗一、目的：除去线材表面的氧化膜，并且在金属表面形成一层磷酸盐薄膜，以减少线材拉丝以及冷墩或成形等加工过程中，对工模具的擦伤。
二、作业流程：（一）酸洗：将整个盘元分别浸入常温、浓度为20-25%的三个盐酸槽数分钟，其目的是除去线材表面的氧化膜。
（二）清水：清除线材表面的盐酸腐蚀产物。
（三）草酸：增加金属的活性，以使下一工序生成的皮膜更为致密。
（四）皮膜处理：将盘元浸入磷酸盐，钢铁表面与化成处理液接触，钢铁溶解生成不溶性的化合物（如Zn2Fe（Po4）2·4H2o），附着在钢铁表面形成皮膜。
（五）清水：清除皮膜表面残余物。
（六）润滑剂：由于磷酸盐皮膜的摩擦系数并不是很低，不能赋予加工时充分的润滑性，但与金属皂（如钠皂）反应形成坚硬的金属皂层，可以增加其润滑性能拉丝一、目的：将盘元冷拉至所需线径。
实用上针对部分产品又可分粗抽（剥壳）和精抽两个阶段。
、作业流程拉丝：为了减小由于冷拉所产生的加工应力，确保线材的可加工性，将线材的冷拉分两个阶段，首先利用连续式伸线机将盘元粗抽至一定线径（以确保精抽减面率小于15%为原则），之后退火，以消除粗抽产生的加工应力。
- 1、下载文档前请自行甄别文档内容的完整性，平台不提供额外的编辑、内容补充、找答案等附加服务。
- 2、"仅部分预览"的文档,不可在线预览部分如存在完整性等问题,可反馈申请退款(可完整预览的文档不适用该条件!)。
- 3、如文档侵犯您的权益，请联系客服反馈,我们会尽快为您处理(人工客服工作时间：9:00-18:30)。
螺栓的生产工艺 螺丝生产工艺(一)--退火 一、目的：把线材加热到适当的温度，保持一定时间，再慢慢冷却，以调整结晶组织，降低硬度，改良线材常温加工性。 二、作业流程： （一）、入料：将需要处理的产品吊放炉内，注意炉盖应盖紧。一般一炉可同时处理7卷（约1.2吨/卷）。 （二）、升温：将炉内温度缓慢（约3-4小时）升至规定温度。 （三）、保温：材质1018、1022线材在680℃-715℃下保持4-6h，材质为10B21，1039，CH38F线材在740℃-760℃下保持5.5-7.5 h。 （四）、降温：将炉内温度缓慢（约3-4小时）降至550℃以下，然后随炉冷却至常温。 三、品质控制： 1、 硬度：材质为1018、1022线材退火后硬度为HV120-170，材质为中碳线材退火后硬度为HV120-180。 2、外观：表面不得有氧化膜及脱碳现象。
螺丝生产工艺(二)--酸洗 一、目的：除去线材表面的氧化膜，并且在金属表面形成一层磷酸盐薄膜，以减少线材抽线以及冷墩或成形等加工过程中，对工模具的擦伤。 二、作业流程： （一）、酸洗：将整个盘元分别浸入常温、浓度为20-25%的三个盐酸槽数分钟，其目的是除去线材表面的氧化膜。 （二）、清水：清除线材表面的盐酸腐蚀产物。 （三）、草酸：增加金属的活性，以使下一工序生成的皮膜更为致密。 （四）、皮膜处理：将盘元浸入磷酸盐，钢铁表面与化成处理液接触，钢铁溶解生成不溶性的化合物（如Zn2Fe（Po4）2·4H2o），附着在钢铁表面形成皮膜。 （五）、清水：清除皮膜表面残余物。 （六）、润滑剂：由于磷酸盐皮膜的摩擦系数并不是很低，不能赋予加工时充分的润滑性，但与金属皂（如钠皂）反应形成坚硬的金属皂层，可以增加其润滑性能。 螺丝生产工艺(三)--抽线 一、目的：将盘元冷拉至所需线径。实用上针对部分产品又可分粗抽（剥壳）和精抽两个阶段。 二、作业流程 盘元经酸洗之后，通过抽线机冷拉至所需线径。适用于大螺丝、螺帽、牙条所用线材。 螺丝生产工艺(四)--成型 一、目的：将线材经冷间锻造（或热间锻造），以达到半成品之形状及长度（或厚度）。 二、作业流程： 1、六角螺栓（四模四冲或三模三冲） （1）、切断：通过可动的剪刀单向移动，将卡于剪模内的线材切成所需胚料。 （2）、一冲：后冲模顶住胚料冲模挤压胚料，初步成型，之后后冲模将胚料推出。 （3）、二冲：胚料进入第二打模，二冲模挤压，胚料呈扁圆状，之后后冲模将胚料推出。 （4）、三冲：胚料进入第三打模，通过六角三冲模仁剪切，胚料六角头初步形成，之后，后冲模将胚料推入第三打模，切料自六角头切断，六角头形成。 2、六角螺栓（三模三冲） 3、螺丝（一般头型一模二冲） （1）、切断：通过可动剪刀单向移动，将卡于剪模内的线材切成所需胚料。 （2）、一冲：打模固定，一冲模将产品头部初步成型，以使下一冲程能完全成型。当产品为一字割沟时，一冲模为内凹、椭圆槽，产品为十字槽时，一冲模为内凹四方槽。 （3）、二冲：一冲之后，冲具整体运行，二冲模移向打模正前方，同时二冲模向前运行，将产品最终成型。之后由后冲棒将胚料推出。 三、热打 1、 加热：于加热设备将胚料需成型一端加热至白热状态，依据产品规格设定加热温度和时间。一般3/4以下加热7-10秒，7/8-1＂加热15秒左右。 2、 成型：将加热后的胚料迅速移至成型机，通过后座，夹模固定，头模冲击胚料，加以成型。可以根据胚料的长度调整后座的距离。 3、 束杆：于束杆机上利用挤压将产品缩杆。 热打也称红打。 四、螺帽成型： （一）、作业流程： 1、切断：由内刀模（410）与剪切刀（301）配合，将线材切成所需胚料。 2、一冲：由前冲模（111）、冲程模（411）、后冲棒（211）配合，将变形不平的切断胚料加以整形，并由后冲棒（211）将胚料推出。 3、二冲：运转夹（611）将胚料从一冲夹至二冲，由前冲模（112）、冲程模（412）、后冲棒（412）配合，更进一步将胚料整形，并加强第一冲的压平与饱角作用，之后由后冲棒（212）将胚料推出。 4、三冲：运转夹（612）将胚料从二冲夹至三冲，由前冲模（113）、冲程模（413）、后冲棒（213）配合，再次挤压胚料，以使下冲能完全成型，之后由后冲棒（213）将胚料推出。 5、四冲：运转夹（613）将胚料从三冲夹至四冲，由前冲模（114）、冲程模（414）、后冲棒（214）配合，将螺帽完全成型，并藉控制铁屑厚度来调整螺帽的厚度，之后由后冲棒（214）将胚料推出。 6、五冲：运转夹（614）将胚料从四冲夹至五冲，由前冲模（119）、脱料盘（507）配合，将成型完全的胚料冲孔，并使冲断的铁屑进入打孔模下仁，而最终完成螺帽的成型。螺帽的头部标记在此过程形成。 螺丝生产工艺(五)--辗牙 一、目的：将已成型的半成品辗制或攻丝以达到所需的螺纹。实用上针对螺栓（螺丝）称为辗牙，牙条称为滚牙，螺帽称为攻牙。 二、辗牙：辗牙即是将一块牙板固定，另一块活动牙板带动产品移动，利用挤压使产品产生塑性变形，形成所需螺纹。 三、攻牙：攻牙即是将已成型之螺帽，利用丝攻攻丝，形成所需螺纹。 四、滚牙：滚牙是以两个相对应的螺丝滚轮，正向转动，利用挤压使产品产生塑性变形，形成所需螺纹。滚牙通常用于牙条。 螺丝生产工艺(六)-热处理 一、热处理方式：根据对象及目的不同可选用不同热处理方式。 调质钢：淬火后高温回火（500-650℃） 弹簧钢：淬火后中温回火（420-520℃） 渗碳钢：渗碳后淬火再低温回火（150-250℃） 低碳和中碳（合金）钢淬成马氏体后，随回火温度的升高，其一般规律是强度下降，而塑性、韧性上升。但由于低、中碳钢中含碳量不同，回火温度对其影响程度不同。所以为了获得良好的综合机械性能，可分别采取以下途径： （1）、选取低碳（合金）钢，淬火后进行低温250℃以下回火，以获得低碳马氏体。为了提高这类钢的表面耐磨性，只有提高各面层的含碳量，即进行表面渗碳，一般称为渗碳结构钢。 （2）、采取含碳较高的中碳钢，淬火后进行高温（500-650℃）回火（即所谓调 质处理），使其能在高塑性情况下，保持足够的强度，一般称这类钢为调质钢。如果希望获得高强度，而宁肯降低塑性及韧性，对含碳量较低的含金调质可采取低温回火，则得到所谓“超高强度钢”。 （3）、含碳量介于中碳和高碳之间的钢种（如60，70钢）以及一些高碳钢（如80，90钢）， 如果用于制造弹簧，为了保证高的弹性极限、屈服极限和疲劳极限，则采用淬火后中温回火。 （4）、脱碳：指黑色金属材料（钢）表面碳的损耗。热处理后会有脱碳现象，轻微脱碳是允许的，脱碳层深度影响表面硬度。脱碳层越深，表面硬度值越小。 具体检测依据GB3098.1 二、作业流程： 退火（珠光体型钢） 1、预热处理：正火 高温回火（马氏体型钢） （1）、正火目的是细化晶粒，减少组织中的带状程度，并调整好硬度，便于机械加工，正火后，钢材具有等轴状细晶粒。 2、淬火：将钢体加热到850℃左右进行淬火，淬火介质可根据钢件尺寸大小和该钢的淬透性加以选择，一般可选择水或油甚至空气淬火。处于淬火状态的钢，塑性低，内应力大。 3、回火： （1）、为使钢材具有高塑性、韧性和适当的强度，钢材在400-500℃左右进行高温回火，对回火脆性敏感性较大的钢，回火后必须迅速冷却，抑制回火脆性的发生。 （2）、若要求零件具有特别高的强度，则在200℃左右回火，得到中碳回火马氏体组织。 （二）、弹簧钢： 1、淬火：于830-870℃进行油淬火。 2、回火：于420-520℃左右进行回火，获得回火屈氏体组织。 （三）、渗碳钢： 1、 渗碳：化学热处理的一种，指在一定温度下，在含有某种化学元素的活性介质中，向钢件表面渗入C元素。分预热（850℃） 渗碳（890℃） 扩散（840℃）过程 2、淬火：碳素和低合金渗碳钢，一般采用直接淬火或一次淬火。 3、回火：低温回火以消除内应力，并提高渗碳层的强度及韧性。 螺丝生产工艺(七)-表面处理 一、表面处理种类： 表面处理即是通过一定的方法在工件表面形成覆盖层的过程，其目的是赋以制品表面美观、防腐蚀的效果，进行的表面处理方法都归结于以下几种方法： 1、 电镀：将接受电镀的部件浸于含有被沉积金属化合物的水溶液中，以电流通过镀液，使电镀金属析出并沉积在部件上。一般电镀有镀锌、铜、镍、铬、铜镍合金等，有时把煮黑（发蓝）、磷化等也包括其中。 2、热浸镀锌：通过将碳钢部件浸没温度约为510℃的溶化锌的镀槽内完成。其结果是钢件表面上的铁锌合金渐渐变成产品外表面上的钝化锌。热浸镀铝是一个类似的过程。 3、机械镀：通过镀层金属的微粒来冲击产品表面，并将涂层冷焊到产品的表面上。 二、品质控制： 电镀的质量以其耐腐蚀能力为主要衡量标准，其次是外观。耐腐蚀能力即是模仿产品工作环境，设置为试验条件，对其加以腐蚀试验。电镀产品的质量从以下方面加以控制： 1、外观： 制品表面不允许有局部无镀层、烧焦、粗糙、灰暗、起皮、结皮状况和明显条纹，不允许有针孔麻点、黑色镀渣、钝化膜疏松、龟裂、脱落和严重的钝化痕迹。 2、镀层厚度： 紧固件在腐蚀性大气中的作业寿命与它的镀层厚度成正比。一般建议的经济电镀镀层